Search

The bonding of wood with assembly adhesives is crucial for manufacturing wood composites, such as solid wood panels, glulam, furniture parts, and sport and musical instruments. This work investigates 13 hardwoods—bangkirai, beech, black locust, bubinga, ipé, iroko, maçaranduba, meranti, oak, palisander, sapelli, wengé and zebrano—and analyzes the impact of their selected structural and physical characteristics (e.g., the density, cold water extract, pH value, roughness, and wettability) on the adhesion strength with the polyvinyl acetate (PVAc) adhesive Multibond SK8. The adhesion strength of the bonded hardwoods, determined by the standard EN 205, ranged in the dry state from 9.5 MPa to 17.2 MPa, from 0.6 MPa to 2.6 MPa in the wet state, and from 8.5 MPa to 19.2 MPa in the reconditioned state. The adhesion strength in the dry state of the bonded hardwoods was not influenced by their cold water extracts, pH values, or roughness parallel with the grain. On the contrary, the adhesion strength was significantly with positive tendency influenced by their higher densities, lower roughness parameters perpendicular to the grain, and lower water contact angles. [ABSTRACT FROM AUTHOR]

A barrier plasma, created at atmospheric pressure, was used to improve the surface and adhesive properties of polyester (PES) film with respect to wood using polyurethane adhesives. The modification of PES film surfaces using barrier discharge plasma is attractive for various applications. Plasma pre-treatment initiates and participates in grafting, polymerization, or cross-linking reactions on the PES surface. This method of surface modification is clean, dry, ecological, and very efficient. The enhancement of the wettability of the polyester film was necessary for promoting higher adhesion to wood with water-based adhesives. The treatment of polyester films by barrier plasma led to a considerable increase in the surface free energy of the film and subsequently an increase in the peel strength of the adhesive joint of PES film-oak wood with polyurethane adhesive. [ABSTRACT FROM AUTHOR]

The purpose of this study was to evaluate the feasibility of using magnesium and sodium lignosulfonates (LS) in the production of particleboards, used pure and in mixtures with urea-formaldehyde (UF) resin. Polymeric 4,4′-diphenylmethane diisocyanate (pMDI) was used as a crosslinker. In order to evaluate the effect of gradual replacement of UF by magnesium lignosulfonate (MgLS) or sodium lignosulfonate (NaLS) on the physical and mechanical properties, boards were manufactured in the laboratory with LS content varying from 0% to 100%. The effect of LS on the pH of lignosulfonate-urea-formaldehyde (LS-UF) adhesive compositions was also investigated. It was found that LS can be effectively used to adjust the pH of uncured and cured LS-UF formulations. Particleboards bonded with LS-UF adhesive formulations, comprising up to 30% LS, exhibited similar properties when compared to boards bonded with UF adhesive. The replacement of UF by both LS types substantially deteriorated the water absorption and thickness swelling of boards. In general, NaLS-UF-bonded boards had a lower formaldehyde content (FC) than MgLS-UF and UF-bonded boards as control. It was observed that in the process of manufacturing boards using LS adhesives, increasing the proportion of pMDI in the adhesive composition can significantly improve the mechanical properties of the boards. Overall, the boards fabricated using pure UF adhesives exhibited much better mechanical properties than boards bonded with LS adhesives. Markedly, the boards based on LS adhesives were characterised by a much lower FC than the UF-bonded boards. In the LS-bonded boards, the FC is lower by 91.1% and 56.9%, respectively, compared to the UF-bonded boards. The boards bonded with LS and pMDI had a close-to-zero FC and reached the super E0 emission class (≤1.5 mg/100 g) that allows for defining the laboratory-manufactured particleboards as eco-friendly composites. [ABSTRACT FROM AUTHOR]

This research optimizes the process of plywood production to determine its effectiveness in reducing energy and adhesive consumption for more efficient production with the required quality. The influence of selected parameters including veneer treatment (non-densified and densified), plywood structure, temperature, time and pressure of pressing, on the bonding quality and temperature evolution within the veneer stacks during hot pressing was investigated. Rotary-cut, non-densified and densified birch veneers and phenol formaldehyde (PF) adhesive were used to manufacture plywood samples. The effect of pressure and time of pressing on bonding quality of the plywood was determined. Bonding quality was evaluated by determining the shear strength of the plywood samples. The temperature evolution inside the veneer stacks was measured for birch veneers for different pressing temperatures and pressures for different numbers of veneer layers. The heating rate of the veneer stacks increased as the pressing temperature increased and decreased markedly with an increasing number of veneer layers. At a high pressing pressure, the heating rate of the densified veneer stacks was faster than that of non-densified veneers at the same pressure. The use of densified veneers for the production of plywood can lead to a shorter pressing time (17–50% reduction), lower glue consumption (33.3% reduction) and a lower pressing pressure (22.2% reduction) without negatively impacting the bonding strength of the plywood. [ABSTRACT FROM AUTHOR]

In this study, the effect of the veneer-drying process at elevated temperatures on selected properties and formaldehyde emission of plywood panels was determined. We assume that during the veneer drying at high temperatures, more formaldehyde is released from it, and therefore, a lower formaldehyde emission can be expected from the finished plywood. Prior to bonding, birch veneers were dried at 160 °C (control) and 185 °C in an industrial veneer steam dryer (SD) and at 180 °C, 240 °C and 280 °C in an industrial veneer gas dryer (GD). Two types of adhesives were used: urea–formaldehyde (UF) and phenol–formaldehyde (PF) resins. Bonding quality, bending strength and modulus of elasticity in bending, water absorption and thickness swelling of plywood samples were determined. The formaldehyde emission level of samples was also measured. It was concluded from the study that the effects of veneer-drying temperatures on the bonding strength and physical and mechanical properties of plywood panels were significant. Veneer-drying temperatures of 185 °C/SD, 180 °C/GD and 240 °C/GD negatively affected the bending strength and the modulus of elasticity along and across the fibres for both UF and PF plywood samples. Bonding strength mean values obtained from all test panels were above the required value (1.0 MPa) indicated in EN 314-2 standard. The lowest formaldehyde emissions for the UF and PF plywood samples were observed in the samples from veneer dried in a steam dryer at 185 °C/SD. [ABSTRACT FROM AUTHOR]

Thermoplastic films exhibit good potential to be used as adhesives for the production of veneer-based composites. This work presents the first effort to develop and evaluate composites based on alder veneers and high-density polyethylene (HDPE) film. The effects of hot-pressing temperature (140, 160, and 180 °C), hot-pressing pressure (0.8, 1.2, and 1.6 MPa), hot-pressing time (1, 2, 3, and 5 min), and type of adhesives on the physical and mechanical properties of alder plywood panels were investigated. The effects of these variables on the core-layer temperature during the hot pressing of multiplywood panels using various adhesives were also studied. Three types of adhesives were used: urea–formaldehyde (UF), phenol–formaldehyde (PF), and HDPE film. UF and PF adhesives were used for the comparison. The findings of this work indicate that formaldehyde-free HDPE film adhesive gave values of mechanical properties of alder plywood panels that are comparable to those obtained with traditional UF and PF adhesives, even though the adhesive dosage and pressing pressure were lower than when UF and PF adhesives were used. The obtained bonding strength values of HDPE-bonded alder plywood panels ranged from 0.74 to 2.38 MPa and met the European Standard EN 314-2 for Class 1 plywood. The optimum conditions for the bonding of HDPE plywood were 160 °C, 0.8 MPa, and 3 min. [ABSTRACT FROM AUTHOR]