Search

Abstract: Preparation of highly developed mesoporous activated carbons from renewable source Arundo donax Linn was performed using H4P2O7 as activator. The influences of chemical impregnation ratio (mass of H4P2O7:A. donax Linn), activation temperature and soaking time on the properties (yield, BET surface area, pore volume and surface functional group) of activated carbon were investigated. The optimal activated carbon (ALAC) was characterized by scanning electron micrograph (SEM), N2 adsorption/desorption isotherms, X-ray photoelectron spectrometry (XPS) and oxytetracycline (OTC) adsorption experiments. Results showed that the pore development was significant at temperatures >400°C, and reached a maximum BET surface area (1463m2/g) at 600°C and maximum total pore volume (1.24cm3/g) at 500°C. At a low impregnation ratio of 0.4, BET surface area and pore volume could reach as high as 1150.69m2/g and 0.59m3/g. Both BET surface area and pore volume initial increase followed by a decrease after reaching a maximum, with the maximal surface area was obtained at an impregnation ratio of 0.75 and maximal pore volume at 1.0. BET surface area and mesopore volume reached maximum after 10h of soaking. Acidic surface groups followed the order of: strong acidic groups>weak acidic groups>intermediate acidic groups. Low activation temperature was favorable to the formation of acidic surface functional groups. With the increase of soaking time, the acidic surface functional initial increase was followed by a gradual decrease and finally tended to level off. [Copyright &y& Elsevier]

Abstract: The objective of this research is to produce high surface area–activated carbon derived from cotton linter fibers by fused NaOH activation and to examine the feasibility of removing oxytetracycline (OTC) from aqueous solution. The cotton linter fibers activated carbon (CLAC) was characterized by N2 adsorption/desorption isotherms, Fourier transform infrared spectroscopy (FTIR), and scanning electron microscope (SEM). The results showed that CLAC had a predominantly microporous structure with a large surface area of 2143m2/g. The adsorption system followed pseudo-second-order kinetic model, and equilibrium was achieved within 24h. The equilibrium data were described well by Langmuir isotherm. Thermodynamic study showed that the adsorption was exothermic reaction at low concentration and became endothermic nature with the concentration increasing. Competitive adsorption took place in the weakly acidic to neutral conditions. Under the strong acidity or strong alkaline condition, the adsorption of the oxytetracycline was hindered by electrostatic repulsion. The adsorption mechanism depended on the pH of the solutions as well as the pK a of the oxytetracycline. [Copyright &y& Elsevier]

Abstract: The paper presents advantages and limitations of microwave heating in preparation of lotus stalk-based activated carbon by comparing the characteristic and adsorption properties of carbons with microwave (Mic-LSAC) and conventional (LSAC) heating methods employing H3PO4 as chemical agent. Mic-LSAC was produced with radiation power of 700W and radiation time of 15min. LSAC was allowed by single step to get carbonized at 450°C in a muffle furnace for 1h. Both produced carbons showed typical Type IV nitrogen adsorption isotherms. Mic-LSAC had large surface area of 1434m2/g and micropore volume of 1.337cm3/g, while LSAC had surface area of 1220m2/g and micropore volume of 1.191cm3/g. Moreover, Mic-LSAC had higher portion of mesopores than LSAC. Boehm''s titration results and Fourier transform infrared spectra indicated that Mic-LSAC possessed smaller acidic oxygen functionalities. Mic-LSAC had higher pHpzc, more ordered stacking of layer compared to LSAC. For both adsorbents, the adsorption kinetics followed the pseudo-second-order model and the adsorption equilibrium data were very well represented by the Langmuir isotherm. The maximum adsorption capacities obtained at pH 2.80 were 564.97mg/g and 537.63mg/g for Mic-LSAC and LSAC, respectively. The differences of textual and chemical characteristics caused by heating method were related to adsorption capacity. [Copyright &y& Elsevier]