Search

Abstract: A carbon supported PtNi/C electrocatalyst synthesized via a polyol process was characterized by XRD, TEM and voltammetry techniques. The XRD analysis showed a decreased lattice constant of Pt for the PtNi/C catalyst compared with the Pt/C, indicating partial PtNi alloy formed. The PtNi/C exhibited enhanced mass activity towards methanol oxidation reaction as well as decreased CO stripping currents in alkaline media compared with the Pt/C. Density functional theory studies revealed the electronic structure modification of Pt by Ni atoms and weakened CO adsorption energy on the Pt3Ni than on the Pt4 clusters, which may account for the increased MOR activity. [ABSTRACT FROM AUTHOR]

Abstract: Carbon-supported bimetallic PdAg catalysts with Pd/Ag atomic ratios varying from 4/1 to 1/2 were prepared by an impregnation–reduction method. The impregnated black mixture was treated in H2/N2 atmosphere at a temperature varying from 180 to 500°C. The obtained Pd x Ag y /C catalysts were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), cyclic voltammetry (CV) and chronoamperometry (CA). XRD results show that the lattice constant of Pd is dilated, suggesting the formation of PdAg alloy. The lattice constant of Pd for the Pd x Ag y /C-500 (reduced at 500°C by H2) increases linearly and the average metal particle size decreases slightly from 6.8 to 5.1nm with increasing Ag fractions from 20% to 67% in the PdAg composition. For Pd x Ag y /C catalysts with a certain specific Pd/Ag atomic ratio, e.g., Pd2Ag1/C, the dilated lattice constant of Pd is independent of the reducing temperature, indicating the alloy degree for the Pd2Ag1/C-t catalysts is comparable. The average metal particle size for the Pd2Ag1/C-t catalysts increases from 3.4 to 5.2nm with H2 reduction temperature increasing from 180 to 500°C. The potentiodynamic measurements on ethanol electrooxidation reaction (EOR) show that the catalytic activities for the Pd x Ag y /C-t catalysts toward the EOR are improved by alloying Pd with Ag. At typical potential of a working fuel cell, e.g., −0.4V vs. Hg/HgO, the EOR current density presents a volcano shape as a function of the Ag fractions in PdAg with the maximum occurs at the Pd/Ag atomic ratios between 2/1 and 3/1. The CA tests show that the Pd x Ag y /C-500 catalysts perform high stability than that of Pd/C-500. The improved EOR activity for the Pd x Ag y /C-t catalysts, compared with whether Pd/C or Ag/C catalyst, may possibly be attributed to the formation of PdAg alloy and the fitted particle size. [Copyright &y& Elsevier]

Abstract: Carbon-supported bimetallic Pt m Pb1 (m =1, 2, 3) electrocatalysts with different Pt/Pb atomic ratios were synthesized by a polyol method. The X-ray diffraction results reveal that a PtPb alloy formed in the Pt m Pb1/C electrocatalysts. TEM images show that the PtPb nanoparticles distribute uniformly on the carbon support, and are about 4–5nm in size. The Pt m Pb1/C bimetallic catalysts show superior activities toward methanol electrooxidation reaction (MOR) than the Pt/C in alkaline media. Both CO stripping measurements and density functional theory studies reveal that CO adsorption decreased significantly on the Pt m Pb1/C bimetallic catalysts compared with on pure Pt, which may offer an explanation for the enhanced MOR activity of the Pt m Pb1/C bimetallic catalysts. [Copyright &y& Elsevier]