Modulation of the band gap energy and diameter of quantum dots (QDs) formed in glasses is important to achieve the optimized performance for applications as infrared light sources, lasers, saturable absorbers, etc. Absorption and photoluminescence of PbS QDs were extended into mid-infrared wavelength range in glasses containing small amount of lead but oversaturated with sulfur. Dual-band photoluminescence of PbSe QDs was prepared in oxyfluoride glass-ceramics containing BaF2 nanocrystals. By introducing SnO in the glasses, alloyed Pb1-xSnxSe QDs with smaller band gap energies were formed in glasses, and mid-infrared photoluminescence of Pb1-xSnxSe QDs at ~2570 nm in wavelength was achieved. [ABSTRACT FROM AUTHOR]

Abstract: Optical properties of PbS quantum dots (QDs) precipitated inside the oxide glass matrix were investigated. Photoluminescence (PL) from the PbS QDs showed peak wavelengths located at 1170–1680nm with widths of 150–550nm. Radii of QDs in glasses were 2.3–4.7nm depending upon the thermal treatment. Peak wavelengths of PL bands shifted as much as 70nm as the temperatures and excitation irradiances increased. Calculated effective local temperatures indicated that these shifts of PL spectra were associated with local heating induced by the temperatures and laser beam. [Copyright &y& Elsevier]

Abstract: CdSe quantum dots (QDs) were precipitated in silicate glasses under various durations and temperatures of heat-treatment. Absorption and photoluminescence (PL) spectra of the QDs showed the quantum confinement effect from CdSe QDs. When the glass was heat-treated for 10h, estimated average QD sizes increased from 5.2nm when the glass was heat-treated at 490°C and to 6.9nm when it was treated at 500°C. When the glass was heat-treated at 480°C, estimated average QD sizes were 4.9nm after 20h and 5.3nm after 30h. The PL peak position was independent of the excitation wavelengths; this result indicates that the size distribution of CdSe QDs was narrow. [ABSTRACT FROM AUTHOR]