Search

In this work, flexible Cu2−xS films on nylon membranes are prepared by combining a simple hydrothermal synthesis and vacuum filtration followed by hot pressing. The films consist of Cu2S and Cu1.96S two phases with grain sizes from nano to submicron. Doping Se on the S site not only increases the Cu1.96S content in the Cu2−xS to increase carrier concentration but also modifies electronic structure, thereby greatly improves the electrical properties of the Cu2−xS. Specifically, an optimal composite film with a nominal composition of Cu2−xS0.98Se0.02 exhibits a high power factor of ~150.1 μW m−1 K−2 at 300 K, which increases by ~138% compared to that of the pristine Cu2−xS film. Meanwhile, the composite film shows outstanding flexibility (~97.2% of the original electrical conductivity is maintained after 1500 bending cycles with a bending radius of 4 mm). A four-leg flexible thermoelectric (TE) generator assembled with the optimal film generates a maximum power of 329.6 nW (corresponding power density of 1.70 W m−2) at a temperature difference of 31.1 K. This work provides a simple route to the preparation of high TE performance Cu2−xS-based films. [ABSTRACT FROM AUTHOR]

Copper-sulfide-based materials have attracted noteworthy attention as thermoelectric materials due to rich elemental reserves, non-toxicity, low thermal conductivity, and adjustable electrical properties. However, research on the flexible thermoelectrics of copper sulfide has not yet been reported. In this work, we developed a facile method to prepare flexible Mn-doped Cu2−xS films on nylon membranes. First, nano to submicron powders with nominal compositions of Cu2−xMnyS (y = 0, 0.01, 0.03, 0.05, 0.07) were synthesized by a hydrothermal method. Then, the powders were vacuum-filtrated on nylon membranes and finally hot-pressed. Phase composition and microstructure analysis revealed that the films contained both Cu2S and Cu1.96S, and the size of the grains was ~20–300 nm. By Mn doping, there was an increase in carrier concentration and mobility, and ultimately, the electrical properties of Cu2−xS were improved. Eventually, the Cu2−xMn0.05S film showed a maximum power factor of 113.3 μW m−1 K−2 and good flexibility at room temperature. Moreover, an assembled four-leg flexible thermoelectric generator produced a maximum power of 249.48 nW (corresponding power density ~1.23 W m−2) at a temperature difference of 30.1 K, and had good potential for powering low-power-consumption wearable electronics. [ABSTRACT FROM AUTHOR]

A facile preparation method for flexible p-type CuI/polyvinylpyrrolidone (PVP) nanocomposite thermoelectric (TE) film is developed. First, CuI powder was synthesized by a one-pot method; second, PVP was coated in situ with the CuI powder; third, the CuI/PVP nanocomposite film was prepared on a nylon membrane by vacuum filtration and then hot-pressing. Transmission electron microscopy (TEM) observation indicates that the film consists of CuI nanograins with an average size of ~15 nm and PVP distributed at the inner wall of nanopores and the surface of the CuI nanograins. The composite film shows a large Seebeck coefficient of ~605 µVK−1 and a power factor of ~8.05 µWm−1K−2 at 300 K. The nanocomposite film also exhibits excellent flexibility (~96% of initial electrical conductivity retention after being bent 1000 times along a 4 mm radius rod). A single-leg TE module outputs a voltage of ~3.6 mV when the temperature difference is 6 K. This work provides a fast, simple, and environmentally friendly method by which to prepare flexible CuI/PVP nanocomposite TE film with a large Seebeck coefficient, which could be used as a wearable sensor. [ABSTRACT FROM AUTHOR]

Flexible Ag2Se thermoelectric (TE) films are promising for wearable applications near room temperature (RT). Herein, a Ag2Se film on a nylon membrane with high TE performance was fabricated by a facile method. First, Ag2Se powders were prepared by a microwave-assisted synthesis method using Ag nanowires as a template. Second, the Ag2Se powders were deposited onto nylon via vacuum filtration followed by hot pressing. Through modulating the Ag/Se molar ratio for synthesizing the Ag2Se powders, an optimized Ag2Se film demonstrates a high power factor of 1577.1 μW m−1 K−2 and good flexibility at RT. The flexibility of the Ag2Se film is mainly attributed to the flexible nylon membrane. In addition, a six-leg flexible TE generator (f-TEG) fabricated with the optimized Ag2Se film exhibits a maximum power density of 18.4 W m−2 at a temperature difference of 29 K near RT. This work provides a new solution to prepare high-TE-performance flexible Ag2Se films for f-TEGs. [ABSTRACT FROM AUTHOR]

Highlights: [•] The electronic structure and some transport properties of Mn3Cu4Bi4 was studied used by DFT. [•] The result shows that the Seebeck coefficient of Mn3Cu4Bi4 is isotropic and reaches 30.9μV/K. [•] It is the first time to report the Seebeck coefficient of Mn3Cu4Bi4. [ABSTRACT FROM AUTHOR]

Researches on flexible thermoelectric materials usually focus on conducting polymers and conducting polymer-based composites; however, it is a great challenge to obtain high thermoelectric properties comparable to inorganic counterparts. Here, we report an n-type Ag2Se film on flexible nylon membrane with an ultrahigh power factor ~987.4 ± 104.1 μWm−1K−2 at 300 K and an excellent flexibility (93% of the original electrical conductivity retention after 1000 bending cycles around a 8-mm diameter rod). The flexibility is attributed to a synergetic effect of the nylon membrane and the Ag2Se film intertwined with numerous high-aspect-ratio Ag2Se grains. A thermoelectric prototype composed of 4-leg of the Ag2Se film generates a voltage and a maximum power of 18 mV and 460 nW, respectively, at a temperature difference of 30 K. This work opens opportunities of searching for high performance thermoelectric film for flexible thermoelectric devices. Although flexible thermoelectric materials based on conducting polymers are attractive for energy harvesting, their performance is inferior to their inorganic counterparts. Here, the authors present a facile method to deliver inorganic nanowire films with high power factor and flexibility. [ABSTRACT FROM AUTHOR]

Bi 2 Te 3 and Bi 2 Se 3 nanoplates were synthesized by a microwave-assisted wet chemical method, and Bi 2 Se x Te 3−x (x=1, 2, 3) bulk nanocomposites were then prepared by hot pressing the Bi 2 Te 3 and Bi 2 Se 3 nanoplates at 80 MPa and 723 K in vacuum. The phase composition and microstructures of the bulk samples were characterized by powder X-ray diffraction and field-emission scanning electron microscopy, respectively. The electrical conductivity of the Bi 2 Se x Te 3−x bulk nanocomposites increases with increasing Se content, and the Seebeck coefficient value is negative, showing n-type conduction. The absolute Seebeck coefficient value decreases with increasing Se content. A highest power factor, 24.5 µWcm −1 K −2 , is achieved from the sample of x=1 at 369 K among the studied samples. [ABSTRACT FROM AUTHOR]

In this work, flexible Cu 2-x S films on nylon membranes are prepared by combining a simple hydrothermal synthesis and vacuum filtration followed by hot pressing. The films consist of Cu 2 S and Cu 1.96 S two phases with grain sizes from nano to submicron. Doping Se on the S site not only increases the Cu 1.96 S content in the Cu 2-x S to increase carrier concentration but also modifies electronic structure, thereby greatly improves the electrical properties of the Cu 2-x S. Specifically, an optimal composite film with a nominal composition of Cu 2-x S 0.98 Se 0.02 exhibits a high power factor of ~150.1 μW m -1 K -2 at 300 K, which increases by ~138% compared to that of the pristine Cu 2-x S film. Meanwhile, the composite film shows outstanding flexibility (~97.2% of the original electrical conductivity is maintained after 1500 bending cycles with a bending radius of 4 mm). A four-leg flexible thermoelectric (TE) generator assembled with the optimal film generates a maximum power of 329.6 nW (corresponding power density of 1.70 W m -2 ) at a temperature difference of 31.1 K. This work provides a simple route to the preparation of high TE performance Cu 2-x S-based films.