Search

Optimally increasing the catalytic activity of Co3O4‐based materials is crucial for promoting their practical applications for acetone detection; however, this still remains challenging. Herein, a strategy is proposed in this work to increase the catalytic activity of Co3O4 toward the oxidation of acetone through the synergistic effect of boron doping and chemical reduction, which can substantially improve the sensing performance for acetone detection. The characterization results confirm that the present strategy facilitates the formation of more oxygen vacancies and increases the content of Co2+ ions serving as active sites. As expected, the optimal sensor yields a higher response. To extend the practical application to the auxiliary diagnosis of diabetes through exhaled breath, the optimal sensors distinguished between acetone concentrations in the breath of healthy individuals and in the simulated breath of patients with diabetes. Detailed gas‐sensing measurements reveal that the enhanced acetone sensing performance is attributed to the increased catalytic activity of materials for oxidation of acetone by the Mars–van Krevelen, Langmuir–Hinshelwood, and Eley–Rideal mechanisms. This study provides new insights into the fabrication of high‐performance metal oxide‐based gas sensors by improving the catalytic activity of sensing materials. [ABSTRACT FROM AUTHOR]

Reduced graphene oxide (rGO)-based materials are deemed as promising candidates for fabrication of room-temperature gas sensors, while a tougher challenge is to develop an effective strategy for improving gas responses. Here, a noble metal decoration strategy is developed to enhance NO2 responses of α-Fe2O3/SnO2–rGO hybrids. Noble metal decorated α-Fe2O3/SnO2–rGO hybrids were prepared by depositing noble metals onto α-Fe2O3/SnO2–rGO hybrids through reduction of noble metal ions by NaBH4. Most importantly, Pt modified α-Fe2O3/SnO2–rGO hybrids (designated as Pt-FSR) exhibit the highest response value of 21.3 toward 5 ppm NO2, which is much higher than that of α-Fe2O3/SnO2–rGO (8.8). Combined characterization studies indicate that the enhanced NO2 response of Pt-FSR is attributed to the narrow band gap of Pt-FSR, small particle size and excellent catalytic activity of Pt. The NO2 sensing mechanism is also investigated by FT-IR spectroscopy. The findings proposed in this work not only broaden the study of room-temperature gas sensors, but also provide suggestions for discovering the gas sensing mechanism. [ABSTRACT FROM AUTHOR]

Toluene is widely used as a solvent and reactant in a wide range of industrial fields; however, gaseous toluene is toxic to humans, causing severe acute respiratory effects. In this case, Co3O4-based chemiresistive gas sensors are promising candidates for monitoring toluene. However, it is challenging to prepare Co3O4-based sensing materials with good toluene sensing performances on a large-scale. In this study, oxygen vacancy-rich Co3O4 materials were successfully synthesized via the reduction of commercial Co3O4 using NaBH4 as the reducing agent (designated as Co3O4-R), and the oxygen vacancy concentrations in Co3O4-R materials were effectively modulated by regulating the NaBH4 concentration. With an increase in oxygen vacancies, the optimal Co3O4-R-5 samples displayed better sensing performances toward 100 ppm toluene at 190 °C than that of the pristine commercial Co3O4, including an enhanced response value of 3.18 (vs. 1.22 for commercial Co3O4) and fast response time of 48 s and recovery time of 38 s. The combination of band structure analysis and chemisorption analysis indicated that the enhanced toluene sensing performances of Co3O4-R is attributed to the synergistic effect of reducing the band gap and activating the surface oxygen species. This work demonstrates the first utilization of commercial Co3O4 for toluene sensing applications, providing a universal and high-throughput preparation method to prepare gas sensing materials using commercial metal oxides. [ABSTRACT FROM AUTHOR]

The high-pressure structures of alkaline earth metal hydride-fluorides (AHFs) (A = Ca, Sr, Ba) were investigated up to 8 GPa. While AHF adopts the fluorite-type structure (Fm3¯m) at ambient pressure without anion ordering, the PbCl2-type (cotunnite-type) structure (Pnma) is formed by pressurization, with a declining trend of critical pressure as the ionic radius of the A2+ cation increases. In contrast to PbCl2-type LaHO and LaOF whose anions are fully ordered, the H−/F− anions in the high-pressure polymorph of SrHF and BaHF are partially ordered, with a preferential occupation of H− at the square-pyramidal site (vs. tetrahedral site). First-principles calculations partially support the preferential anion occupation and suggest occupation switching at higher pressure. These results provide a strategy for controlling the anion ordering and local structure in mixed-anion compounds. [ABSTRACT FROM AUTHOR]