Search

This paper focuses on the in-plane compression mechanism of two-dimensional biaxial braided composite laminates under quasi-static compression and dynamic compression. Three types of specimens with different off-axial angles in respect of OA00, OA60, and OA90 were employed for compression experiments. The surface damage process of the specimen was recorded using optical camera and infrared thermal imaging technology. The internal damage morphology of the tested specimens was analyzed by X-ray computed tomography. The progressive damage behavior of braiding yarns and matrix resin was simulated by a three-dimensional meso-level finite element model. Experimental and simulation results revealed that the off-axial angle significantly affects mechanical properties and damage mechanisms. The stress distribution and compression deformation of braiding yarns are affected by the boundary conditions of load-bearing yarn, which relies on the off-axial angle. The stress of OA00 specimen is concentrated at the interface of yarn and matrix resin. The failure mode of OA00 specimen is dominated by the shear band, which is induced by the interface microcracks between yarn and matrix resin. The stress of OA60 and OA90 specimens are concentrated at the undulation position of the braiding yarn. The critical failure mode of OA60 and OA90 specimens is delamination induced by interlaminar microcracks. The OA60 specimen achieves a better compression response with respect to bearing the load and absorbing the fracture energy because the sub-laminate that is formed after delamination can continue to bear the load until its intralaminar fracture occurs. [ABSTRACT FROM AUTHOR]

• Difference of damage modes caused by the boundary conditions of primary load-bearing yarns. • Straightening effect of braided yarns with undulations under low-velocity impact. • Variation of off-axial angles leading to the transition of failure modes. The sensitivity of off-axial angle on impact response was investigated by experimental and numerical methods in this work. Three types of braided laminates with different on/off-axial angles in terms of OA00, OA225 and OA45 were prepared and low-velocity impact tests with various energy levels were performed. Meso-level finite element model (FEM) was also developed to reveal impact damage initiation and development. We discovered that the boundary condition of primary load-bearing yarns depending on the off-axial angles caused the difference of structural deformation and stress distribution of braiding yarns during impact process. Due to the restriction of the pressurized tips, the straightening effect of primary load-bearing yarns with heavy waviness caused its out-of-plane movement and related main cracks in OA00 specimen. In addition, the matrix resin cracks were found at the edge of the specimen because of in-plane shear movement of braiding yarns. As for OA45 specimen, more evident bending deformation was observed, resulting in elevated tensile stress of braiding yarns on non-impact side. The variation of off-axial angle from 0 to 45 degree led to the failure mode transforming from the extensive matrix damage on specimen edge to the severe fiber breakage on non-impact side. As a medium off-axial angle, OA225 specimen exhibited a mixture failure mode to resist impact and achieved excellent performance with respect to higher peak force and delayed load dropping. [Display omitted] [ABSTRACT FROM AUTHOR]

Braided composite laminates allow a reinforcement architecture design method of varying ply-to-ply braided structure instead of rotating fiber orientation in traditional unidirectional laminates. The stacking sequence sensitivities of braided laminates subjected to low-velocity impact were experimentally studied. Uniform ([±45° 6 ]) and non-uniform ([±30° 2 /±45° 2 /±60° 2 ]) architectures were designed to evaluate the effect of braided structure on impact performance. In addition, non-uniform laminate was impacted on both sides to identify the role of impact side on the failure mode. Quasi-static indentation was conducted to understand the damage initiation and propagation of braided laminates. The experimental results show that braided ply with high crimp level in impact side induced the main cracks along the load-carrying yarn, causing that the laminate failed in a kink-band dominated mode. For braided ply with low crimp level, a micro-buckling damage was found in the impact side, leading to the delamination dominated failure mode. It was also found that uniform braided laminate presents inferior impact resistance with respect to lower peak load and more concentrated damage because the kink-band can propagate into the specimen along braiding yarn easily. [ABSTRACT FROM AUTHOR]