Search

This research investigated the influence of adding cellulose nanofiber (CNF) on the rheology and hardened properties of self-compacting concrete (SCC). The CNFs were produced from wastepaper through chemical treatment and added as 0.25%, 0.50%, 1%, 2%, and 3% by weight of cement in SCC. The results revealed that the increase in the content of CNF caused the decrease in slump flow diameter (SFD), and the lowest SFD of 600 mm was achieved at 2% CNF. In addition, the T50 flow and unit weight increased with the increase in the content of CNF, and the maximum values of 5 s and 2.6 kg/m3 were achieved at 2% and 3% CNF, respectively. Furthermore, the compressive strength increased with an increase in curing age and CNF content (until 0.5%), and the maximum value of compressive strength was achieved as 89 MPa for 0.5% CNF at 28-days of curing. The dry density results increased with the increase in CNF contents at 7-days of curing. The ultrasound pulse velocity and strength ultrasound decreased with the increase in CNF contents. The results showed that the inclusion of CNF improved the microstructure and formed crack bridging. In conclusion, CNF (up to 0.5%) can be used for the production of SCC.

The absence of biodegradability exhibited by plastics is a matter of significant concern among environmentalists and scientists on a global scale. Therefore, it is essential to figure out potential pathways for the use of recycled plastics. The prospective applications of its utilisation in concrete are noteworthy. The use of recycled plastic into concrete, either as a partial or complete substitution for natural aggregates, addresses the issue of its proper disposal besides contributing to the preservation of natural aggregate resources. Furthermore, the use of agricultural wastes has been regarded as a very promising waste-based substance in the industry of concrete manufacturing, with the aim of fostering the creation of an environmentally sustainable construction material. This paper illustrates the impact of nano sunflower ash (NSFA) and nano walnut shells ash (NWSA) on durability (compressive strength and density after exposure to 800 °C and sulphate attack), mechanical properties (flexural, splitting tensile and compressive strength) and fresh characteristics (slump flow diameter, T50, V-funnel flow time, L-box height ratio, segregation resistance and density) of lightweight self-compacting concrete (LWSCC). The waste walnut shells and local Iraqi sunflower were calcinated at 700 ± 50 °C for 2 h and milled for 3 h using ball milling for producing NSFA and NWSA. The ball milling succeeded in reducing the particle size lower than 75 nm for NSFA and NWSA. The preparation of seven LWSCC concrete mixes was carried out to obtain a control mix, three mixtures were created using 10%, 20% and 30% NWSA, and the other three mixtures included 10%, 20% and 30% NSFA. The normal weight coarse aggregates were substituted by the plastic waste lightweight coarse aggregate with a ratio of 75%. The fresh LWSCC passing capacity, segregation resistance, and filling capability were evaluated. The hardened characteristics of LWSCC were evaluated by determining the flexural and splitting tensile strength at 7, 14 and 28 days and the compressive strength was measured at 7, 14, 28 and 60 days. Dry density and compressive strength were measured after exposing mixes to a temperature of 800 °C for 3 h and immersed in 10% magnesium sulphate attack. The results demonstrated that the LWSCC mechanical characteristics were reduced when the percentages of NWSA and NSFA increased, except for 10% NWSA substitution ratio which had an increase in splitting tensile strength test and similar flexural strength test to the control mixture. A minor change in mechanical characteristics was observed within the results of LWSCC dry density and compressive strength incorporating various NSFA and NWSA` contents after exposing to temperature 800 °C and immersed in 10% magnesium sulphate attack. Furthermore, according to the findings, it is possible to use a combination of materials consisting of 10-20% NSFA and 10-20% NWSA to produce LWSCC., (© 2024. The Author(s).)

In this work, carbon-based nanomaterials such as active carbon which is prepared from common sunflower (Helianthus annuus) seed shell, and the characterization of the activated carbon NPs were studied using FTIR (Fourier transform infrared spectroscopy), XRD, SEM, EDS, and DTA techniques. Activated carbon NPs have been used in the adsorption of Pb(II), Cd(II), and Cr(III) ions from the aqueous phase. The results showed the highest adsorption efficiency was 99.9%, 92.45%, and 98% for Pb(II), Cd(II), and Cr(III) ions respectively at a temperature of 25 °C, pH = 7-9, and a time of 60 and 180 min, in addition to the accordance of the adsorption models for activated carbon with the Freundlich isotherm model at the value of R 2 (0.9976, 0.9756, and 0.9907) and Langmuir isotherm model (0.966, 0.999, and 0.9873) of the Pb(II), Cd(II), and Cr(III) ions, respectively. We conclude the possibility of using activated carbon to have an extremely high sorption capacity across the conditions tested, with the highest adsorption efficiency having been >99% for Pb(II), Cd(II), and Cr(III) ions within the pH range 7-9 and a contact time of 60 to 180 min., (© 2024. The Author(s), under exclusive licence to Springer Nature Switzerland AG.)