Abstract: Whereas Ce0.9Sr0.1Cr0.5V0.5O3 is an active fuel cell anode catalyst for conversion of only the H2S content of 0.5% H2S–CH4 at 850°C, inclusion of 5wt% NiO to form a composite catalyst enabled concurrent electrochemical conversion of CH4. A fuel cell with a 0.3mm thick YSZ membrane and Ce0.9Sr0.1Cr0.5V0.5O3 as anode catalyst had a maximum power density of 85mWcm−2 in 0.5% H2S–CH4 at 850°C, arising only from the electro-oxidation of H2S. Using a same thick membrane, promotion of the anode with 5wt% NiO increased the total anode electro-oxidation activity to afford maximum power density of 100mWcm−2 in 0.5% H2S–CH4. The same membrane provided 30mWcm−2 in pure CH4, showing that the incremental improvement arose substantially from CH4 conversion. Performance of each anode was stable for over 12h at maximum power output. XPS and XRD analyses showed that an increase in conductivity of Ce0.9Sr0.1Cr0.5V0.5O3 in H2S-containing environments resulted from a change in composition and structure from the tetragonal oxide to monoclinic Ce0.9Sr0.1Cr0.5V0.5(O,S)3. [Copyright &y& Elsevier]

Abstract: Undoped BaTiO3 perovskite oxide is more effective than SrTiO3 and La2Ti2O7 oxide as anode catalyst in SOFC fueled with H2S-containing methane. Electrochemical performance, impedance spectroscopy and other characterizations show that pure BaTiO3 is a good anode catalyst for conversion of methane in SOFC, especially in H2S-containing atmospheres. Compared with SrTiO3 and La2Ti2O7 samples, the BaTiO3−based fuel cell has higher resistance to carbon deposition, better electrochemical performance and much higher stability during long term operation. A maximum power density of 135 mW cm−2 was achieved at 900 °C with 0.5% H2S–CH4 in a fuel cell having a 300 μm thick YSZ electrolyte. High catalytic activity for methane conversion, mixed electronic and ionic conductivity, and the surface basicity of BaTiO3 unexpectedly provides promising performance as anodes in SOFC. [Copyright &y& Elsevier]