Search

The future generation of modern illumination should not only be cheap and highly efficient, but also demonstrate high quality of light, light which allows better color differentiation and fidelity. Here we are presenting a novel approach to create a white solid-state light source providing ultimate color rendition necessary for a number of applications. The proposed semi-hybrid device combines a monolithic blue-cyan light emitting diode (MBC LED) with a green-red phosphor mixture. It has shown a superior color rendering index (CRI), 98.6, at correlated color temperature of around 3400 K. The MBC LED epi-structure did not suffer from the efficiency reduction typical for monolithic multi-color emitters and was implemented in the two most popular chip designs: “epi-up” and “flip-chip”. Redistribution of the blue and cyan band amplitudes in the white-light emission spectrum, using the operating current, is found to be an effective tool for fine tuning the color characteristics. (Figure presented.).

We demonstrate a phosphor free, dichromatic GaN-based monolithic white LED with vertically stacked green and blue emitting multiple quantum wells. The optimal thickness of GaN barrier layer between green and blue quantum wells used is 8 nm. This device can be tuned over a wide range of correlated color temperature (CCT) to achieve warm white (CCT = 3600 K) to cool white (CCT = 13,000 K) emission by current modulation from 2.3 A/cm2 to 12.9 A/cm2. It is also demonstrated for the first time that a color rendering index (CRI) as high as 67 can be achieved with such a dichromatic source. The observed CCT and CRI tunability is associated with the spectral power evolution due to the pumping-induced carrier redistribution.

External quantum efficiency of industrial-grade green InGaN light-emitting diodes (LEDs) has been measured in a wide range of operating currents at various temperatures from 13 K to 300 K. Unlike blue LEDs, the efficiency as a function of current is found to have a multi-peak character, which could not be fitted by a simple ABC-model. This observation correlated with splitting of LED emission spectra into two peaks at certain currents. The characterization data are interpreted in terms of non-uniformity of the LED active region, which is tentatively attributed to extended defects like V-pits. We suggest a new approach to evaluation of temperature-dependent light extraction and internal quantum efficiencies taking into account the active region non-uniformity. As a result, the temperature dependence of light extraction and internal quantum efficiencies have been evaluated in the temperature range mentioned above and compared with those of blue LEDs.

External quantum efficiency of industrial-grade green InGaN light-emitting diodes (LEDs) has been measured in a wide range of operating currents at various temperatures from 13 K to 300 K. Unlike blue LEDs, the efficiency as a function of current is found to have a multi-peak character, which could not be fitted by a simple ABC-model. This observation correlated with splitting of LED emission spectra into two peaks at certain currents. The characterization data are interpreted in terms of non-uniformity of the LED active region, which is tentatively attributed to extended defects like V-pits. We suggest a new approach to evaluation of temperature-dependent light extraction and internal quantum efficiencies taking into account the active region non-uniformity. As a result, the temperature dependence of light extraction and internal quantum efficiencies have been evaluated in the temperature range mentioned above and compared with those of blue LEDs.

Internal quantum efficiency (IQE) of a blue high-brightness InGaN/GaN light-emitting diode (LED) was evaluated from the external quantum efficiency measured as a function of current at various temperatures ranged between 13 and 440 K. Processing the data with a novel evaluation procedure based on the ABC-model, we have determined the temperature-dependent IQE of the LED structure and light extraction efficiency of the LED chip. Separate evaluation of these parameters is helpful for further optimization of the heterostructure and chip designs. The data obtained enable making a guess on the temperature dependence of the radiative and Auger recombination coefficients, which may be important for identification of dominant mechanisms responsible for the efficiency droop in III-nitride LEDs. Thermal degradation of the LED performance in terms of the emission efficiency is also considered.

Efficiency of commercial 620 nm InAlGaP Golden Dragon-cased high-power LEDs has been studied under extremely high pump current density up to 4.5 kA/cm2 and pulse duration from microsecond down to sub-nanosecond range. No efficiency decrease and negligible red shift of the emission wavelength is observed in the whole range of drive currents at nanosecond-range pulses with duty cycles well below 1%. Analysis of the pulse-duration dependence of the LED efficiency and emission spectrum suggests the active region overheating to be the major mechanism of the LED efficiency reduction at higher pumping, dominating over the electron overflow and Auger recombination.

Two blue (450 nm) light–emitting diodes (LED), which only differ in top p-GaN layer growth conditions, were comparatively investigated. I-V, C-V, TLM, Electroluminescence (EL) and Photoluminescence (PL) techniques were applied to clarify a correlation between MOCVD carrier gas and internal properties. The A-structure grown in the pure N2 environment demonstrated better parameters than the B-structure grown in the N2/H2 (1:1) gas mixture. The mixed growth atmosphere leaded to an increase of sheet resistances of p-GaN layer. EL and PL measurements confirmed the advantage of the pure N2 utilization, and C(VR) measurement pointed the increase of static charge concentration near the p-GaN interface in the B structure.

In this paper, current-dependent emission spectra and efficiency measured on the same AlGaInP red light-emitting diode (LED) pumped with the current pulses of very different durations are recorded. This enabled for the first time distinguishing between high-carrier concentration and self-heating effects on the efficiency decline at high current magnitudes. The electron leakage to the p-side of the LED structure, which is the major mechanism of the efficiency reduction, is found to rise substantially when the device self-heating starts to develop. As a result, in comparison to continuous-wave excitation, driving the LED with sub-microsecond current pulses allows suppressing the device self-heating and, eventually, increasing the operating current by an order of magnitude without noticeable efficiency losses. Based on the reduced ABC-model, neglecting Auger recombination, the light extraction efficiency, injection efficiency, and internal quantum efficiency of the LED are estimated, suggesting light extraction to be the most critical factor for the overall efficiency of the LED. The coupled spectral/power LED characterization using the variable-duration current pulse pumping is found to be an effective approach for analyzing mechanisms of the device operation.

Internal Quantum Efficiency (IQE) of two-colour monolithic white light emitting diode (LED) was measured by temperature dependant electro-luminescence (TDEL) and analysed with modified rate equation based on ABC model. External, internal and injection efficiencies of blue and green quantum wells were analysed separately. Monolithic white LED contained one green InGaN QW and two blue QWs being separated by GaN barrier. This paper reports also the tunable behaviour of correlated colour temperature (CCT) in pulsed operation mode and effect of self-heating on device performance.

A simple experimental method of light emitting diode (LED) injection efficiency (IE) determination was suggested. IE and internal quantum efficiency (IQE) calculation is an actual and difficult problem in LED science. In this paper IE and IQE of blue LEDs were determined separately. The method is based on electroluminescence data fitting by the modified rate equation model. Efficiency droop caused by Auger recombination and poor injection were taken into account. Only one reasonable assumption was accepted during the calculations: IE tends to 1 at low current densities.