Pinewood was modified by vacuum impregnation with various aqueous lignin solutions of low concentration (0.5- 1.0%) and its decay resistance was tested by the standard procedure EN 113. Five lignin types were tested against three brown rot and one white rot fungi. The bio-durability of wood was considerably increased by the treatment. The highest effect of modification was for alkali, kraft, hydrolysis lignins and industrial lignosulfonate, when mass losses of wood for brown-rot fungi were negligible. The effect of the modification with certified lignosulfonates was insignificant. Chemical analysis revealed that phenols, which are leached from lignin and are adsorbed by wood in the impregnation process, could act as a biocide. The hydrophilic properties of wood either did not change (certified lignins) or were enhanced because of some change in the pore structure (industrial lignins). Further tests are needed to verify the positive effects of this technologically simple and environmentally friendly treatment. [ABSTRACT FROM AUTHOR]

Novel biobased materials from fungal hyphae and cellulose fibers have been proposed to address the increasing demand for natural materials in personal protective equipment (PPE). Materials containing commercially available kraft fibers (KF), laboratory-made highly fibrillated hemp fibers (HF) and fungal fibers (FF) obtained from fruiting bodies of lignicolous basidiomycetes growing in nature were prepared using paper production techniques and evaluated for their mechanical and air permeability properties. SEM and microscopy revealed the network structure of materials. The tensile index of materials was in the range of 8–60 Nm/g and air permeability ranged from 32–23,990 mL/min, depending on the composition of materials. HF was the key component for strength; however, the addition of FF to compositions resulted in higher air permeability. Chemical composition analysis (Fourier-transform infrared spectroscopy) revealed the presence of natural polysaccharides, mainly cellulose and chitin, as well as the appropriate elemental distribution of components C, H and N. Biodegradation potential was proven by a 30-day-long composting in substrate, which resulted in an 8–62% drop in the C/N ratio. Conclusions were drawn about the appropriateness of fungal hyphae for use in papermaking-like technologies together with cellulose fibers. Developed materials can be considered as an alternative to synthetic melt and spun-blown materials for PPE. [ABSTRACT FROM AUTHOR]