Ho3+ and Eu3+ co-doping GdScO 3 crystal was successfully grown by special EFG method. The spectroscopic properties of the crystal were measured and analyzed. The absorption cross section was calculated to be 2.027 × 10−20 cm2 at 1161 nm. The J-O theory intensity parameters Ω t (t = 2, 4, 6), radiative transition rates, fluorescence branching ratios and radiative lifetimes were calculated. The Ho,Eu:GdScO 3 crystal has very strong emission at 2869 nm and the emission cross section was 13.524 × 10−21 cm2. The fluorescence lifetimes of the 5I 7 and 5I 6 levels were measured to be 4.457 ms and 1.265 ms. Confirmed that Eu3+ can be used as an effective deactivation ion of Ho3+ in GdScO 3 crystal. All those results show that the Ho,Eu:GdScO 3 crystal would be a potential laser material for ∼3 μm mid-infrared region. • Ho,Eu:GdScO 3 crystal was successfully grown. • The spectroscopic properties of the Ho,Eu:GdScO 3 crystal were analyzed. • J-O theory was applied to analyze fluorescence properties of the Ho,Eu:GdScO 3 crystal. • The energy transfer between Ho3+ and Eu3+ ions, spectroscopic characteristic of ∼3 μm emission were calculated and analyzed. [ABSTRACT FROM AUTHOR]

Ho:Lu 2 O 3 crystal was successfully grown by TGT method. The spectroscopic properties of the crystal were analyzed. The absorption cross section of Ho:Lu 2 O 3 were 0.307 × 10−20 cm2 at 1147 nm and 1.076 × 10−20 cm2 at 1929 nm. J-O theory was applied to analyze fluorescence properties of the Ho:Lu 2 O 3 crystal. The intensity parameters Ω t (t = 2,4,6), radiative transition rates, branching ratios and radiative lifetime were calculated. The Ho:Lu 2 O 3 crystal had very strong emission at 2027 nm and 2849 nm and emission cross sections were calculated to be 3.271 × 10−21 cm2 and 8.852 × 10−21 cm2, respectively. The fluorescence lifetimes of the Ho3+5I 7 and 5I 6 levels were measured to be 12.400 ms and 0.622 ms. All those results show that the Ho: Lu 2 O 3 crystal would be a potential laser material for mid-infrared region. • Ho: Lu 2 O 3 crystal was successfully grown by TGT method. • The spectroscopic properties of the Ho: Lu 2 O 3 crystal were analyzed. • J-O theory was applied to analyze fluorescence properties of the Ho:Lu 2 O 3 crystal. • The gain cross-section of Ho:Lu 2 O 3 crystal for ∼2 μm region and ∼3 μm region were calculated. [ABSTRACT FROM AUTHOR]