During the study, transparent ceramics based on yttrium-aluminum garnet (Y3Al5O12) were obtained:Ce) with graphene oxide (GO) additions from 0.1 to 1%, annealed at a temperature of 1250-1650 °C. The effect of the annealing temperature and the concentration of additives on the composition, density and optical characteristics of the obtained samples is investigated. It is shown that graphene oxide has a positive effect on the characteristics of luminescent ceramics.

Based on the registration and analysis of the full wave profiles, the Hugoniot elastic limit and spall strength of ceramics based on tungsten carbide with different cobalt content are measured. We also study the influence of the cobalt content on the mechanical characteristics of tungsten carbide such as hardness, fracture strength, Young’s modulus, shear modulus, and sound velocity. It is shown that in the process of spalling, the failure stresses grow and the dynamic elastic limit decreases almost linearly within the scatter of their values with growing cobalt content; moreover, the value of the Hugoniot elastic limit is abruptly practically halved as the cobalt content grows from 0 to 2 wt %.

На основе регистрации и анализа полных волновых профилей проведены измерения динамического предела упругости и откольной прочности керамики на основе карбида вольфрама с различным содержанием кобальта. Исследовано также влияние концентрации кобальта на механические характеристики карбида вольфрама, такие как твердость, трещиностойкость, модуль Юнга, модуль сдвига, скорость звука. Показано, что разрушающие напряжения при отколе увеличиваются, а динамический предел упругости уменьшается практически линейно в рамках разброса их значений с ростом концентрации кобальта, причем величина предела упругости уменьшается скачком практически в 2 раза при увеличении концентрации кобальта от 0 до 2%.