Alumina is one of the most commonly used and researched structural ceramic because of its excellent properties. However, its intrinsic brittleness is the fatal drawback, which hinders it from wider applications. How to improve its fracture toughness as well as the bending strength is always challenging for material researchers. In this paper, alumina matrix composites were fabricated by hot-pressing, in which some additives, including zirconia, alumina platelets, and MXene, were incorporated. The influence of the introduced additives on their microstructure and mechanical properties was investigated. Compare with the monolithic alumina, both bending strength and fracture toughness of all samples were improved greatly. Incorporation of zirconia was beneficial to the mechanical properties due to the phase-transformation strengthening and toughening mechanism. While alumina platelets resulted in high fracture toughness because of the self-toughening of elongated grains. The synergistic effect of alumina platelets and MXene enormously improved the fracture toughness from 2.9 ± 0.3 MPa·m1/2 for monolithic alumina to 7.5 ± 0.4 MPa·m1/2 for the composite, which was increased by 159%. This work will provide useful references for the fabrication of high-strength and high-toughness alumina ceramics by introducing additives properly. [ABSTRACT FROM AUTHOR]

Synergic effect of graphene oxide (GO) and silicon nitride whisker (Si 3 N 4 w) on the mechanical properties of nacre-like alumina was investigated in this study. A comprehensive analysis on the composites, including microstructure, relative densities, flexural strength and fracture toughness, was carried out. The experimental results showed that, GO promoted the fracture toughness of the composites, but reduced the flexural strength slightly; while adding a certain amount of Si 3 N 4 w improved both flexural strength and fracture toughness. With the incorporation of GO and Si 3 N 4 w, the highest flexural strength reached 520 MPa and the fracture toughness reached 9.59 MPa m1/2. Microstructure observation revealed that the enhanced mechanical properties were ascribed to the synergistic toughening mechanisms induced by the nacre-like structure of alumina, GO pull-out, Si 3 N 4 w pinning and pull-out. [ABSTRACT FROM AUTHOR]