Search

Acetylation is a breakthrough in wood modification and has been established on industrial scale. However, concerns have been raised regarding the stability of acetylated wood under elevated temperatures, particularly during post hot-pressing processes to manufacture products such as laminated veneer lumber (LVL). At around 150 °C, the added acetyl groups might cleave off (“de-acetylation”) and by that release sorption sites for water. This would increase the moisture uptake of the modified wood. In this study, the impact of hot-pressing at 150 °C on the stability of acetylated beech veneers and LVL was investigated. Fourier transform infrared (FTIR) spectroscopy showed that the chemical composition of acetylated veneers seemed to be unaffected after the heat treatment. Dynamic vapor sorption (DVS) analysis and long-term storing over saturated salt-solutions in miniature climate chambers, indicated no de-acetylation on the basis of negligible changes in wood-water interactions. The number of hydroxyl groups of heat-treated acetylated samples was similar to that of not heat-treated ones, indicating the persistence of the effects of acetylation. By the present study, a certain resilience of acetylated wood towards elevated temperature, like it may occur during hot-pressing of acetylated veneers, became apparent and illustrated the thermal stability of this chemical modification approach. [ABSTRACT FROM AUTHOR]

This study demonstrates acetylation with acetic anhydride, one of the few industrial wood modification techniques on the market, to increase the dimensional stability and durability of laminated veneer lumber (LVL) made from beech wood (Fagus sylvatica L.). After being acetylated, veneers were hot-bonded to LVL using phenol-formaldehyde resin (PF) or phenol-resorcinol-formaldehyde resin (PRF). The bonding performance (bonding shear strength (BSS) and wood failure (WF)) was tested under the following three conditions: 20°C and 65% RH, water immersion, and rigorous boiling-drying-boiling cycle. Additionally, using the same specimen sizes on a second sample set, the moisture content (MC) and dimensional stability were determined. Results indicate that the PRF resin provided the strongest bonding performance on acetylated LVL and references. Acetylated LVL had higher BSS in wet conditions than untreated controls, especially after boiling in water, which could be attributed to less wood-water interaction at the cell wall level after acetylation. [ABSTRACT FROM AUTHOR]

Acetylation with acetic anhydride is well known to improve the dimensional stability and durability of wood. Veneer is appealing for acetylation because of its thin thickness, which supports a complete and even impregnation of difficult-to-treat wood species, such as beech (Fagus sylvatica L.). Unlike resin-based veneer impregnation, acetylated veneer does not require any additional curing. As a result, veneer properties are already altered prior to bonding. The compression thickness reduction in acetylated beech veneer during the manufacturing of laminated veneer lumber (LVL) utilizing 1, 3, and 6 MPa at 150 °C for 30 min is investigated in this study. The results show that acetylated beech veneer is considerably less compressible than the references. Moreover, the density of acetylated LVL at low pressure (1 MPa) is similar to the one of references, even though the compressibility is much lower. This is due to the added acetyl groups after acetylation. The reduction in compressibility is most likely caused due to a decrease in moisture content (MC) and its accompanied mechanisms. [ABSTRACT FROM AUTHOR]

The purpose of this review is to put previous research findings on acetylated wood and the fabrication of veneer-based products in a common context. The first research on wood acetylation was already conducted in the 1920s using wood meal, whereas relevant research on veneer acetylation was published nearly two decades later, during the 1940s. In the years that followed, a great deal of research has been done on both solid wood and composite acetylation. Developments in the 1990s and early 2000s resulted in the creation of commercial products. Nowadays, wood is becoming increasingly popular in construction. Therefore, high-performance materials with high dimensional stability and durability are required. Veneers are thereby of particular relevance because of their propensity to absorb chemicals into even tough-to-treat wood species. However, acetylation alters the bonding properties of wood, which is important for the manufacture of engineered veneer products, especially in load-bearing construction. A large amount of research is now being conducted on the acetylation of veneer, and acetylated veneer products are anticipated in the near future. This study covers the fundamentals of bonding but focuses specifically on veneer acetylation and its fabrication to engineered veneer-based products. The influencing factors of acetylation on bonding are also discussed. [ABSTRACT FROM AUTHOR]

Leaving wooden façades uncoated has become popular in modern architecture, especially for large buildings like multi-story houses, in order to circumvent frequent maintenance, particularly repainting. To obtain a quick and even artificial graying of the entire façade that gradually turns into natural graying, a one-off treatment with iron (II) sulfate may be applied. Its mode of action is commonly ascribed to a reaction with phenolic wood extractives, especially hydrolyzable tannins. This does not however sufficiently explain iron (II) sulfate's ability to color wood species containing only marginal amounts of phenolic extractives; moreover, little is known about the influence of the wooden substrate and light conditions on the color development of façades treated with iron (II) sulfate. In the present study, we investigated the influence of wood extractives, exposure conditions, and nine different wooden substrates on iron (II) sulfate's staining effect. Spruce specimens with and without extractives were treated with a 4% iron (II) sulfate solution and exposed to sunlight behind window glass. Both wood types darkened slowly but significantly during 51 weeks of exposure. This shows that artificial graying with iron (II) sulfate (1) does not require precipitation unlike natural graying, (2) takes place without initial wood extractives, and (3) proceeds at a slow rate. Specimens protected from sunlight changed their color only slightly, suggesting that photo-induced phenoxyl and ketyl radicals from photolysis of lignin's ether bonds oxidize iron (II) to iron (III). Specimens made of spruce, pine, larch, and western red cedar (WRC) and exposed outdoors decreased strongly in lightness during the first two months of exposure. In contrast, a staining effect of iron (II) sulfate in terms of artificial graying was not seen on acetylated radiata pine, possibly because iron ions are hindered from entering the cell wall. Specimens partly protected by a roof overhang showed an uneven color development; this is due to the protection from radiation and not from precipitation as is known for natural graying. [ABSTRACT FROM AUTHOR]