1. A high absorption efficiency blue-emitting phosphor NaSrScSi2O7:Eu2+ for near-UV-pumped white light-emitting diodes.
- Author
-
Yang, Jiaojie, He, Peihua, Xie, Yijie, Chen, Qiang, Dong, Quan, Nie, Wendong, Yang, Fengli, Wang, Wei, Du, Fu, Peng, Jiaqing, and Ye, Xinyu
- Subjects
- *
PHOSPHORS , *LIGHT emitting diodes , *RIETVELD refinement , *ABSORPTION , *MOLECULAR spectra , *BLUE light - Abstract
• A brand-new blue-emitting phosphor NaSrScSi 2 O 7 :Eu2+ was prepared. • NaSrScSi 2 O 7 :0.03Eu2+phosphor possesses a high absorption efficiency of 84.35%. • The blue phosphor allows the WLED-2 spectrum to cover more short-wavelength region. A high absorption efficiency blue-emitting phosphor NaSrScSi 2 O 7 :Eu2+ for near-UV-pumped white light-emitting diodes [Display omitted] The Eu2+ ion is extensively used as an activator due to its wide excitation band and high efficiency emission spectrum. However, most Eu2+-activated blue-emitting phosphors have low absorption efficiency in the near-ultraviolet (n-UV) region or lack the short-wavelength blue light emission (<450 nm), resulting in UV light leakage or poor color rendering. Herein, we have successfully prepared a brand-new blue phosphor NaSrScSi 2 O 7 : Eu2+ by solid-state reaction method. The Rietveld refinement of the powder diffraction data, luminescent properties, decay lifetime, quantum efficiencyand thermal quenching have been investigated in detail. Under 345 nm excitation, the NaSrScSi 2 O 7 : 0.03Eu2+phosphor manifests an asymmetric emission spectrum centered at 427 nm, and notably, shows a high absorption efficiency of 84.35%. Finally, we encapsulated two white light-emitting diodes (WLEDs) devices using as-prepared blue-emitting phosphor and three commercial phosphors. At 80 mA drive current, both packaged devices demonstrate warm white light. Meanwhile, the WLED-2 with NaSrScSi 2 O 7 : 0.03Eu2+ blue-emitting phosphor has a lower correlated color temperature of 3726 K, its spectrum complements more short-wavelength spectrum, and the special color rendering index R 6 and R 7 increased from 95.2, 94.5 to 98.3, 96.5, respectively, compared with WLED-1 without present phosphor. These results demonstrate that NaSrScSi 2 O 7 : Eu2+ blue-emitting phosphor is a prospective novel luminescent material for WLEDs. [ABSTRACT FROM AUTHOR]
- Published
- 2022
- Full Text
- View/download PDF