Yb,Pr:CaF 2 crystals have been grown successfully by the temperature gradient technique(TGT). The absorption spectra, fluorescence spectra, fluorescence decay lifetime of Pr3+ ions in CaF 2 crystal sensitized by different Yb3+ ions concentration have been measured. The effective J-O intensity parameters were fitted to be Ω 2 =0.36 × 10−20cm2, Ω 4 =2.89 × 10−20cm2, Ω 6 =6.69 × 10−20cm2 for 0.3 at.%Pr,1.5 at.%Yb:CaF 2. And the emission cross sections of 3P 1 →3H 5 (535 nm), and 3P 0 →3F 4 (750 nm) are calculated to be 2.02 × 10−20cm2, and 2.50 × 10−20cm2 with the FWHM of 17.2 nm, and 10.5 nm, respectively. The fluorescence lifetime of 3P 0 has achieved great increasing by sensitizing of Yb3+ ion. Not only the up-conversion luminescence can be achieved, but also the broad band emission from 1D 2 energy level can be observed. The results show that Yb,Pr:CaF 2 could be a potential laser gain medium for visible and near-IR laser operation. • Not only the up-conversion luminescence can be achieved, but also the broad band emission from 1D 2 energy level can be observed by Yb3+ ion sensitizing. • Spectral properties and Judd-Ofelt parameters of Yb,Pr:CaF 2 crystal were investigated and analysed. [ABSTRACT FROM AUTHOR]

We report on the comparative growth and spectroscopy of Eu3+-doped Y 3 Al 5 O 12 (YAG) and Y 3 ScAl 4 O 12 crystals grown by the micro-pulling-down (μ-PD) method. The structure of the as-grown crystals was determined by X-ray diffraction (XRD) and Raman spectroscopy. The absorption spectra of the crystals are dominated by a strong line centered at 395 nm, matching well with the emission of commercial ultraviolet laser diodes. The Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals exhibit strongest red emission centered at 710 nm and the full width at half maximum (FWHM) was calculated to be 2.03 and 3.19 nm, respectively. The fluorescence decay curves of 5D 0 levels were measured and discussed. All the results indicate that the Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals are promising candidates for red luminescent/laser materials. • Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals were successfully grown by the micro-pulling-down technique for the first time. • The structure parameters of Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals were investigated by XRD. • Spectral parameters of Eu:YAG and Eu:Y 3 ScAl 4 O 12 crystals were obtained and compared. [ABSTRACT FROM AUTHOR]