This work aimed to assess the biomechanics, using the finite element method (FEM), of traditional titanium Morse taper (MT) dental implants compared to one-piece implants composed of zirconia, polyetheretherketone (PEEK), carbon fiber-reinforced PEEK (CFR-PEEK), or glass fiber-reinforced PEEK (GFR-PEEK). MT and one-piece dental implants were modeled within a mandibular bone section and loaded on an oblique force using FEM. A MT implant system involving a Ti6Al4V abutment and a cp-Ti grade IV implant was compared to one-piece implants composed of cp-Ti grade IV, zirconia (3Y-TZP), PEEK, CFR-PEEK, or GFR-PEEK. Stress on bone and implants was computed and analyzed while bone remodeling prediction was evaluated considering equivalent strain. In comparison to one-piece implants, the traditional MT implant revealed higher stress peak (112 MPa). The maximum stresses on the one-piece implants reached ~80 MPa, regardless their chemical composition. MT implant induced lower bone stimulus, although excessive bone strain was recorded for PEEK implants. Balanced strain levels were noticed for reinforced PEEK implants of which CFR-PEEK one-piece implants showed proper biomechanical behavior. Balanced strain levels might induce bone remodeling at the peri-implant region while maintaining low risks of mechanical failures. However, the strength of the PEEK-based composite materials is still low for long-term clinical performance.

The aim of this study was to manufacture zirconia periodic open cellular structures (POCS) (39%–57% porosity) and evaluate their mechanical properties. Zirconia POCS with 39%, 47% and 57% porosity were obtained from a CAD/CAM blank using a CNC milling machine. Specimens with a feldspar-based porcelain infiltrated in the porosities were also produced and tested. The elastic and inelastic properties of the all samples were obtained by compression strength tests. The structures were analyzed using XRD and SEM. FEA was also performed to evaluate the porous structures and for optimization. Zirconia POCS were successfully produced using a CAD/CAM technique. Porous size and distribution can be easily modified to tailor the desired POCS mechanical properties. Elastics and inelastic properties were well fitted by the Gibson-Ashby model, which allows designing POCS with predictable results.

Objectives: The aim of this study was to evaluate the use of dual-cure resin cement to promote the bonding between a veneering PEEK and zirconia or titanium surfaces.Materials and methods: The surf...

Objectives The aim of this work was to evaluate the biomechanical behavior of one-piece zirconia implants with a functionally graded bioglass (BG) layer as compared to monolithic zirconia and BG-coated implants, using the finite element method (FEM). Methods Zirconia disks were infiltrated with bioglass S53P4 and then morphologically inspected by scanning electron microscopy (SEM) followed by mechanical analyses on micro-indentation tests for further biomechanical validation using the finite element method (FEM). On modeling, zirconia dental implants anchored into mandibular bone were simulated on occlusal loading as recorded under mastication. Three types of implants were simulated: i) free of BG coating, ii) with 100 μm or 150 μm thick conventional BG coatings; and iii) with graded BG coatings involving 3 different chemical composition distributions. The stress state at both implant and bone were evaluated using the FEM. The mechanically-induced bone remodelling was analyzed through the bone strain results. Results Infiltration of BG into a zirconia structure resulted in a ∼100 μm thick layer with an exponential-like gradation of chemical composition and properties. Regarding the FEM calculations, the BG coating induced up to 30% decrease on stress in the implant body when compared to the monolithic zirconia implant. The gradient of chemical composition also improved the stresses’ distribution. The stresses distribution towards the BG-coatings were significantly high and could lead to failure. Stresses on the bone were recorded down to its strength threshold, with insignificant influence of the coating layer. The bone strain values on all models indicates further bone remodelling although BG-coated and BG-graded zirconia implants showed the highest strain magnitude that may enhance the mechanical stimulation for bone maintenance. Significance Graded BG-zirconia dental implants showed enhanced overall biomechanical behaviour as compared to the BG-coated or monolithic zirconia dental implants. Also, such biomechanical improvements noticed for the BG-graded system should be considered in combination with the well-known osseointegration benefits of bioactive glasses.

The purpose of this study was to evaluate the mechanical properties of laser printed monolithic and laminated nano ceramic resins (NCR) for dental prosthetic applications. Three different types of discs were produced by laser printing: monolithic NCR discs and laminated NCR discs with 100 μm (laminate_100) and 500 μm (laminate_500) resin interlayers (n = 10). To assess the adhesion strength of the photosensitive resin used as interlayer to the NCR, cylindrical specimens were produced. The biaxial flexural strength and shear bond strength of the specimens were measured using a universal testing machine. Data was statistically analyzed by one-way ANOVA followed by Tukey HSD test (α = 0.05). The microstructure and fracture surfaces were analyzed by SEM/EDS. Results were rationalized with finite element analysis (FEA). Laminate_100 specimens showed significantly higher flexural strength (∼50%) than monolithic and Laminate_500 specimens (p

Objectives Thermal cycling is widely used to simulate the aging of restorative materials corresponding to the changes of temperature in the oral cavity. However, test parameters present in literature vary considerably, which prevents comparison between different reports. The aim of this work is to assess the influence of the specimens’ geometry and materials on the thermal stresses developed during thermal cycling tests. Materials and methods Finite elements method was used to simulate the conditions of thermal cycling tests for three different sample geometries: a three-points bending test sample, a cylinder rod and more complex shape of a restoration crown. Two different restorative systems were considered: all-ceramic (zirconia coupled with porcelain) and metal-ceramic (CoCrMo alloy coupled with porcelain). The stress state of each sample was evaluated throughout the test cycle. Results The results show that the sample geometry has great influence on the stress state, with difference of up to 230% in the maximum stress between samples of the same composition. The location of maximum stress also changed from the interface between materials to the external wall. Conclusions Maximum absolute stress values were found to vary between 2 and 4 MPa, which might not be critical even for ceramics. During multi-cycle testing these stresses would cause different fatigue in various locations. The zirconia-based specimens and zirconia-based restoration (crown) exhibited the most similar stress states. Thus it might be recommended to use these geometries for fast screening of the materials for this type of restorations. Clinical significance The selection of specimens’ geometry and materials should be carefully considered when aging conditions close to clinical ones want to be simulated.

Bioceramics are a great alternative to use in implants due to their excellent biocompatibility and good mechanical properties. Depending on their composition, bioceramics can be classified into bioinert and bioactive, which relate to their interaction with the surrounding living tissue. Surface morphology also has great influence on the implant biological behavior. Controlled texturing can improve osseointegration and reduce biofilm formation. Among the techniques to produce nano- and micropatterns, laser texturing has shown promising results due to its excellent accuracy and reproducibility. In this work, the use of laser techniques to improve surface morphology of biomaterials is reviewed, focusing on the application of direct laser interference patterning (DLIP) technique in bioceramics., This study was funded by FCT-Portugal through the following projects-UID/EEA/04436/2013, COMPETE 2020 with the code POCI-01-0145-FEDER-00694 and LaserMULTICER (POCI-01-0145-FEDER-031035) and by Conselho Nacional de Desenvolvimento Cientifico e Tecnologico (CNPq), Brazil through the project-CNPq/UNIVERSAL/421229/2018-7. B.H. acknowledges the support of the Alexander von Humboldt Foundation.

The purpose of this study was to evaluate the biaxial flexural stresses in classic bilayered and in graded zirconia-feldspathic porcelain composites. A finite element method and an analytical model were used to simulate the piston-on-ring test and to predict the biaxial stress distributions across the thickness of the bilayer and graded zirconia-feldspathic porcelain discs. An axisymmetric model and a flexure formula of Hsueh et al. were used in the FEM and analytical analysis, respectively. Four porcelain thicknesses were tested in the bilayered discs. In graded discs, continuous and stepwise transitions from the bottom zirconia layer to the top porcelain layer were studied. The resulting stresses across the thickness, measured along the central axis of the disc, for the bilayered and graded discs were compared. In bilayered discs, the maximum tensile stress decreased while the stress mismatch (at the interface) increased with the porcelain layer thickness. The optimized balance between both variables is achieved for a porcelain thickness ratio in the range of 0.30–0.35. In graded discs, the highest tensile stresses were registered for porcelain rich interlayers (p=0.25) whereas the zirconia rich ones (p=8) yield the lowest tensile stresses. In addition, the maximum stresses in a graded structure can be tailored by altering compositional gradients. A decrease in maximum stresses with increasing values of p (a scaling exponent in the power law function) was observed. Our findings showed a good agreement between the analytical and simulated models, particularly in the tensile region of the disc. Graded zirconia-feldspathic porcelain composites exhibited a more favourable stress distribution relative to conventional bilayered systems. This fact can significantly impact the clinical performance of zirconia-feldspathic porcelain prostheses, namely reducing the fracture incidence of zirconia and the chipping and delamination of porcelain.

Objectives The aim of this study was to evaluate the influence of a surface conditioning technique using laser ablation and acid etching on PEEK substrate on its bonding strength to a resin cement. Materials and methods Cylindrical specimens of unfilled PEEK, 30% glass fiber reinforced PEEK and 30% carbon fiber reinforced PEEK were separated in four groups according to the following surface treatments: acid etching with H2SO4, laser ablation with 200 µm holes spaced 400 µm apart (D2E4), laser ablation with 200 µm holes spaced 600 µm apart (D2E6), and laser ablation (D2E4) followed by acid etching. A dual-curing resin cement (Allcem CORE) was then applied to the PEEK surface. Specimens were aged in distilled water at 37 °C for 24 h. Shear bond strength tests were performed to the fracture of the samples. Two-way ANOVA statistical analysis was performed with a significance level of 0.05. Scanning electron microscopy analysis was performed to analyse the conditioned and fracture surfaces. Results SEM images of the test interfaces showed that the resin cement could not flow in the holes designed by the laser ablation on the PEEK surface. The shear bond strength of PEEK to resin cement was not improved by the surface modification of the PEEK. Also, there was a statistically significant decrease in shear bond strength for unfilled PEEK specimens. On carbon or glass reinforced PEEK, the change was not significant. SEM images of the fracture surfaces revealed that the failure mode was mainly adhesive. Conclusions Although laser ablation promoted the PEEK surface modification by the formation of retentive holes, the test resin cement could not thoroughly flow on the rough modified surfaces to establish an effective mechanical interlocking. That negatively affected the shear bonding strength of PEEK to the resin cement. Further studies should be carried out to increase the bonding between PEEK and resin cements.

Objectives The aim of this study was to evaluate the effect of laser surface structuring on the bond strength of feldspar-based porcelain to zirconia, as compared to conventional sandblasting treatment. Materials and methods Thirty cylindrical zirconia substrates, previously sintered, were divided in three groups according to the type of surface conditioning: 1) sandblasting with 50 µm Al2O3; 2) laser structuring (O25 µm holes); and 3) laser structuring (O50 µm holes). Porcelain was injected onto the zirconia substrates. X-ray diffractometry (XRD) was used to evaluate the influence of the laser treatment on zirconia crystallographic phases. Shear bond strength test was performed. Micrographs using SEM were used to evaluate the zirconia surface after each surface treatment and to evaluate the fracture surface after the shear test. Results The laser-structured groups presented the highest shear bond strength (65 ± 16 MPa and 65 ± 11 MPa, for the 25 µm and 50 µm holes, respectively). The sandblasting samples presented shear bond strength of 37 ± 16 MPa. XRD analysis showed that there was no phase transformation on the thermally affected surface due to laser action. Microcracks were created at some holes due to the high temperature gradient generated by laser. Significance Laser structuring significantly increased (up to 75%) the shear bond strength of zirconia to veneering porcelain as compared to conventional sandblasting treatment. Therefore, laser structuring arises as a surface conditioning method for producing stronger and long lasting zirconia-porcelain interfaces.

Residual thermal stresses are formed in dental restorations during cooling from high temperature processing. The aim of this study was to evaluate the influence of constructive design variables (composition and interlayer thickness) on residual stresses in alumina- and zirconia-graded restorations. Restorations' real-like cooling conditions were simulated using finite elements method and temperature-dependent material properties were used. Three different designs were evaluated: a bilayered restoration (sharp transition between materials); a trilayered restoration with a homogenous interlayer between core and veneer; and a trilayered restoration with a graded interlayer. The interlayer thickness and composition were varied. Zirconia restorations presented overall higher thermal stress values than alumina ones. Thermal stresses were significantly reduced by the presence of a homogeneous interlayer. The composition of the interlayer showed great influence on the thermal stresses, with the best results for homogeneous interlayers being observed for porcelain contents in the composite ranging between 30%–50% (vol.%), for both alumina and zirconia restorations. The interlayer's thickness showed a minor contribution in the thermal stress reduction. The graded interlayer showed an optimized reduction in restorations' thermal stresses. The use of graded interlayer, favoring enhanced thermal stress distributions and lower magnitude is expected to reduce the risk of catastrophic failure.

Layered ceramic systems are usually hit by residual thermal stresses created during cooling from high processing temperature. The purpose of this study was to determine the thermal residual stresses at different ceramic multi-layered systems and evaluate their influence on the bending stress distribution. Finite elements method was used to evaluate the residual stresses in zirconia-porcelain and alumina-porcelain multi-layered discs and to simulate the ‘piston-on-ring’ test. Temperature-dependent material properties were used. Three different multi-layered designs were simulated: a conventional bilayered design; a trilayered design, with an intermediate composite layer with constant composition; and a graded design, with an intermediate layer with gradation of properties. Parameters such as the interlayer thickness and composition profiles were varied in the study. Alumina-porcelain discs present smaller residual stress than the zirconia-porcelain discs, regardless of the type of design. The homogeneous interlayer can yield a reduction of ~40% in thermal stress relative to bilayered systems. Thinner interlayers favoured the formation of lower thermal stresses. The graded discs showed the lowest thermal stresses for a gradation profile given by power law function with p=2. The bending stresses were significantly affected by the thermal stresses in the discs. The risk of failure for all-ceramic dental restorative systems can be significantly reduced by using trilayered systems (homogenous or graded interlayer) with the proper design.