Ceramic foams with significant porosity and robust mechanical properties have received extensive attentions. However, it is still difficult to achieve excellent compressive strength at high porosity levels. In this work, a gelation of foamed boehmite sol method is proposed to settle this issue. The technological parameters during preparation process are systematically investigated. As‐prepared alumina ceramic foams possess unprecedentedly high compressive strength of 34.1‐89.1 MPa at high porosity levels of 66.0%‐87.2%, which is attributed to the present of hierarchical pore structure, small grain size and pore size. This work demonstrates a facile and novel method for the fabrication of high‐performance alumina ceramic foams toward practical applications. [ABSTRACT FROM AUTHOR]

Abstract The mechanical strength of highly porous ceramic foams shows significant attenuation with the increase of porosity, especially for ceramic foams with very high porosity level above 95%. Ultra-light bulk composite ceramic foams were fabricated via introducing 20 wt% zirconia in alumina-based cell wall, aiming at improving mechanical strength of alumina based ceramic foams. The preparation and stability of alumina and zirconia particles synergistically stabilized foams were investigated. The obtained bulk ceramic foams manifested an exciting combination of both high porosity above 96% and excellent specific compressive strength, due to their closed pore structure, defect-free cell wall with uniform thickness, and uniformly distributed zirconia grains in alumina matrix. The alumina/zirconia composite ceramic foams with porosity of 96.7% exhibited compressive strength of 1.11 ± 0.07 MPa, which was much higher than that of alumina ceramic foams in the case of same porosity. [ABSTRACT FROM AUTHOR]

The weak compressive strength of dried ceramic foams is a disadvantage of fabricating ultralight ceramic foams, especially for the ceramic foams with porosity exceeding 95%. In this study, dried alumina foams were enhanced by agar and PVA-freezing-thawing using sodium dodecyl sulfate as surfactant. It is found that the two additives have no negative influence on adsorption of sodium dodecyl sulfate on alumina particles as well as the hydrophobic character of alumina particles. Stable alumina particle-stabilized foams were prepared with less than 0.5 wt% agar and 1.0 wt% PVA. High additive concentration above the critical values weakens stability of wet foams, which is probably due to the aggregate of alumina particles caused by long-chain molecules connecting. The compressive strength of dried alumina foams has a significant improvement with the employment of agar and PVA-freezing-thawing. The dried foams prepared with 1wt% PVA assisted by freezing-thawing has porosity of 97.1% and compressive strength of 0.16 MPa, which could maintain integrity of dried foams without destruction in the fabricating process. [ABSTRACT FROM AUTHOR]