Search

We characterize composition and structure of ultrathin nickel silicide during formation from 3 nm Ni films on Si(1 0 0) using in-situ high-resolution ion scattering and high-resolution transmission electron microscopy. We show the transition to occur in discrete steps, in which an intermediate phase is observed within a narrow range of temperature from 230 °C to 290 °C. The film composition of this intermediate phase is found to be 50% Ni:50% Si, without evidence for long-range structure, indicating the film to be a homogeneous monosilicide NiSi phase. The final phase is resemblant of the cubic disilicide NiSi2, but with slightly off-stoichiometric composition of 38% Ni and 62% Si. Along the [1 0 0] axis, the lattices of the film and the substrate are found in perfect alignment. Due to the epitaxial growth of the silicide, a contraction of the c lattice constant of the film by 0.7–1% is detected.

The authors have studied the reaction between a Ge (100) substrate and thin layers of Ni ranging from 2 to 10 nm in thickness. The formation of metal-rich Ni5Ge3 was found to precede that of the monogermanide NiGe by means of real-time in situ x-ray diffraction during ramp-annealing and ex situ x-ray pole figure analyses for phase identification. The observed sequential growth of Ni5Ge3 and NiGe with such thin Ni layers is different from the previously reported simultaneous growth with thicker Ni layers. The phase transformation from Ni5Ge3 to NiGe was found to be nucleationcontrolled for Ni thicknesses < 5 nm, which is well supported by thermodynamic considerations. Specifically, the temperature for the NiGe formation increased with decreasing Ni (rather Ni5Ge3) thickness below 5 nm. In combination with sheet resistance measurement and microscopic surface inspection of samples annealed with a standard rapid thermal processing, the temperature range for achieving morphologically stable NiGe layers was identified for this standard annealing process. As expected, it was found to be strongly dependent on the initial Ni thickness.

This letter presents a proof-of-concept process for tunable, self-limiting growth of ultrathin epitaxial NiSi2 films on Si (100). The process starts with metal sputter-deposition, followed by wet etching and then silicidation. By ionizing a fraction of the sputtered Ni atoms and biasing the Si substrate, the amount of Ni atoms incorporated in the substrate after wet etching can be controlled. As a result, the thickness of the NiSi2 films is increased from 4.7 to 7.2 nm by changing the nominal substrate bias from 0 to 600 V. The NiSi2 films are characterized by a specific resistivity around 50 mu Omega cm.

This letter reports on a process scheme to obtain highly reproducible Ni1−xPtx silicide films of 3–6 nm thickness formed on a Si(100) substrate. Such ultrathin silicide films are readily attained by sputter deposition of metal films, metal stripping in wet chemicals, and final silicidation by rapid thermal processing. This process sequence warrants an invariant amount of metal intermixed with Si in the substrate surface region independent of the initial metal thickness, thereby leading to a self-limiting formation of ultrathin silicide films. The crystallographic structure, thickness, uniformity, and morphological stability of the final silicide films depend sensitively on the initial Pt fraction.

Non-native mammals are major drivers of ecosystem change and biodiversity loss; this is especially apparent on islands. However, techniques exist to remove non-native mammals, providing a powerful conservation tool. Conservation practitioners are now targeting larger islands for restoration. Leveraging existing and developing new techniques and technologies will prove critical to successful eradications on large islands. Using the removal of introduced goats (Capra hircus) from Santiago Island, Galapagos as a case study, we present a suite of Geographic Information System (GIS) tools that aid island conservation actions. GIS tools were incorporated into the three phases of the eradication campaign: planning, hunting, and monitoring. Further, these tools were adopted for three eradication techniques: ground-based hunting, aerial hunting by helicopter, and Judas goats. These geographic approaches provide a foundation for statistical, spatial, and economic analyses that should increase the capability and efficiency of removal campaigns. Given limited conservation funds and the dire status of many insular species, efficiently removing non-native mammals from islands is of paramount global conservation importance.

Français, Palmaro Collections Pouchet