Abstract: A large and transparent Yb:FAP crystal with dimensions up to ∅30mm×85mm has been grown by the Czochralski method. The preparation of the raw material has been investigated. X-ray power diffraction studies of Yb:FAP crystal confirm that the as-grown crystal is isostructural with the FAP crystal. The crystalline quality has been studied using X-ray rocking curve analysis. The segregation coefficient of Yb3+ in the Yb:FAP crystal has been also determined. Linear thermal expansion coefficients in [001] and [100] directions have been measured in the 30–800°C temperature range. [Copyright &y& Elsevier]

Abstract: The high optical quality Tm: YAG single crystals with dopant concentrations of 2, 4, 8 at % Tm3+ ions have been grown by the Czochralski (CZ) method .The segregation coefficients of Tm3+ ions in CZ-grown 2, 4, 8 at % doped Tm: YAG crystals determined by ICP-AES method are equal to 0.93, 1.04, 1.10, respectively. The absorption spectra in the range of 190–900nm and the IR absorption spectra in the range of 1000–4500cm-1 of the Tm: YAG crystals were also measured at room temperature. The results indicate that Tm: YAG is favorable for laser diode-pumped system, and air annealing can improve the quality of the Tm: YAG crystal. [Copyright &y& Elsevier]

The high optical quality 5 at% doped Yb:YAG single crystals with diameter of 3 inches have been grown by temperature gradient technology (TGT). The segregation coefficient of Yb ions in TGT-grown 5 at% doped Yb:YAG crystals determined by ICP-AES method is equal to 1.1. The absorption spectra in the range of 190–1200 nm of TGT-grown Yb:YAG crystals were also measured at the room temperature. The absorption peaks of trivalent Yb ions and the unknown color centers were found in the absorption spectra. [Copyright &y& Elsevier]