Search

SiO2/Nb2O5 multilayer thin films were designed for the special application of an aviation lighting system emitting green light. For optical components in this system to meet requirements such as a high transmittance and durability, SiO2/Nb2O5 multilayer thin films of 60 individual layers were fabricated by a plasma-assisted reactive magnetron sputtering method. As a result, the transmittance spectra were confirmed to have a flat top surface and a square bandwidth. The transmittances of the SiO2/Nb2O5 multilayer thin films in the range of 500 nm to 550 nm was approximately 96.14%. The reason for high transmittance was attributed to the almost matching between the designed and fabricated SiO2/Nb2O5 multilayer thin films. It was found that there was little difference in the total thickness between the designed and fabricated SiO2/Nb2O5 multilayer thin films without interlayer diffusion. The surface roughness and hardness of the SiO2/Nb2O5 multilayer thin films on a glass substrate was 2.32 nm ± 0.19 nm and 6.6 GPa, respectively. These results indicate that SiO2/Nb2O5 multilayer thin films can be applied not only to the optical filters used in aviation lighting devices, but also to various optics applications because of high transmittance. [ABSTRACT FROM AUTHOR]

The formation mechanism of Cd–S–Se quantum dots (QDs) with a CdS/CdSe core–shell structure within a silicate glass system was investigated by monitoring the change in the first excitonic absorption peak of CdSe, CdS, and Cd–S–Se QDs as a function of the heat‐treatment (HT) duration. When a silicate glass containing QD formation components for CdSe or CdS single‐phased QDs was heat‐treated, CdSe QDs grew via Ostwald ripening, whereas CdS QDs hardly formed within the given silicate glass matrix. When the glass, including CdO, ZnSe, and ZnS, was utilized for the synthesis of Cd–S–Se QDs within the glass matrix, Cd–S–Se QDs were successfully formed and exhibited similar growth behavior to CdSe QDs during the initial stage of HT. The structural changes in the QD‐embedded glasses during HT were also monitored by Raman spectroscopy and discussed, and a possible formation mechanism of CdSe/CdS core–shell‐structured QDs within silicate glasses is suggested. [ABSTRACT FROM AUTHOR]

We successfully fabricated Y2O3:RE3+ (RE = Eu, Tb, and Dy) core and core–shell nanophosphors by the molten salt method and sol–gel processes with Y2O3 core size of the order of 100~150 nm. The structural and morphological studies of the RE3+-doped Y2O3 nanophosphors are analyzed by using XRD, SEM and TEM techniques, respectively. The concentration and annealing temperature dependent structural and luminescence characteristics were studied for Y2O3:RE3+ core and core–shell nanophosphors. It is observed that the XRD peaks became narrower as annealing temperature increased in the core–shell nanophosphor. This indicates that annealing at higher temperature improves the crystallinity which in turn enhances the average crystallite size. The emission intensity and quantum yield of the Eu3+-doped Y2O3 core and core–shell nanoparticles increased significantly when annealing temperature is varied from 450 to 550 °C. No considerable variation was noticed in the case of Y2O3:Tb3+ and Y2O3:Dy3+ core and core–shell nanophosphors. [ABSTRACT FROM AUTHOR]

In this paper, the glass systems, TeO2–ZnO–BaO (TZB), TeO2–ZnO–BaO–Nb2O5 (TZB–Nb) and TeO2–ZnO–BaO–MoO3 (TZB–Mo), were fabricated by the traditional melt-quench protocol for use as mid-infrared (mid-IR) transmitting optical material. The effect of Nb2O5 and MoO3 on the key glass material properties was studied through various techniques. From the Raman analysis, it was found that the structural modification was clear with the addition of both Nb2O5 and MoO3 in the TZB system. The transmittance of studied glasses was measured and found that the optical window covered a region from 0.4 to 6 μm. The larger linear refractive index was obtained for the Nb2O5-doped TZB glass system than that of other studied systems. High glass transition temperature, low thermo-mechanical coefficient and high Knoop hardness were noticed in the Nb2O5-doped TZB glass system due to the increase in cross-linking density and rigidity in the tellurite network. The results suggest that the Nb2O5-doped TZB optical glasses could be a promising material for mid-infrared transmitting optics. [ABSTRACT FROM AUTHOR]