Search

Transparent Sm:Y 2 O 3 ceramics were fabricated by spark plasma sintering (SPS). The effects of LiF additive and sintering temperature on the microstructure and optical transmittance of the Sm:Y 2 O 3 ceramics were investigated. The optimal content of LiF additive and sintering temperature was found to be 0.3 wt% and 1500 ℃. The transmittance of Sm:Y 2 O 3 ceramics with a thickness of 1.7 mm reached 75.3% at 609 nm, which is about 94% of the theoretical value. The average grain size of the sample was about 50 µm. [ABSTRACT FROM AUTHOR]

Transparent Y 2 O 3 ceramics were fabricated by the solid-state reaction and vacuum sintering method using La 2 O 3 , ZrO 2 and Al 2 O 3 as sintering aids. The microstructure of the Y 2 O 3 ceramics sintered from 1550 °C to 1800 °C for 8 h were analyzed by SEM. The sintering process of the Y 2 O 3 transparent ceramics was optimized. The results showed that when the samples were sintered at 1800 °C for 8 h under vacuum, the average grain sizes of the ceramics were about 3.5 µm. Furthermore, the transmittance of Y 2 O 3 ceramic sintered at 1800 °C for 8 h was 82.1% at the wavelength around the 1100 nm (1 mm thickness), which was close to its theoretical value. Moreover, the refractive index of the Y 2 O 3 transparent ceramic in the temperature range from 30 °C to 400 °C were measured by the spectroscopic ellipsometry method. [ABSTRACT FROM AUTHOR]

Tb3Al5O12 ( TAG) transparent ceramics were prepared by a reactive sintering method using presintering in a muffle furnace combined with hot isostatic pressing ( HIP) sintering. The dilatometric, differential scanning calorimetry-thermogravimetric ( DSC- TG) curves and optical quality were investigated. The microstructure evolution of the TAG ceramic samples was clarified. Two successive transformations were found to generate a TAG phase, as observed in the dilatometric and DSC- TG curves and XRD patterns of TAG ceramics sintered at different temperature. The changes in average grain size and densification suggest that a 1600°C presintering temperature is suitable for HIP. The optical transmittance of the obtained 0.4 wt% TEOS: TAG transparent ceramics, which were fabricated by a new two-step sintering of presintering at 1600°C in a muffle furnace followed by HIP at 1650°C, can reach above 80% in the visible (vis) and near-infrared ( NIR) regions. Its transmittance was very close to the theoretical limit. To the best of our knowledge, this is the first time that TAG transparent ceramics with ideal optical quality were obtained without vacuum sintering. [ABSTRACT FROM AUTHOR]

2 at.% Tm, xat.% Dy:Y 2 O 3 (x = 0, 0.1, 0.5 and 1) transparent ceramics were fabricated via vacuum sintering. The microstructural properties of the prepared ceramics were determined using XRD and SEM. The absorption cross-section of 2 at.% Tm, 1 at.% Dy:Y 2 O 3 ceramic was 0.53 × 10−20 cm2 with the FWHM of 43.59 nm. The increased cross-section originates from a large overlapping range appearing in the absorption spectrum of the Dy3+:6H 15/2 → 6F 5/2 and Tm3+:3H 6 →6H 4 transitions. The J-O intensity parameters Ω 2 , Ω 4 and Ω 6 and the fluorescence characteristics of the pivotal luminescent level of the Dy3+ ions were investigated. Under 793 nm excitation, the emission cross section of the Tm,Dy:Y 2 O 3 ceramic at 3094 nm was 3.63 × 10−21 cm2 with the FWHM of 355 nm. The fluorescence lifetimes of Dy3+:6H 13/2 level of 2 at.% Tm, xat.% Dy:Y 2 O 3 (x = 0.1, 0.5 and 1) ceramics were fitted to be 357 μs, 282 μs and 149 μs, respectively. In order to explore the quenching mechanism of Tm3+:3F 4 level, the fluorescence lifetimes of Tm3+:3F 4 of the 2 at.% Tm, xat.% Dy:Y 2 O 3 ceramics (x = 0, 0.1, 0.5 and 1) were measured to be 4.878 ms, 462 μs, 104 μs and 61 μs, respectively. The possible energy transfer mechanisms between Tm3+ and Dy3+ ions are discussed. The results show that adding Tm3+ ions to Dy:Y 2 O 3 ceramics can effectively enhance the 2.9 μm MIR through energy transfer. [ABSTRACT FROM AUTHOR]

• After co-doping Tb3+ ions, the Ω4/Ω6 increased 1.57 from to 1.66. • The branching ratios of the 3H 4 →3F 4 transition also strengthened. • The decay curve of 3F 4 level doped with different Tb3+ ions concentration decreased. • Tb3+ ion is a productive deactivator that could reduce the filling of 3F 4 mainfold and enhance the emission of 3H 4 →3F 4 transition. Tm3+ and Tb3+ co-doped Y 3 Al 5 O 12 (YAG) ceramics were fabricated by high temperature solid state reaction under oxygen sintering. The absorption spectra, fluorescence spectra and fluorescence decay curves of Tm,Tb:YAG ceramics were measured. The spectral parameters of Tm,Tb:YAG ceramic were calculated. The lifetimes of Tm3+:3F 4 level of Tm,Tb:YAG ceramics were calculated to be 11.28, 2.12, 1.24, 0.63 and 0.49 ms for the Tb3+ doping concentration of 0, 0.1, 0.2, 0.35 at 0.5 at%, respectively. The co-doping Tb3+ ion is a productive deactivator that could reduce the filling of 3F 4 mainfold and enhance the emission of 3H 4 →3F 4 transition. These results indicate that the addition of Tb3+ ions in Tm,Tb:YAG ceramic could be a promising technique for laser operation around 1.5 µm. [ABSTRACT FROM AUTHOR]

In this paper, we report the fabrication of high-quality 5 at. % Er3+ ions doped SrF2 transparent ceramics, the potential candidate materials for a mid-infrared laser-gain medium by hot-pressing at 700 °C for 40 h using a chemically-derived powder. The phase structure, densification, and microstructure evolution of the Er:SrF2 ceramics were systematically investigated. In addition, the grain growth kinetic mechanism of Er:SrF2 was clarified. The results showed lattice diffusion to be the grain growth mechanism in the Er:SrF2 transparent ceramic of which highest in-line transmittance reached 92% at 2000 nm, i.e., very close to the theoretical transmittance value of SrF2 single crystal. Furthermore, the emission spectra showed that the strongest emission band was located at 2735 nm. This means that it is possible to achieve a laser output of approximately 2.7 μm in the 5 at. % Er3+ ions doped SrF2 transparent ceramics. [ABSTRACT FROM AUTHOR]