Search

ObjectivesAcetate and lactate are important cariogenic acids produced by oral bacteria. They produced different residual dentin structures in artificial lesions of similar depth. We evaluated if such lesions responded in the same way to a polymer-induced-liquid-precursor (PILP) remineralization.DesignDentin blocks obtained from human third molars, divided into 6 groups (n=3). Blocks were demineralized with acetate (66h) or lactate (168h) buffer at pH 5.0 to create 140μm target lesion depths. A-DEM and L-DEM groups received no remineralization. Other groups were remineralized for 14days. 100μg/mL polyaspartate was added into the remineralizing buffer for A-PIL and L-PIL, whereas A-CAP and L-CAP were treated with the same solution but without polyaspartate. Cross-sectioned blocks were examined for shrinkage and AFM-topography. Line profiles of reduced elastic modulus (Er) were obtained by AFM-based nanoindentation across the lesion. Ultrastructures were examined with TEM.ResultsA-PIL and L-PIL recovered in shrinkage to the original height of the dentin and it appeared normal with tubules, with increases in Er at both outer flat and inner sloped zones. At the sloped zone, acetate lesions lost more Er but recovery rate after PILP was not statistically different from lactate lesions. A-CAP and L-CAP showed surface precipitates, significantly less recovery in shrinkage or Er as compared to PILP groups. TEM-ultrastructure of PILP groups showed similar structural and mineral components in the sloped zone for lesions produced by either acid.ConclusionsThe PILP process provided significant recovery of both structure and mechanical properties for artificial lesions produced with acetate or lactate.

Dentinogenesis imperfecta type II (DGI-II) lacks intrafibrillar mineral with severe compromise of dentin mechanical properties. A Dspp knockout (Dspp-/-) mouse, with a phenotype similar to that of human DGI-II, was used to determine if poly-L-aspartic acid [poly(ASP)] in the "polymer-induced liquid-precursor" (PILP) system can restore its mechanical properties. Dentin from six-week old Dspp-/- and wild-type mice was treated with CaP solution containing poly(ASP) for up to 14 days. Elastic modulus and hardness before and after treatment were correlated with mineralization from Micro x-ray computed tomography (Micro-XCT). Transmission electron microscopy (TEM)/Selected area electron diffraction (SAED) were used to compare matrix mineralization and crystallography. Mechanical properties of the Dspp-/- dentin were significantly less than wild-type dentin and recovered significantly (P < 0.05) after PILP-treatment, reaching values comparable to wild-type dentin. Micro-XCT showed mineral recovery similar to wild-type dentin after PILP-treatment. TEM/SAED showed repair of patchy mineralization and complete mineralization of defective dentin. This approach may lead to new strategies for hard tissue repair.

With the aging population, there is a growing need for mineralized tissue restoration and synthetic bone substitutes. Previous studies have shown that a polymer-induced liquid-precursor (PILP) process can successfully mineralize collagen substrates to achieve compositions found in native bone and dentin. This process also leads to intrafibrillar apatitic crystals with their [001] axes aligned roughly parallel to the long axis of the collagen fibril, emulating the nanostructural organization found in native bone and dentin. When demineralized bovine bone was remineralized via the PILP process using osteopontin (OPN), the samples were able to activate mouse marrow-derived osteoclasts to similar levels to those of native bone, suggesting a means for fabricating bioactive bone substitutes that could trigger remodeling through the native bone multicellular unit (BMU). In order to determine if OPN derived from bovine milk could be a cost-effective process-directing agent, the mineralization of type I collagen scaffolds using this protein was compared to the benchmark polypeptide of polyaspartic acid (sodium salt; pAsp). In this set of experiments, we found that OPN led to much faster and more uniform mineralization when compared with pAsp, making it a cheaper and commercially attractive alternative for mineralized tissue restorations.

Mineralized collagen composites are of interest because they have the potential to provide a bone-like scaffold that stimulates the natural processes of resorption and remodeling. Working towards this goal, our group has previously shown that the nanostructure of bone can be reproduced using a polymer-induced liquid-precursor (PILP) process, which enables intrafibrillar mineralization of collagen with hydroxyapatite to be achieved. This prior work used polyaspartic acid (pASP), a simple mimic for acidic non-collagenous proteins, to generate nanodroplets/nanoparticles of an amorphous mineral precursor which can infiltrate the interstices of type-I collagen fibrils. In this study we show that osteopontin (OPN) can similarly serve as a process-directing agent for the intrafibrillar mineralization of collagen, even though OPN is generally considered a mineralization inhibitor. We also found that inclusion of OPN in the mineralization process promotes the interaction of mouse marrow-derived osteoclasts with PILP-remineralized bone that was previously demineralized, as measured by actin ring formation. While osteoclast activation occurred when pASP was used as the process-directing agent, using OPN resulted in a dramatic effect on osteoclast activation, presumably because of the inherent arginine-glycine-aspartate acid ligands of OPN. By capitalizing on the multifunctionality of OPN, these studies may lead the way to producing biomimetic bone substitutes with the capability of tailorable bioresorption rates., (Copyright © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.)

It was hypothesized that applying the polymer-induced liquid-precursor (PILP) system to artificial lesions would result in time-dependent functional remineralization of carious dentin lesions that restores the mechanical properties of demineralized dentin matrix. 140 µm deep artificial caries lesions were remineralized via the PILP process for 7-28 days at 37°C to determine temporal remineralization characteristics. Poly-L-aspartic acid (27 KDa) was used as the polymeric process-directing agent and was added to the remineralization solution at a calcium-to-phosphate ratio of 2.14 (mol/mol). Nanomechanical properties of hydrated artificial lesions had a low reduced elastic modulus (E(R) = 0.2 GPa) region extending about 70 μm into the lesion, with a sloped region to about 140 μm where values reached normal dentin (18-20 GPa). After 7 days specimens recovered mechanical properties in the sloped region by 51% compared to the artificial lesion. Between 7-14 days, recovery of the outer portion of the lesion continued to a level of about 10 GPa with 74% improvement. 28 days of PILP mineralization resulted in 91% improvement of E(R) compared to the artificial lesion. These differences were statistically significant as determined from change-point diagrams. Mineral profiles determined by micro x-ray computed tomography were shallower than those determined by nanoindentation, and showed similar changes over time, but full mineral recovery occurred after 14 days in both the outer and sloped portions of the lesion. Scanning electron microscopy and energy dispersive x-ray analysis showed similar morphologies that were distinct from normal dentin with a clear line of demarcation between the outer and sloped portions of the lesion. Transmission electron microscopy and selected area electron diffraction showed that the starting lesions contained some residual mineral in the outer portions, which exhibited poor crystallinity. During remineralization, intrafibrillar mineral increased and crystallinity improved with intrafibrillar mineral exhibiting the orientation found in normal dentin or bone.

Bone is an organic-inorganic composite which has hierarchical structuring that leads to high strength and toughness. The nanostructure of bone consists of nanocrystals of hydroxyapatite embedded and aligned within the interstices of collagen fibrils. This unique nanostructure leads to exceptional properties, both mechanical and biological, making it difficult to emulate bone properties without having a bone-like nanostructured material. A primary goal of our group's work is to use biomimetic processing techniques that lead to bone-like structures. In our prior studies, we demonstrated that intrafibrillar mineralization of porous collagen sponges, leading to a bone-like nanostructure, can be achieved using a polymer-induced liquid precursor (PILP) mineralization process. The objective of this study was to investigate the use of this polymer-directed crystallization process to mineralize dense collagen substrates. To examine collagen scaffolds that truly represent the dense-packed matrix of bone, manatee bone was demineralized to isolate its collagen matrix, consisting of a dense, lamellar osteonal microstructure. This biogenic collagen scaffold was then remineralized using polyaspartate to direct the mineralization process through an amorphous precursor pathway. The various conditions investigated included polymer molecular weight, substrate dimension and mineralization time. Mineral penetration depths of up to 100 μms were achieved using this PILP process, compared to no penetration with only surface precipitates observed for the conventional crystallization process. Electron microscopy, wide-angle X-ray diffraction and thermal analysis were used to characterize the resulting hydroxyapatite/collagen composites. These studies demonstrate that the original interpenetrating bone nanostructure and osteonal microstructure could be recovered in a biogenic matrix using the PILP process., (Copyright © 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.)

The nanostructure of bone has been replicated using a polymer-induced liquid-precursor (PILP) mineralization process. This polymer-mediated crystallization process yields intrafibrillar mineralization of collagen with uniaxially-oriented hydroxyapatite crystals. The process-directing agent, an anionic polymer which we propose mimics the acidic non-collagenous proteins associated with bone formation, sequesters calcium and phosphate ions to form amorphous precursor droplets that can infiltrate the interstices of collagen fibrils. In search of a polymeric agent that produces the highest mineral content in the shortest time, we have studied the influence of various acidic polymers on the in vitro mineralization of collagen scaffolds via the PILP process. Among the polymers investigated were poly-L aspartic acid (PASP), poly-L-glutamic acid (PGLU), polyvinylphosphonic acid (PVPA), and polyacrylic acid (PAA). Our data indicate that PASP and the combination of PGLU/PASP formed stable mineralization solutions, and yielded nano-structured composites with the highest mineral content. Such studies contribute to our goal of preparing biomimetic bone graft substitutes with composition and structure that mimic bone.

Bone is an organic-inorganic composite consisting primarily of collagen fibrils and hydroxyapatite crystals intricately interlocked to provide skeletal and metabolic functions. Non-collagenous proteins (NCPs) are also present, and although only a minor component, the NCPs are thought to play an important role in modulating the mineralization process. During secondary bone formation, an interpenetrating structure is created by intrafibrillar mineralization of the collagen matrix. Many researchers have tried to develop bone-like collagen-hydroxyapatite (HA) composites via the conventional crystallization process of nucleation and growth. While those methods have been successful in inducing heterogeneous nucleation of HA on the surface of collagen scaffolds, they have failed to produce a composite with the interpenetrating nanostructured architecture of bone. Our group has shown that intrafibrillar mineralization of type I collagen can be achieved using a polymer-induced liquid-precursor (PILP) process. In this process, acidic polypeptides are included in the mineralization solution to mimic the function of the acidic NCPs, and in vitro studies have found that acidic peptides such as polyaspartate induce a liquid-phase amorphous mineral precursor. Using this PILP process, we have been able to prepare collagen-HA composites with the fundamental nanostructure of bone, wherein HA nanocrystals are embedded within the collagen fibrils. This study shows that through further optimization a very high degree of mineralization can be achieved, with compositions matching that of bone. Synthetic collagen sponges were mineralized with calcium phosphate while analyzing various parameters of the reaction, with the focus of this report on the molecular weight of the polymeric process-directing agent. In order to determine whether intrafibrillar mineralization was achieved, an in-depth characterization of the mineralized composites was performed, including wide-angle X-ray diffraction, electron microscopy and thermogravimetric analyses. The results of this work lead us closer to the development of bone-like collagen-HA composites that could become the next generation of synthetic bone grafts., (2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.)

In this research, screening and central composite experimental designs are used to determine the effect of various factors on the aggregation and dispersion characteristics of previously grown calcium oxalate monohydrate (COM) crystals in artificial urinary environments of controlled variables. The variables examined are pH and calcium, oxalate, pyrophosphate, citrate, and protein concentrations in ultrapure water and artificial urine. Optical density measurements, particle size analysis, optical microscopy, AFM force measurements, and protein adsorption have been used to assess the state of aggregation and dispersion of the COM crystals and to elucidate the mechanisms involved in such a complex system. The data indicate that our model protein, mucin, acts as a dispersant. This is attributed to steric hindrance resulting from the adsorbed mucoprotein. Oxalate, however, promotes aggregation. Interesting interactions between protein and oxalate along with protein and citrate are observed. Such interactions (synergistic or antagonistic) are found to depend on the concentrations of these species. Surface responses for these interactions are presented and discussed in this paper. In summary, solution, surface, and interface chemistries interact in a complex manner in the physiological environment to either inhibit or promote aggregation, and an understanding of such interactions may help determine and control the factors affecting kidney stone formation.

•  The chemical nature and biological basis for crystal deposition in epidermal subcuticular areas are reported here for the angiosperm Dracaena sanderiana. •  Position, development and identification of crystals in adult leaves of D. sanderiana was carried out using X-ray diffraction, crystal morphology and scanning and transmission electron microscopy techniques. •  Numerous small (< 1-6 µm) calcium oxalate monohydrate crystals were found between the primary epidermal cell wall and the cuticle. Their formation was highly specific and predictable with respect to location and relative timing of development during leaf ontogeny. The crystals were perisplasmic as, at formation, the nascent epidermal cell wall was external to the crystals. Cuticular crystallization of calcium oxalate monohydrate in D. sanderiana occurred in crystal chambers situated between the plasma membrane and the primary cell wall. Crystal deposition did not occur in developing guard cells. •  The spatial pattern of calcium oxalate monohydrate within the epidermal cells, orientation of the crystallographic axes and the existence of crystal chambers outside the plasma membrane suggest biologically controlled crystal deposition in D. sanderiana.