The transparent [Li 0.04 (K 0.5 Na 0.5) 0.96 ]NbO 3 +0.5mol% Er 2 O 3 (KNNLN-Er) lead-free piezoelectric ceramics were prepared by stereolithography technique. The influence of different sintering holding time (4h∼8h) on the micromorphology, relative density, shrinkage, electric properties, and photoluminescence properties were systematically investigated. The KNNLN-Er ceramics show the coexistence of orthorhombic and tetragonal structures. The grain size increases obviously and then decreases slightly with the holding time increasing. The KNNLN-Er ceramics exhibit good piezoelectric performance (piezoelectric constant d 33 ∼97 pC/N, electromechanical couple coefficient k t ∼0.36) and the moderate transparency of 34% when the holding time is 6h during sintering at 1120°C. Besides, the intensity of the photoluminescence emission spectra increases with the holding time increasing. Furthermore, in order to estimate the properties of the KNNLN-Er transparent ceramics, an ultrasonic transducer with a center frequency of 10.5 MHz was fabricated, which can be used for photoacoustic and fluorescence imaging. The results indicate that the KNNLN-Er ceramics have potential for multimode imaging applications. [ABSTRACT FROM AUTHOR]

Abstract The PZT ceramics with different weight content from 78% to 89% were printed using the stereolithography method. The piezoelectric properties as well as the microstructure of the ceramics were investigated in detail. X-ray patterns and Raman spectra demonstrate that the steady PZT tetragonal phase has already formed in these sintered ceramics. Besides, the piezoelectric constant and dielectric constant were 212–345 pC/N and 760–1390, which were sligthly lower than that of the dry pressing disk. Furthermore, a two-dimensional ultrasound transducer array (8 × 8) was designed and developed to evaluate the properties of the 3D-printed PZT ceramics. [ABSTRACT FROM AUTHOR]

In this work, a stereolithography-based method of 3D printing was successfully used to fabricate a complex-shaped triangular zirconia cutting tool with a tool withdrawal groove and a honeycomb ceramic component. The sintered bodies displayed significant shrinkage after sintering, with the maximum shrinkage being 35.26%. The XRD pattern indicated that the crystalline phase of the parts was the t-ZrO 2 phase, while SEM characterization revealed that the sintered bodies were composed of densely packed submicron-grade grains, without any discernible pores. The density of the parts was measured as 97.14% via Archimedes’ water displacement method, which is consistent with the results of SEM characterization. Additionally, the measured Vickers hardness and fracture toughness of the fabricated parts were 13.0597 GPa and 6.0380 MPa m 1/2 , respectively. These values are close to the structural properties of common zirconia ceramics prepared by conventional approaches. Hence, a novel DLP-stereolithography-based 3D printing process for the fabrication of complex and dense zirconia ceramic parts has been proposed in this work. [ABSTRACT FROM AUTHOR]