1. Microstructure control and properties of β″-Al2O3 solid electrolyte.
- Author
-
Chen, Guangyu, Lu, Jiachun, Li, Lin, Chen, Lixin, and Jiang, Xinbiao
- Subjects
- *
ALUMINUM oxide , *METAL microstructure , *SOLID electrolytes , *DOPING agents (Chemistry) , *TITANIUM dioxide , *IONIC conductivity - Abstract
Doping a small amount of TiO 2 can promote the relative density, increase the content of β″-Al 2 O 3 phase and improve the microstructure of β″-Al 2 O 3 electrolyte. In this work, the influence of microstructure, relative density, content of β″ phase and performance of β″-Al 2 O 3 electrolyte were studied by adjusting the doping amount of TiO 2 and the sintering temperature. Samples were characterized with respect of density, closed-cell porosity, XRD, SEM, bending strength, AC Impedance Spectroscopy. The results demonstrated that the addition of TiO 2 can significantly improve the densification rate of β″-Al 2 O 3 ceramics. 1500–1550 °C is the key temperature section of eliminating pore process. At 1550 °C, the sample of 0.1–0.8 wt.% TiO 2 formed homogeneous microstructure associated with a refinement in the grain size of the final compact. Macro defects appeared when the sintering temperature reached to 1580 °C or the content of TiO 2 was 1.6–2.0 wt.%. The total conductivity linearly depended on the temperature and fitted well with the Arrhenius equation. β″-Al 2 O 3 ceramics showed the best bending strength and ionic conductivity at 1550 °C when the doping amount of TiO 2 is 0.4 wt.% and 0.8 wt.%, respectively. [ABSTRACT FROM AUTHOR]
- Published
- 2016
- Full Text
- View/download PDF