Search

Ti-xMg (x=17, 33, and 55 mass%) alloy films, which cannot be prepared by conventional melting processes owing to the absence of a solid-solution phase in the phase diagram, were prepared by direct current magnetron sputtering in order to investigate their biocompatibility. Ti and Mg films were also prepared by the same process for comparison. The crystal structures were examined by X-ray diffraction (XRD) analysis and the surfaces were analyzed by X-ray photoelectron spectroscopy. The Ti, Ti-xMg alloy, and Mg films were immersed in a 0.9% NaCl solution at 310 K for 7d to evaluate the dissolution amounts of Ti and Mg. In addition, to evaluate the formation ability of calcium phosphate in vitro, the Ti, Ti-xMg alloy, and Mg films were immersed in Hanks' solution at 310 K for 30 d. Ti and Mg form solid-solution alloys because the peaks attributed to pure Ti and Mg do not appear in the XRD patterns of any of the Ti-xMg alloy films. The surfaces of the Ti-17 Mg alloy and Ti-33 Mg alloy films contain Ti oxides and MgO, whereas MgO is the main component of the surface oxide of the Ti-55 Mg alloy and Mg films. The dissolution amounts of Ti from all films are below or near the detection limit of inductively coupled plasma-optical emission spectroscopy. On the other hand, the Ti-17 Mg alloy, Ti-33 Mg alloy, Ti-55 Mg alloy, and Mg films exhibit Mg dissolution amounts of approximately 2.5, 1.4, 21, and 41 μg/cm(2), respectively. The diffraction peaks attributed to calcium phosphate are present in the XRD patterns of the Ti-33 Mg alloy, Ti-55 Mg alloy, and Mg films after the immersion in Hanks' solution. Spherical calcium phosphate particles precipitate on the surface of the Ti-33 Mg film. However, many cracks are observed in the Ti-55 Mg film, and delamination of the film occurs after the immersion in Hanks' solution. The Mg film is dissolved in Hanks' solution and calcium phosphate particles precipitate on the glass substrate. Consequently, it is revealed that the Ti-33 Mg alloy film evaluated in this study is suitable for biomedical applications., (Copyright © 2015 Elsevier B.V. All rights reserved.)

The springback behavior of Ti-12Cr and Ti-29Nb-13Ta-4.6Zr (TNTZ) during deformation by bending was investigated; and the microstructures of the non-deformed and deformed parts of both alloys were systematically examined to clarify the relationship between microstructure and springback behavior. For the deformed Ti-12Cr alloy, deformation-induced ω-phase transformation occurs in both the areas of compression and tension within the deformed part, which increases the Young׳s modulus. With the deformed TNTZ alloy, deformation-induced ω-phase transformation is observed in the area of compression within the deformed part; while a deformation-induced α″ martensite transformation occurs in the area under tension, which is likely to be associated with the pseudoelasticity of TNTZ. Among these two alloys, Ti-12Cr exhibits a smaller springback and a much greater bending strength when compared with TNTZ; making Ti-12Cr the more advantageous for spinal fixation applications., (Copyright © 2014 Elsevier Ltd. All rights reserved.)

The age-hardening behavior of the dental-casting Ag-20Pd-12Au-14.5Cu alloy subjected to aging treatment at around 673K is well known, and this hardening has been widely employed in various applications. To date, the age-hardening of this alloy has been explained to attribute to the precipitation of a β phase, which is a B2-type ordered CuPd phase or PdCuxZn1-x phase. In this study, results obtained from microstructural observations using a transmission electron microscopy and a scanning transmission electron microscopy revealed that a fine L10-type ordered β' phase precipitated in the matrix and a coarse-structure region (consisting of Ag- and Cu-rich regions) appeared after aging treatment at 673K and contributed to increase in hardness. The microstructure of the coarse β phase, which existed before aging treatment, did not change by aging treatment. Thus, it is concluded that the fine β' phase precipitated by aging treatment contributed more to increase in hardness than the coarse-structure region and coarse β phase., (Copyright © 2013 Elsevier B.V. All rights reserved.)

In order to meet the requirements of the patients and surgeons simultaneously for spinal fixation applications, a novel biomedical alloy with a changeable Young's modulus, that is, with a low Young's modulus to prevent the stress-shielding effect for patients and a high Young's modulus to suppress springback for surgeons, was developed. In this study, the chromium and oxygen contents in ternary Ti(11, 12 mass%)Cr-(0.2, 0.4, 0.6 mass%)O alloys were optimized in order to achieve a changeable Young's modulus via deformation-induced ω-phase transformation with good mechanical properties. The Young's moduli of all the examined alloys increase after cold rolling, which is attributed to the deformation-induced ω-phase transformation. This transformation is suppressed by oxygen but enhanced with lower chromium content, which is related to the β(bcc)-lattice stability. Among the examined alloys, the Ti-11Cr-0.2O alloy shows a low Young's modulus of less than 80GPa in the solution-treated (ST) condition and a high Young's modulus of more than 90GPa in the cold rolled (CR) condition. The Ti-11Cr-0.2O alloy also exhibits a high tensile strength, above 1000MPa, with an acceptable elongation of ~12% in the ST condition. Furthermore, the Ti-11Cr-0.2O alloy exhibits minimal springback. This value of springback is the closest to that of Ti64 ELI alloy among the compared alloys. Therefore, the Ti-11Cr-0.2O alloy, which has a good balance between large changeable Young's modulus, high tensile strength, good plasticity, and minimal springback, is considered to be a potential candidate for spinal fixation applications., (© 2013 Elsevier Ltd. All rights reserved.)

Hydroxyapatite (HAp) films were deposited on a β-type titanium alloy, Ti-29Nb-13Ta-4.6Zr (TNTZ), by metal organic chemical vapor deposition (MOCVD) in order to improve its hard-tissue compatibility. The surface morphologies of TNTZ substrates were changed by acid treatments and mechanical polishing prior to the HAp film deposition. The adhesive strength of the HAp films formed on TNTZ substrates treated with an HF solution increased to twice that of the HAp film deposited on a TNTZ substrate with a mirror-like finish. Complex microstructures with deeply etched grain boundaries, formed on the TNTZ substrates after immersion in the HF solution, were responsible for the increase in the adhesive strength of the HAp film caused by an interlocking effect. The HAp films on TNTZ substrates treated with a H(2)SO(4) solution exhibited lower adhesive strength than HAp films on TNTZ substrates treated with HF solution, regardless of the surface roughness of the substrates. Additionally, acid treatments using HNO(3) and H(2)O(2) solutions did not change the surface morphologies of the TNTZ substrates. The complex microstructures with deeply etched grain boundaries and nanosized asperities formed on the TNTZ substrates are important factors in the improvement of the adhesive strengths of HAp films deposited on TNTZ substrates., (Copyright © 2012 Elsevier Ltd. All rights reserved.)

New low modulus β-type titanium alloys for biomedical applications are still currently being developed. Strong and enduring β-type titanium alloy with a low Young's modulus are being investigated. A low modulus has been proved to be effective in inhibiting bone atrophy, leading to good bone remodeling in a bone fracture model in the rabbit tibia. Very recently β-type titanium alloys with a self-tunable modulus have been proposed for the construction of removable implants. Nickel-free low modulus β-type titanium alloys showing shape memory and super elastic behavior are also currently being developed. Nickel-free stainless steel and cobalt-chromium alloys for biomedical applications are receiving attention as well. Newly developed zirconium-based alloys for biomedical applications are proving very interesting. Magnesium-based or iron-based biodegradable biomaterials are under development. Further, tantalum, and niobium and its alloys are being investigated for biomedical applications. The development of new metallic alloys for biomedical applications is described in this paper., (Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.)

Metallic implant rods used in spinal fixtures should have a Young's modulus that is sufficiently low to prevent stress shielding for the patient and sufficiently high to suppress springback for the surgeon. Therefore, we propose a new concept: novel biomedical titanium alloys with a changeable Young's modulus via deformation-induced ω phase transformation. In this study, the Cr content in the range of 10-14 mass% was optimized to produce deformation-induced ω phase transformation, resulting in a large increase in the Young's modulus of binary Ti-Cr alloys. The springback and cytotoxicity of the optimized alloys were also examined. Ti-(10-12)Cr alloys exhibit an increase in Young's modulus owing to deformation-induced ω phase transformation. In this case, such deformation-induced ω phase transformation occurs along with {332}(β) mechanical twinning, resulting in the maintenance of acceptable ductility with relatively high strength. Among the examined alloys, the lowest Young's modulus and largest increase in Young's modulus are obtained from the Ti-12Cr alloy. This alloy exhibits smaller springback than and comparable cytocompatibility to the biomedical Ti alloy Ti-29Nb-13Ta-4.6Zr., (Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.)

To develop a novel biomedical titanium alloy with a changeable Young's modulus via deformation-induced ω phase transformation for the spinal rods in spinal fixation devices, a series of metastable β type binary Ti-(15-18)Mo alloys were prepared. In this study, the microstructures, Young's moduli and tensile properties of the alloys were systemically examined to investigate the effects of deformation-induced ω phase transformation on their mechanical properties. The springback of the optimal alloy was also examined. Ti-(15-18)Mo alloys subjected to solution treatment comprise a β phase and a small amount of athermal ω phase, and they have low Young's moduli. All the alloys investigated in this study show an increase in the Young's modulus owing to deformation-induced ω phase transformation during cold rolling. The deformation-induced ω phase transformation is accompanied with {332}(β) mechanical twinning. This resulted in the maintenance of acceptable ductility with relatively high strength. Among the examined alloys, the Ti-17Mo alloy shows the lowest Young's modulus and the largest increase in the Young's modulus. This alloy exhibits small springback and could be easily bent to the required shape during operation. Thus, Ti-17Mo alloy is considered to be a potential candidate for the spinal rods in spinal fixation devices., (Copyright © 2012 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.)

Abstract: A super-hydrophobic film was successfully deposited on magnesium alloy AZ31 by the microwave plasma-enhanced chemical vapor deposition (MPECVD) process. The film surface showed a static water contact angle of more than 150°. The hydrophobicity and root mean square roughness of the film surface increased with an increase in deposition time. The anticorrosion resistance of the deposited film was estimated by electrochemical impedance spectroscopy (EIS) measurements. The EIS measurements and appropriate equivalent circuit models revealed that the super-hydrophobic film considerably improved the anticorrosion resistant performance of magnesium alloy AZ31. The anticorrosion mechanism of the super-hydrophobic film was also considered. Moreover, the chemical stability of the super-hydrophobic film in acidic, neutral, and alkaline aqueous solutions was investigated. The super-hydrophobic film showed high chemical stability in acidic and neutral aqueous solutions. [ABSTRACT FROM AUTHOR]