High-yield pulping of wood chips using low-consistency (LC) refining in combination with primary-stage high-consistency (HC) refining has previously been shown to produce paper with quality parameters (tensile strength and light-scattering coefficient) commonly targeted for newsprint with significantly less refining energy input than using only HC refining. However, questions remain on the differences in the refining action between the two refiner types and for high-yield pulping, the refiner energy demand is a crucial process parameter. Therefore, fines- and fiber-fraction development in HC and LC refining has been studied in detail using Bauer-McNett fractionation, and the respective tensile strengths of the different fractions have been compared. Quantitative and qualitative (morphological) characteristics of the isolated fine fractions have also been analyzed in detail using a newly developed automated fluorescence microscopy method and scanning electron microscopy. The results suggest the difference in LC/HC pulp properties (strength and optical) is partly derived from deviating fiber and fines morphologies and mass balances. The quality of the fines generated during HC and LC refining also differs. LC-refined pulps contain thinner fibrillar fines (thread-like) and HC-refined pulps broader fibrils such as lamellae-type fines. Flake-like fines from the outer fiber wall decreased in relative amount with energy input.

Primary refined softwood was subjected to high-consistency (HC) or low-consistency (LC) secondary refining, and the nature of the development of the internal and external fiber microstructure and ultrastructure has been compared. The primary refining of mixed softwood as a raw material was performed in pilot scale by the advanced thermomechanical pulp process. The study was aiming at the comparative characterization of LC and HC pulps at the fiber level when produced with similar and well-characterized handsheet properties. The formerly described Simons’ staining method was applied. A significant degree of fiber wall delamination/internal fibrillation (D/IF) was observed during both LC and HC refining. Both the energy input and the refining consistency had a significant impact on elevating the degree of fiber wall D/IF. The statistical evaluation of internal fiber development indicated that the fiber populations in LC- and HC-refined pulps had a similar degree of fiber wall D/IF despite having a large difference in refining energy input (420 kW h odt-1), confirming that D/IF was promoted more energy-efficiently in LC than in HC refining. The characteristic of the external fiber development from HC and LC refining was very different. Secondary LC refining promoted fiber surfaces with ribbons of thin hairlike threads arising from the inner secondary S2 layer that occasionally developed along the whole fiber length. Broad sheet- and lamellae-type external fibrillation from the S2 was typical for HC refining, and these characteristics were rarely observed in the LC pulps. The mechanisms for LC and HC fiber development are proposed. The cell wall characteristics (internal and external) of the pulp fibers appear to govern most of the physical and optical properties in handsheets.