Improvement of the mechanical properties of advanced ceramics fabricated by additive manufacturing has been a prerequisite for their wide applications. In this work, zirconia-toughened alumina (ZTA) parts with a variety of yttria-stabilized zirconia (YSZ) content were fabricated by stereolithography (SL) technology, based on the appropriate self-holding ability of the viscoelastic paste and application of conformal contactless support strategy. Combining microstructural analysis and mechanical assessment by three-point bending and indentation tests, the influence of YSZ content on the SL process and subsequent mechanical properties was discussed. The results showed that the optimized matching of flexural strength (477.54 MPa) and fracture toughness (6.56 MPa m1/2) was acquired by ZTA ceramic with a YSZ content of 20 wt%. When the YSZ content reached 30 wt%, agglomerations formed and led to a negative influence on the properties of ZTA ceramics. It is confirmed that the combined contribution from the addition of YSZ on the improvement of mechanical property and influence of the SL process should be synthetically considered during the design of ceramic paste feedstock for such additive manufacturing. [ABSTRACT FROM AUTHOR]

The nanoscale plasticity phenomena in zirconia-toughened alumina (ZTA) ceramics with yttria-stabilized zirconia (YSZ) addition of 10% and 30% fabricated by additive manufacturing based on a stereolithography technique were explored in detail by nanoindentation and scanning electron microscopy. It was demonstrated that the initiation of nanoscale plasticity was attributed to the combined contributions from the generation of nanoscale shear deformation bands and localized microcracking at the indentations. Such localized plastic behavior underneath the nanoindenter was interpreted by maximum shear stress analysis. The response of the phase boundary during indentation was emphasized through crack propagation paths, and optimization of alumina–YSZ adaptation through component design and SL processing was expected. [ABSTRACT FROM AUTHOR]