Search

A series of 0.5 at.% Tm:Ca 1-x Y x F 2+x (x = 0, 0.01, 0.04, 0.06, 0.08, 0.12) crystals have been successfully grown by the temperature gradient technique (TGT) method. The absorption spectra, fluorescence spectra, and fluorescence decay curves were measured and analyzed at room temperature. By comparison, it is found that when the concentration of Y3+ ions reaches 8 at.%, the absorption cross section corresponding to the 3H 6 →3H 4 energy level is 2.56 × 10−21 cm2 at 793 nm, which is suitable for GaAlAs LD pumping. The J-O strength parameters Ω 2 , Ω 4 , and Ω 6 were obtained. With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. When the concentration of Y3+ ions reaches 8 at.%, the emission cross sections are 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, and the full widths at half maximum (FWHM) are 76 nm and 195 nm, respectively. The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. • With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. • When the concentration of Y3+ ions reaches 8 at.%, the emission cross section is 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, respectively. • The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. [ABSTRACT FROM AUTHOR]

Nd:SrAl 11 O 19 (Nd:SRA) crystal has been grown by the Czochralski method. Polarized absorption spectra, polarized fluorescence spectra and fluorescence lifetime were investigated. For σ-polarization, the peak absorption cross section at 798 nm is 2.08 × 10−20 cm2 with full width at half maximum (FWHM) of 10.2 nm and the peak emission cross section is 3.36 × 10−20 cm2 at 1048.5 nm with FWHM of 4.80 nm. The Judd-Ofelt parameters Ω 2,4,6 were obtained to be 0.51 × 10−20 cm2, 2.08 × 10−20 cm2, and 2.12 × 10−20 cm2, respectively. Continuous-wave laser operation of the a-cut and c-cut Nd:SRA sample has been demonstrated. The maximum output power of 8.33 W was achieved from c-cut sample at an absorbed power of 27.73 W, corresponding to a slope efficiency of 31.3%. • Nd:SrAl 12 O 19 crystal has been gown by the Czochralski method. • Spectral parameters of Nd:SrAl 12 O 19 crystal were obtained. • Continuous-wave laser was demonstrated from Nd:SrAl 12 O 19 crystal. [ABSTRACT FROM AUTHOR]

GdScO 3 single crystal codoped with Tm3+ and Tb3+ ions was successfully grown by the Edge-defined Film-fed Growth Method (EFG) for the first time. Absorption, fluorescence spectrum and fluorescence lifetimes of the grown crystal at room temperature were measured. The absorption cross-section at 789 nm was calculated to be 8.20 × 10−21 cm2. The emission cross-section was 1.35 × 10−21 cm2 at 1504 nm with the FWHM of 95.3 nm. The fluorescence lifetimes of the 3H 4 state and the 3F 4 state were fitted to be 253 μs and 1460 μs, respectively. Compared with Tm3+ single doped GdScO 3 crystal, the codoping of Tb3+ successfully depopulated the 3F 4 energy level and enhanced the emission at 1.5 μm region. It indicated that Tm,Tb:GdScO 3 could be favorable laser medium for 1.5 μm-laser operation. • Tm3+ and Tb3+ co-doped GdScO 3 crystal was successfully grown by the edge-defined film-fed method (EFG) for the first time. • Spectral parameters and Judd-Ofelt parameters of Tm,Tb:GdScO3 crystal were obtained and compared. • The fluorescence mechanism of Tm3+ and Tb3+ co-doped GdScO 3 crystal has been studied. [ABSTRACT FROM AUTHOR]