Search

[Display omitted] • Prins cyclisation from isovaleraldehyde and isoprenol to tetrahydropyranol. • Zeolites with varying acidity and hierarchical materials as catalysts. • H-Beta-300 zeolite giving 72% selectivity to the desired product at 99% conversion. • The cis/trans ratio of tetrahydropyranols depends on porous structure. • Parallel formation of tetrahydropyranol and dihydropyran confirmed by DFT. In this work, several heterogeneous micro- and mesoporous, acidic catalysts were tested for the selective synthesis of Florol®, an industrial product formed via condensation and rehydration starting from isoprenol and isovaleraldehyde in dimethylcarbonate as a solvent. The results showed that a mildly acidic, microporous H-Beta-300 with SiO 2 /Al 2 O 3 ratio of 300 was the best catalyst, giving 72% selectivity with 99% conversion at 40 °C when using the molar ratio isoprenol to isovaleraldehyde of 1:5. More acidic zeolites gave slightly lower selectivity, while the lowest selectivity (up to 52%) was obtained with mesoporous catalysts exhibiting mild acidity and no strong Brønsted acid sites. Selectivity to pyranols was nearly constant when changing temperature, while a larger excess of isovaleraldehyde promoted formation of tetrahydropyranol. H-Beta-300 catalyst was successfully after calcination at 400 °C. DFT calculations pointed out on the parallel formation of tetrahydro pyranols and dihydropyrans, which are the corresponding dehydration products. [ABSTRACT FROM AUTHOR]

Abstract: Desilication of ITQ-4 (IFR code, 1-dimensional 12-MR channel system of 0.62nm×0.72nm) in aqueous NaOH solutions was practiced in order to produce the zeolite in the hierarchical form, i.e. combining the native micropores with a secondary network of intracrystalline mesopores. The parent material (Si/Al=32) was synthesized using benzylquinuclidinium as the structure-directing agent in the presence of fluoride anions. The samples were characterized by ICP-OES, XRD, TEM, N2 adsorption, and FTIR spectroscopy. In a representative treatment, the mesopore surface area of the ITQ-4 experienced a sevenfold increase (from 29 to 206m2 g−1) upon optimized NaOH post-treatment, whereas the microporosity was reduced by 70% (from 0.20 to 0.06cm3 g−1). Chemical analysis and infrared spectroscopy of adsorbed pyridine showed that after alkaline treatment the amount of Brønsted acid sites remains practically constant whereas a significant increase in Lewis acid sites was obtained. Infrared studies with adsorbed 2,4,6-collidine concluded that the accessibility of acid sites in the hierarchical zeolite increased substantially due to an increase in the available active sites at the pore mouths of the hierarchical zeolite. [Copyright &y& Elsevier]

An accessibility index (ACI) was derived from infrared spectroscopy of substituted alkylpyridines with different size (pyridine: 0.57nm, 2,6-lutidine: 0.67nm, and 2,4,6-collidine: 0.74nm) over hierarchical porous ZSM-5 crystals. The samples were prepared by selective silicon extraction of a commercial sample in NaOH (desilication), and they contained different degrees of intracrystalline mesoporosity. Our results demonstrate the enhanced accessibility of Brønsted acid sites in the hierarchical zeolites. For example, a relatively bulky molecule such as collidine, which probes practically no acid site of the parent medium-pore MFI structure, can access up to 40% of the acid sites in the mesoporous sample. The ACI is a powerful tool to standardize acid site accessibility in zeolites, and can be used to rank the effectiveness of synthetic strategies to prepare hierarchical zeolites. [Copyright &y& Elsevier]