Search

This work presents an investigation of the fully strained GaAsN/GaAs heterostructures obtained by atmospheric pressure metalorganic vapor phase epitaxy, focusing on the analysis of the strain generated in the GaAsN epilayers and its correlation with the formation of split interstitial complexes (N-As)As. We analyzed strained GaAsN epilayers with nitrogen contents and thicknesses varying from 0.93 to 1.81% and 65 to 130 nm, respectively. The composition and thickness were determined by high resolution X-ray diffraction, and the strain was determined by Raman spectroscopy, while the N-bonding configurations were determined by X-ray photoelectron spectroscopy. We found that the strain generated in the GaAsN epilayers is mainly caused by a lattice mismatch with the GaAs substrate. This macroscopic strain is independent of the amount of (N-As)As interstitial defects, while the local strain, induced by an alloying effect, tends to decrease with an increasing ratio of (N-As)As interstitial defects to substitutional nitrogen atoms incorporated into an arsenic sublattice—NAs. Here, we show experimentally, for the first time, a correlation between the strain in the GaAsN epilayers, caused by an alloying effect determined by Raman spectroscopy, and the (N-As)As/NAs ratio estimated by the XPS method. We found out that the (N-As)As interstitials compensate the local strain resulting from the presence of N in the GaAs matrix, if their amount does not exceed ~65% of the substitutional introduced nitrogen NAs. [ABSTRACT FROM AUTHOR]

In the presented work, an optical approach of stress determining in metalorganic vapor phase epitaxy (MOVPE) grown quantum cascade laser (QCL) structures was reported. In the case of such sophisticated structures containing hundreds of thin layers, it is important to minimize the stress generated in the QCL core. Techniques enabling determination of stress in such thin layers as those described in the article are photoluminescence and Raman spectroscopies. Based on Raman shift or changes in photoluminescence signal, it is possible to analyze stress occurring in the structure. [ABSTRACT FROM AUTHOR]

We report on resonant Raman scattering studies of monolayer MoS 2 as a function of the excitation laser energy (1.959–2.033 eV) and temperature ( T  = 7–295 K). In complementary reflectivity contrast experiments we determined the temperature evolution of the A exciton and trion resonances. We focus our studies on the dispersive, second order ‘b’ mode related to the resonant two phonon Raman process of successive emissions of the acoustic LA and TA phonons at K points. We found that when excitation laser energy is tuned across the A exciton level this mode shifts almost linearly to lower frequency with the rate equal −83 and −71 cm −1 /eV at T  = 7 and 295 K, respectively, which is about two times higher rate than those reported in the previous studies of monolayer MoS 2 but very close the relevant rate recorded for bulk MoS 2 . We interpret this effect as related to the difference of concentration of two dimensional electron gas. We also determined, using excitation with the He-Ne laser the temperature shifts of the Raman peaks of dispersive ‘b’ and dispersionless E′ and A 1 ′ modes. We found that absolute value of the temperature coefficient of ‘b’ mode, equals 3.5 × 10 −2  cm −1 /K, is much higher than those of E′ and A 1 ′ modes, equal 0.4 × 10 −2 and 0.8 × 10 −2  cm −1 /K, respectively. [ABSTRACT FROM AUTHOR]

Monolayers of transition metal dichalcogenides (TMDs) with their unique physical properties are very promising for future applications in novel electronic devices. In TMDs monolayers, strong and opposite spin splittings of the energy gaps at the K points allow for exciting carriers with various combinations of valley and spin indices using circularly polarized light, which can further be used in spintronics and valleytronics. The physical properties of van der Waals heterostructures composed of TMDs monolayers and hexagonal boron nitride (hBN) layers significantly depend on different kinds of interactions. Here, we report on observing both a strong increase in the emission intensity as well as a preservation of the helicity of the excitation light in the emission from hBN/WSe2/hBN heterostructures related to interlayer electron-phonon coupling. In combined low-temperature (T = 7 K) reflectivity contrast and photoluminescence excitation experiments, we find that the increase in the emission intensity is attributed to a double resonance, where the laser excitation and the combined Raman mode A′1 (WSe2) + ZO (hBN) are in resonance with the excited (2s) and ground (1s) states of the A exciton in a WSe2 monolayer. In reference to the 2s state, our interpretation is in contrast with previous reports, in which this state has been attributed to the hybrid exciton state existing only in the hBN-encapsulated WSe2 monolayer. Moreover, we observe that the electron-phonon coupling also enhances the helicity preservation of the exciting light in the emission of all observed excitonic complexes. The highest helicity preservation of more than 60% is obtained in the emission of the neutral biexciton and negatively charged exciton (trion) in its triplet state. Additionally, to the best of our knowledge, the strongly intensified emission of the neutral biexciton XX0 at double resonance condition is observed for the first time. [ABSTRACT FROM AUTHOR]