The heat desorption of styrene from adsorbents is impracticable owing to its spontaneous polymerization under heating conditions. However, the feature also brings a potential promoting effect on styrene adsorption. Therefore, it is expected to develop the non-regenerative adsorbents with large adsorption capacity by strengthening the polymerization effect. In this work, C–Cl grafted silica gel adsorbents were prepared by introducing (Chloromethyl)dimethylchlorosilane (CMDMCS) and FeCl 2 into silica gel. The C–Cl grafted silica gel exhibited excellent styrene adsorption performance, its adsorption amounts for styrene were 4.67 times and 9 times of unmodified silica gel under dry air condition and high humidity condition (RH = 80%), respectively. In addition, the adsorption of styrene on C–Cl grafted silica gel was almost unaffected by the presence of toluene. The characterization of adsorbents after styrene adsorption indicated that the improvement of adsorption capacity of C–Cl grafted silica gel for styrene can be attributed to atom transfer radical polymerization (ATRP) of styrene molecules on modified silica gel during adsorption process. [Display omitted] • C–Cl grafted SiO 2 adsorbents were prepared by introducing CMDMCS and FeCl 2. • The adsorption capacity of SiO 2 -1.5 for styrene was 4.7 times of SiO 2. • The adsorption of styrene on C–Cl grafted SiO 2 was almost unaffected by toluene. • C–Cl grafted SiO 2 showed excellent moisture resistance for styrene adsorption. • ATRP occurred during the adsorption process of styrene on C–Cl grafted SiO 2. [ABSTRACT FROM AUTHOR]

Adsorptive removal of gas phase low concentration macromolecular organic component, represented by naphthalene, from the enclosed space using ordered mesoporous carbon (OMC) has been studied by molecular simulation and experimental investigation. The simulation results indicated that both adsorption capacity and adsorption stability of the OMCs for naphthalene decreased with the increase of pore sizes from 2 nm to 8 nm. Characterizations showed that the prepared OMCs had the pore structure similar to the simulated OMCs except for the rough surface. In particular, the adsorption performance of the prepared OMCs was significantly lower than that of the simulated OMCs when pore size was 2 nm and 3 nm, which was attributed to the rough inner surface of these adsorbents, blocking the narrow pore channels and significantly reducing the pore volume. OMC with pore size of 4 nm had the highest adsorption amount for naphthalene. The co-adsorption experiments in the presence of both naphthalene and toluene, acetone or water showed the adsorption performance of OMCs for naphthalene were almost unaffected by the presence of low concentration toluene and acetone, as well as high relative humidity. [Display omitted] • Adsorption of naphthalene by OMCs were investigated by simulation and experiment. • Realistic molecular models for OMCs were constructed by "delete atom" method. • The impact of pore structure on the adsorption of naphthalene was revealed. • OMC with pore size of 4 nm has the highest adsorption capacity for naphthalene. • OMCs show excellent adsorption selectivity and good moisture resistance. [ABSTRACT FROM AUTHOR]