Search

• Difference of damage modes caused by the boundary conditions of primary load-bearing yarns. • Straightening effect of braided yarns with undulations under low-velocity impact. • Variation of off-axial angles leading to the transition of failure modes. The sensitivity of off-axial angle on impact response was investigated by experimental and numerical methods in this work. Three types of braided laminates with different on/off-axial angles in terms of OA00, OA225 and OA45 were prepared and low-velocity impact tests with various energy levels were performed. Meso-level finite element model (FEM) was also developed to reveal impact damage initiation and development. We discovered that the boundary condition of primary load-bearing yarns depending on the off-axial angles caused the difference of structural deformation and stress distribution of braiding yarns during impact process. Due to the restriction of the pressurized tips, the straightening effect of primary load-bearing yarns with heavy waviness caused its out-of-plane movement and related main cracks in OA00 specimen. In addition, the matrix resin cracks were found at the edge of the specimen because of in-plane shear movement of braiding yarns. As for OA45 specimen, more evident bending deformation was observed, resulting in elevated tensile stress of braiding yarns on non-impact side. The variation of off-axial angle from 0 to 45 degree led to the failure mode transforming from the extensive matrix damage on specimen edge to the severe fiber breakage on non-impact side. As a medium off-axial angle, OA225 specimen exhibited a mixture failure mode to resist impact and achieved excellent performance with respect to higher peak force and delayed load dropping. [Display omitted] [ABSTRACT FROM AUTHOR]

In this work, the synergistic effect of 3D orthogonal woven structure and asymmetric carbon/glass hybridization on impact response was studied by experimental and numerical methods. The hybrid 3D orthogonal woven (H3DOW) composite plates were manufactured on a home-made 3D weaving machine. Impacts with various energies 42.9, 54.9, 66.9 and 78.9 J were applied to carbon (CG) and glass (GC) sides. The impact response was examined using fracture morphology observation and mechanical curves. Yarn-level finite element models including failure criteria and progressive damage law were established in ABAQUS/Explicit to compare the structural deformation and damage behavior. The impact side significantly influences the failure modes of H3DOW materials. GC specimen failed through delamination between carbon layers at non-impact side and subsequent fiber tensile breakage, whereas the crushing damage in the carbon yarn located in the impact-side and large area debonding between yarn and matrix resin in superficial layers was the dominant failure mode in CG specimen. This caused the CG configuration to exhibit better impact resistance with respect to the perforation threshold energy. [ABSTRACT FROM AUTHOR]

Failure mechanism of complex profile component is always different from that of conventional plate counterpart due to the coupling effect of material and structure. In this work, the low-velocity impact (LVI) and compression after impact (CAI) behaviors of Ω-shape hybrid carbon/Kevlar 3 D orthogonal woven (3DOW) composite made for vehicle B-pillar were comprehensively studied by mechanical tests and mesoscale finite element (FE) analysis at component level, high-speed infrared (IR) thermal imaging, acoustic emission (AE) detection, and microscopic damage morphology characterization. It is found that a through-thickness stress concentration ring leads to high stress state and damage zone penetrating from the impact side to non-impact side along the ring path instead of at the lowest impactor position. The slope effect can not only help the stress conduction downward, but also inhibit the damage propagation from the impact side to the slope. Impact-induced cracks are concentrated around the R corners and extended along the axial direction of the specimen, forming the strip-shaped damage concentration zone along the upper eave of the slope. The Progressive Top-Down Crushing (PTDC) mode of compression after impact is due to the complex deformation process of each yarn such as squeezing, folding and eversion in the crushing process from the top of specimen. And the Middle Indentation Fracture (MIF) mode is the result of bending instability and abrupt fracture. This work presents a reference significance for the further development of composite strengthening components in vehicle bodywork. [ABSTRACT FROM AUTHOR]

• Advantages of asymmetric hybridization on impact resistance and resilience. • Rules of external damage area and internal crack volume distribution. • Damage mechanism of carbon/Kevlar hybridization laminates. The ply structure has a significant effect on the impact resistance and failure behavior of composite laminates. In this paper, carbon/Kevlar hybrid fabric reinforcements were prepared with different Kevlar ratio (0%, 25%, 50%, 75%, 100%) by replacing carbon fabric plies on the non-impact side by Kevlar plies. The low-velocity impact tests for all configurations were carried out under 15 J and 25 J energy respectively. The results show that the maximum deflection, impact duration, impact absorption energy and absorption energy efficiency of hybrid laminates increased with the Kevlar hybrid ratio, whereas the peak force presented a decreasing trend, which indicates that the adding of Kevlar layer makes the laminates more ductile than non-hybrid carbon structure. The damage mechanism of the carbon fiber ply was brittle fiber fracture, resin cracking and resin shedding, while the fibers pull-out and tows splitting was found in Kevlar ply. The critical structural damages start from the non-impact side and evolve to the impact side. And the rules of internal crack volume distribution with Kevlar plies are consistent with the trend of external damage area on the non-impact side. It is suggested that in order to take into account the peak strength and excellent structural resilience, Kevlar asymmetric-hybrid ratio of 25% is the most appropriate. The reason is that an appropriate small ratio of Kevlar cushion ply can not only effectively avoid the tensile fracture at non-impact side happened in the non-hybrid carbon structure, but also withstand enough impact load by maintaining a high carbon fiber content. [ABSTRACT FROM AUTHOR]

• The structural hybridization effect on low-velocity impact response of braided/unidirectional (UD) laminates was investigates. • Continuum shell finite element models based on the anisotropic constitutive relationship of braided and UD plies were established to reveal the damage onset and propagation. • The extensive delamination formed rapidly when impacted on the fabric side. • The damage characterized by severe fiber breakage occurs at the impact site when impacted on UD ply side. This work investigated the structural hybridization effect on the low-velocity impact response of braided/unidirectional(UD) laminate. Two groups of hybridization laminates, namely interleaving and clustering groups, were manufactured. The impact performance of the specimens was characterized by combining dropping testbench, optical camera and ultra-sound detector. A continuum shell finite element model was established to reveal the progressive damage behavior of hybridization laminate. The specimen in the interleaving group presented overwhelming performance than that in the clustering group. The impact side effect on failure modes was discussed in detail. When impacted on the braided fabric side, extensive delamination formed on the edge of the specimen due to bending deformation. It further resulted in-plane crushing failure of UD sub-laminate. In contrast, severe fiber breakage occurs at the impact site due to combination stress of tensile and shear when impacted on UD side. Therefore, the fabric-impacted specimen exhibits better impact resistance than that impacted on UD side with respect to higher peak load and lower absorbed energy. [Display omitted] [ABSTRACT FROM AUTHOR]

• Advantages of symmetric intercalation hybridization on impact strength and resilience. • Correlation of apparent damage area index and internal damage volume data. • Damage mechanism of symmetric and asymmetric carbon/Kevlar structures. Hybrid fiber composite laminates with the same materials, manufacturing methods and molding processes may present different mechanical behaviors. In this paper, the effect of intercalation sequence on the mechanical performance of carbon/Kevlar plain laminates were studied. According to different intercalation methods, the hybrid layout was divided into symmetric and asymmetric configurations. It is found that the symmetric intercalation structures (KCCK and CKKC) possess better load-bearing and resilience capacity compared with asymmetric structures (CCKK and CKCK), even better than pure carbon structure (CCCC) under high energy impact. The impact damage volume of symmetric specimens was significantly smaller than that of asymmetric specimens by quantitative micro-CT analysis. The apparent damage index (d f and d r) can be used to estimate the internal damage data (d CT , H and V). KCCK, a typical symmetric sandwich-like structure, presented the most slight damage among all symmetric and asymmetric configurations, with shear cracks observed at the brittle carbon fiber core layers, while the delamination cracks between Kevlar-carbon interlayers were away from the central damaged region. In CKCK, interlaminar cracks were formed at each carbon-Kevlar interlayers, which shared and relieved the primary interlaminar crack at the core layers compared with CCKK. [ABSTRACT FROM AUTHOR]