Search

The present work concerns the surface modification of The Ti-13Nb-13Zr alloy by electropolishing and plasma electrolytic oxidation (PEO) process in Ca-containing electrolytes: calcium formate and calcium lactate solutions (0.1-1.0 mol dm -3 ) under voltages of 200 and 400 V. As a result of the PEO process, a porous oxide layer containing incorporated calcium compounds was formed on the Ti-13Nb-13Zr alloy surface. The morphology and chemical composition of the modified Ti-13Nb-13Zr alloy were investigated using scanning electron microscopy (SEM + EDS), X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). An increase in the applied voltage caused an increase in the number of pores and an increase in the amount of calcium incorporated in the oxide layer. Analysis showed that all samples were covered by titanium oxide, which was present in the form of anatase and/or rutile. In course of the experiments, it was showed that the proposed procedure has a positive effect on the overall bioactivity of the Ti-13Nb-13Zr alloy. Bioactivity investigations using simulated body fluid (SBF) confirmed the formation of apatite on the anodized surfaces. The cell adhesion results obtained by the use of human bone marrow mesenchymal stem cells (hBMSC) demonstrated that the PEO coatings on the Ti-13Nb-13Zr alloy remarkably enhanced the cytocompatibility of the substrate, indicating a potential application in orthopedic surgeries. The incorporation of Ca into the oxide layer proceeded to a higher extent when the PEO treatment was performed in the calcium lactate bath. The oxide layers formed in the calcium lactate solution exhibited also superior biological behavior towards hBMSC. This can be ascribed to the presence of carboxylic groups onto coatings' surface (as identified by XPS), which facilitated the anchoring of cells and tissues., (Copyright © 2019 Elsevier B.V. All rights reserved.)

Titanium and its aluminum and vanadium-free alloys have especially great potential for medical applications. Electrochemical surface modification improves their surface bioactivity and stimulates osseointegration process. In this work, the effect of plasma electrolytic oxidation of the β-type alloy Ti-15Mo surface on its bioactivity is presented. Bioactivity of the modified alloy was investigated by immersion in simulated body fluid (SBF). Biocompatibility of the modified alloys were tested using human bone marrow stromal cells (hBMSC) and wild intestinal strains (DV/A, DV/B, DV/I/1) of Desulfovibrio desulfuricans bacteria. The particles of apatite were formed on the anodized samples. Human BMSC cells adhered well on all the examined surfaces and expressed ALP, collagen, and produced mineralized matrix as determined after 10 and 21 days of culture. When the samples were inoculated with D. desulfuricans bacteria, only single bacteria were visible on selected samples. There were no obvious changes in surface morphology among samples. Colonization and bacterial biofilm formation was observed on as-ground sample. In conclusion, the surface modification improved the Ti-15Mo alloy bioactivity and biocompatibility and protected surface against colonization of the bacteria. © 2015 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater, 104B: 903-913, 2016., (© 2015 Wiley Periodicals, Inc.)