This work is devoted to the preparation of alloys based on intermetallic compounds in the Ti-Al-Si system by powder metallurgy using mechanical alloying and the spark plasma sintering (SPS) method. The aim was to describe the formation of intermetallic phases during mechanical alloying of TiAl15Si15 (wt-%) alloy and to consolidate the powder prepared by optimised conditions. Phase composition, microstructure and hardness of compacted alloy were determined. Four hours of mechanical alloying is sufficient time for preparation of pure elements free material composed only of intermetallic phases. After consolidation, the TiAl15Si15 alloy has a homogeneous structure composed of silicide (Ti5Si3) in aluminide (TiAl) matrix. The hardness of the material reaches 865 ± 42 HV 5. [ABSTRACT FROM AUTHOR]

Ti–Al–Si alloys are prospective material for high-temperature applications. Due to low density, good mechanical properties, and oxidation resistance, these intermetallic alloys can be used in the aerospace and automobile industries. Ti–Al–Si alloys were prepared by powder metallurgy using reactive sintering, milling, and spark plasma sintering. One of the novel SPS techniques is high-pressure spark plasma sintering (HP SPS), which was tested in this work and applied to a Ti–10Al–20Si intermetallic alloy using a pressure of 6 GPa and temperatures ranging from 1318 K (1045 °C) to 1597 K (1324 °C). The low-porosity consolidated samples consist of Ti5Si3 silicides in an aluminide (TiAl) matrix. The hardness varied between 720 and 892 HV 5. [ABSTRACT FROM AUTHOR]

Ni-Ti alloys are considered to be very important shape memory alloys with a wide application area including, e.g., biomaterials, actuators, couplings, and components in automotive, aerospace, and robotics industries. In this study, the NiTi46 (wt.%) alloy was prepared by a combination of self-propagating high-temperature synthesis, milling, and spark plasma sintering consolidation at three various temperatures. The compacted samples were subsequently heat-treated at temperatures between 400 °C and 900 °C with the following quenching in water or slow cooling in a closed furnace. The influence of the consolidation temperature and regime of heat treatment on the microstructure, mechanical properties, and temperatures of phase transformation was evaluated. The results demonstrate the brittle behaviour of the samples directly after spark plasma sintering at all temperatures by the compressive test and no transformation temperatures at differential scanning calorimetry curves. The biggest improvement of mechanical properties, which was mainly a ductility enhancement, was achieved by heat treatment at 700 °C. Slow cooling has to be recommended in order to obtain the shape memory properties. [ABSTRACT FROM AUTHOR]