Due to high light absorption and high refractive index of silicon nitride (Si3N4) ceramic, it is difficult to prepare Si3N4 slurry with favorable curing ability, high solid loading and low viscosity at the same time, and thus the high-quality Si3N4 parts are hard to fabricate via Digital Light Processing (DLP). In this paper, the oxidation process was used to enhance the curing behavior of Si3N4 slurry, and then silane coupling agent (KH560) was used to improve the rheological properties of the oxidized Si3N4 slurry. The effect of Si3N4 slurry with oxidation and modification on its rheological behavior, light absorption, curing ability and stability have been systematically investigated. A Si3N4 slurry with abundant photocuring ability, high solid loading, low viscosity and reliable stability was fabricated by the oxidized (1 h) and KH560 (1 wt.%) modified Si3N4 powders, and the dense Si3N4 ceramic parts were produced by this slurry via DLP 3D printing. Subsequently, the influence of oxidation and modification on microstructure, mechanical properties and thermal conductivity have been investigated. Finally, the microstructure and performances of Si3N4 ceramic were compared between different forming processes (including: DLP and cool isostatic pressing). [ABSTRACT FROM AUTHOR]

In this work, a stereolithography-based method of 3D printing was successfully used to fabricate a complex-shaped triangular zirconia cutting tool with a tool withdrawal groove and a honeycomb ceramic component. The sintered bodies displayed significant shrinkage after sintering, with the maximum shrinkage being 35.26%. The XRD pattern indicated that the crystalline phase of the parts was the t-ZrO 2 phase, while SEM characterization revealed that the sintered bodies were composed of densely packed submicron-grade grains, without any discernible pores. The density of the parts was measured as 97.14% via Archimedes’ water displacement method, which is consistent with the results of SEM characterization. Additionally, the measured Vickers hardness and fracture toughness of the fabricated parts were 13.0597 GPa and 6.0380 MPa m 1/2 , respectively. These values are close to the structural properties of common zirconia ceramics prepared by conventional approaches. Hence, a novel DLP-stereolithography-based 3D printing process for the fabrication of complex and dense zirconia ceramic parts has been proposed in this work. [ABSTRACT FROM AUTHOR]

We report a novel approach to fabricate dense zirconia-toughened alumina (ZTA) ceramics with excellent properties via an additive manufacturing process based on stereolithography. The XRD patterns show the ZTA sample consists of α-Al 2 O 3 and t-ZrO 2 with the dominance of α-Al 2 O 3 . The zirconia grain with the average size of 0.35 µm is small enough to trigger the toughening behavior of zirconia in the ZTA. The prepared ceramics showed a density, Vickers hardness, bending strength, and fracture toughness of 4.26 g/cm 3 , 17.76 GPa, 530.25 MPa, and 5.72 MPa m 1/2 , respectively. These properties are comparable to those for ceramics obtained through conventional ceramic processing. [ABSTRACT FROM AUTHOR]