Search

The polarization absorption spectra of Pr3+-doped GdScO 3 have been measured. Polarized emission spectra and fluorescence decay from the 3P 0 upper level have been investigated. The strongest absorption peaks are located at 448 nm for a, b and c polarization, the absorption cross sections are 1.29 × 10−20 cm2, 0.98 × 10−20 cm2 and 1.57 × 10−20 cm2, respectively. The maximum emission cross section is located at 662 nm, which is 18.55 × 10−20 cm2 (a polarization), 12.74 × 10−20 cm2 (b polarization) and 22.41 × 10−20 cm2 (c polarization), and the FWHM is 10.02 nm, 9.38 nm and 10.14 nm, respectively. The fluorescence lifetime of 3P 0 level is 12.39 μs. Those results indicated that Pr3+-doped GdScO 3 crystal grown by the Czochralski method is a potential laser medium for visible laser operation. •The spectra of Pr:GdScO 3 have been measured at room temperature. •Pr3+-doped GdScO 3 crystal is a potential laser medium for 662 nm laser. [ABSTRACT FROM AUTHOR]

Ho3+ and Eu3+ co-doping GdScO 3 crystal was successfully grown by special EFG method. The spectroscopic properties of the crystal were measured and analyzed. The absorption cross section was calculated to be 2.027 × 10−20 cm2 at 1161 nm. The J-O theory intensity parameters Ω t (t = 2, 4, 6), radiative transition rates, fluorescence branching ratios and radiative lifetimes were calculated. The Ho,Eu:GdScO 3 crystal has very strong emission at 2869 nm and the emission cross section was 13.524 × 10−21 cm2. The fluorescence lifetimes of the 5I 7 and 5I 6 levels were measured to be 4.457 ms and 1.265 ms. Confirmed that Eu3+ can be used as an effective deactivation ion of Ho3+ in GdScO 3 crystal. All those results show that the Ho,Eu:GdScO 3 crystal would be a potential laser material for ∼3 μm mid-infrared region. • Ho,Eu:GdScO 3 crystal was successfully grown. • The spectroscopic properties of the Ho,Eu:GdScO 3 crystal were analyzed. • J-O theory was applied to analyze fluorescence properties of the Ho,Eu:GdScO 3 crystal. • The energy transfer between Ho3+ and Eu3+ ions, spectroscopic characteristic of ∼3 μm emission were calculated and analyzed. [ABSTRACT FROM AUTHOR]

A series of 0.5 at.% Tm:Ca 1-x Y x F 2+x (x = 0, 0.01, 0.04, 0.06, 0.08, 0.12) crystals have been successfully grown by the temperature gradient technique (TGT) method. The absorption spectra, fluorescence spectra, and fluorescence decay curves were measured and analyzed at room temperature. By comparison, it is found that when the concentration of Y3+ ions reaches 8 at.%, the absorption cross section corresponding to the 3H 6 →3H 4 energy level is 2.56 × 10−21 cm2 at 793 nm, which is suitable for GaAlAs LD pumping. The J-O strength parameters Ω 2 , Ω 4 , and Ω 6 were obtained. With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. When the concentration of Y3+ ions reaches 8 at.%, the emission cross sections are 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, and the full widths at half maximum (FWHM) are 76 nm and 195 nm, respectively. The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. • With the incorporation of Y3+ ions, the value of Ω 4 /Ω 6 gradually increases. • When the concentration of Y3+ ions reaches 8 at.%, the emission cross section is 3.05 × 10−21 cm2 at 1476 nm, 2.56 × 10−21 cm2 at 2378 nm, respectively. • The fluorescence lifetime of 3H 4 level, the upper level of 1.5 μm and 2.3 μm, is 1.05 ms, which is very beneficial for 1.5 μm and 2.3 μm laser. [ABSTRACT FROM AUTHOR]

Ho:Lu 2 O 3 crystal was successfully grown by TGT method. The spectroscopic properties of the crystal were analyzed. The absorption cross section of Ho:Lu 2 O 3 were 0.307 × 10−20 cm2 at 1147 nm and 1.076 × 10−20 cm2 at 1929 nm. J-O theory was applied to analyze fluorescence properties of the Ho:Lu 2 O 3 crystal. The intensity parameters Ω t (t = 2,4,6), radiative transition rates, branching ratios and radiative lifetime were calculated. The Ho:Lu 2 O 3 crystal had very strong emission at 2027 nm and 2849 nm and emission cross sections were calculated to be 3.271 × 10−21 cm2 and 8.852 × 10−21 cm2, respectively. The fluorescence lifetimes of the Ho3+5I 7 and 5I 6 levels were measured to be 12.400 ms and 0.622 ms. All those results show that the Ho: Lu 2 O 3 crystal would be a potential laser material for mid-infrared region. • Ho: Lu 2 O 3 crystal was successfully grown by TGT method. • The spectroscopic properties of the Ho: Lu 2 O 3 crystal were analyzed. • J-O theory was applied to analyze fluorescence properties of the Ho:Lu 2 O 3 crystal. • The gain cross-section of Ho:Lu 2 O 3 crystal for ∼2 μm region and ∼3 μm region were calculated. [ABSTRACT FROM AUTHOR]

Nd:SrAl 11 O 19 (Nd:SRA) crystal has been grown by the Czochralski method. Polarized absorption spectra, polarized fluorescence spectra and fluorescence lifetime were investigated. For σ-polarization, the peak absorption cross section at 798 nm is 2.08 × 10−20 cm2 with full width at half maximum (FWHM) of 10.2 nm and the peak emission cross section is 3.36 × 10−20 cm2 at 1048.5 nm with FWHM of 4.80 nm. The Judd-Ofelt parameters Ω 2,4,6 were obtained to be 0.51 × 10−20 cm2, 2.08 × 10−20 cm2, and 2.12 × 10−20 cm2, respectively. Continuous-wave laser operation of the a-cut and c-cut Nd:SRA sample has been demonstrated. The maximum output power of 8.33 W was achieved from c-cut sample at an absorbed power of 27.73 W, corresponding to a slope efficiency of 31.3%. • Nd:SrAl 12 O 19 crystal has been gown by the Czochralski method. • Spectral parameters of Nd:SrAl 12 O 19 crystal were obtained. • Continuous-wave laser was demonstrated from Nd:SrAl 12 O 19 crystal. [ABSTRACT FROM AUTHOR]

GdScO 3 single crystal codoped with Tm3+ and Tb3+ ions was successfully grown by the Edge-defined Film-fed Growth Method (EFG) for the first time. Absorption, fluorescence spectrum and fluorescence lifetimes of the grown crystal at room temperature were measured. The absorption cross-section at 789 nm was calculated to be 8.20 × 10−21 cm2. The emission cross-section was 1.35 × 10−21 cm2 at 1504 nm with the FWHM of 95.3 nm. The fluorescence lifetimes of the 3H 4 state and the 3F 4 state were fitted to be 253 μs and 1460 μs, respectively. Compared with Tm3+ single doped GdScO 3 crystal, the codoping of Tb3+ successfully depopulated the 3F 4 energy level and enhanced the emission at 1.5 μm region. It indicated that Tm,Tb:GdScO 3 could be favorable laser medium for 1.5 μm-laser operation. • Tm3+ and Tb3+ co-doped GdScO 3 crystal was successfully grown by the edge-defined film-fed method (EFG) for the first time. • Spectral parameters and Judd-Ofelt parameters of Tm,Tb:GdScO3 crystal were obtained and compared. • The fluorescence mechanism of Tm3+ and Tb3+ co-doped GdScO 3 crystal has been studied. [ABSTRACT FROM AUTHOR]