This study investigates thermal transport across nanocrystalline diamond/AlGaN interfaces, crucial for enhancing thermal management in AlGaN/AlGaN-based devices. Chemical vapor deposition growth of diamond directly on AlGaN resulted in a disordered interface with a high thermal boundary resistance (TBR) of 20.6 m^2-K/GW. We employed sputtered carbide interlayers (e.g., $B_4C$, $SiC$, $B_4C/SiC$) to reduce thermal boundary resistance in diamond/AlGaN interfaces. The carbide interlayers resulted in record-low thermal boundary resistance values of 3.4 and 3.7 m^2-K/GW for Al$_{0.65}$Ga$_{0.35}$N samples with $B_4C$ and $SiC$ interlayers, respectively. STEM imaging of the interface reveals interlayer thicknesses between 1.7-2.5 nm, with an amorphous structure. Additionally, Fast-Fourier Transform (FFT) characterization of sections of the STEM images displayed sharp crystalline fringes in the AlGaN layer, confirming it was properly protected from damage from hydrogen plasma during the diamond growth. In order to accurately measure the thermal boundary resistance we develop a hybrid technique, combining time-domain thermoreflectance and steady-state thermoreflectance fitting, offering superior sensitivity to buried thermal resistances. Our findings underscore the efficacy of interlayer engineering in enhancing thermal transport and demonstrate the importance of innovative measurement techniques in accurately characterizing complex thermal interfaces. This study provides a foundation for future research in improving thermal properties of semiconductor devices through interface engineering and advanced measurement methodologies.

We report on the demonstration of metalorganic vapor phase epitaxy-regrown (MOVPE) ohmic contacts in an all MOVPE-grown $\beta$-Ga$_2$O$_3$ metal-semiconductor field effect transistor (MESFET). The low-temperature (600$^{\circ}$C) heavy (n$^{+}$) Si-doped regrown layers exhibit extremely high conductivity with sheet resistance of 73 $\Omega$/$\square$ and record low metal/n$^{+}$-Ga$_2$O$_3$ contact resistance of 80 m$\Omega$.mm and specific contact resistivity of 8.3$\times$10$^{-7}$ $\Omega$.cm$^{2}$ were achieved. The fabricated MESFETs exhibit a maximum drain-to-source current of 130 mA/mm, a high I$_{ON}$/I$_{OFF}$ of $>$10$^{10}$ with a high power FOM of 25 MW/cm$^{2}$ were achieved without any field plates. Nanoparticle-assisted Raman thermometry, thermal modeling, and infrared thermography were performed to assess the device self-heating under the high current and power conditions. This demonstration shows the promise of MOVPE technique for the realization of high-performance lateral $\beta$-Ga$_2$O$_3$ devices and also highlights the need for device-level thermal management.