We report on the degradation of organic photovoltaic (OPV) cells in both indoor and outdoor environments. Eight different research groups contributed state of the art OPV cells to be studied at Pomona College. Power conversion efficiency and fill factor were determined from IV curves collected at regular intervals over six to eight months. Similarly prepared devices were measured indoors, outdoors, and after dark storage. Device architectures are compared. Cells kept indoors performed better than outdoors due to the lack of temperature and humidity extremes. Encapsulated cells performed better due to the minimal oxidation. Some devices showed steady aging but many failed catastrophically due to corrosion of electrodes not active device layers. Degradation of cells kept in dark storage was minimal over periods up to one year. [ABSTRACT FROM AUTHOR]

Four new monomers for directional stepwise synthesis of oligophenylenevinylenes (OPVs) (4-{2-[4-(5,5-dimethyl[1,3]dioxan-2-yl)-2,5-dipropoxyphenyl]vinyl}benzyl)phosphonic acid diethyl ester, (5-{2-[4-(5,5-dimethyl[1,3]dioxan-2-y])-2,5-dipropylphenyl]vinyl}thiophene-2-ylmethyl)phosphonic acid diethyl ester, (5-{2-[4-{5,5-dimethyl[1,3]dioxan-2-yl)-2,5-diprepoxyphenyl]vinyl}thiophene-2-ylmethyl)phosphonic add diethyl ester, and (7-{2-[4-(5,5-limethyl[1,3] dioxan-2-yl)z2,5-dipropylphenyl]-vinyl}benzo[1,2,5]thiadiazol-4-ylmethyl)phosphonic acid diethyl ester have been prepared. Trimeric OPVs were then synthesized and tested as active materials in photovoltaic cells. Conversion efficiencies in the range of 0.5–1% were obtained in blends with the soluble C60 derivative PCBM. A terpyridine end-functionalized trimer and a heterotrimer with a mixed composition of monomers were also prepared. [ABSTRACT FROM AUTHOR]

A new stepwise directional synthetic route to single-oligomer p-phenylenevinylenes (OPVs) has been developed. The first step in the reaction sequence is the condensation of a functionalized benzaldehyde with a novel monomer having a methyl phosphonate ester group in one end and an acetal-protected aldehyde at the other end of a stilbene core. Oligomerization then proceeds stepwise by alternating reaction of the previous aldehyde-terminated OPV fragment with the monomer and deprotection of the acetal. Thus, a series of OPVs with 3, 5, 7, 9, and 11 phenylene vinylene units has been prepared that has an electron-donating methoxy group at one end and an electron-accepting aldehyde group at the other end. Some examples where a dimethylamino group replaced the methoxy group were also prepared. The oligomer with seven phenylene vinylene units was then further derivatized at the aldehyde position to create a series of OPVs with a range of substituents from strongly electron-accepting nitrophenyl to electron-donating methoxyphenyl. Photovoltaic cells were assembled with the synthesized OPVs as the photoactive layer. Illumination under simulated sunlight (AM1.5) gave short circuit currents (Isc) in the range 0.015-0.5 mA cm-2 and typical open circuit voltages (Voc) of 0.4-0.8 V. The maximum efficiency obtained was ∼0.1%. [ABSTRACT FROM AUTHOR]