Search

A novel apatite structure phosphor Ca 9 La(PO 4 ) 5 (GeO 4 )F 2 :Dy 3+ (CLPGF:Dy 3+ ) with a hexagonal lattice in the P 6 3 / m space group was synthesized via a facile solid state technique. The crystal and fine local structure as well as their photoluminescence properties were investigated in detail. The CLPGF:Dy 3+ phosphor can absorb in the UV-vis spectral region of 290–475 nm and exhibit two intense emission bands centered at 485 and 580 nm, which ascribes to 4 F 9/2 → 6 H 15/2 and 4 F 9/2 → 6 H 13/2 transitions of Dy 3+ , respectively. The concentration quenching of Dy 3+ emission occurs via the energy transfer among the nearest-neighbor ions and the corresponding quenching mechanism was verified to be the dipole-dipole interaction. The quantum efficiencies of the phosphors were examined to be 72.9% and its luminescence intensity at 150 °C decreases to 93.8% and 98.6% of the initial value at room temperature, which corresponds to 4 F 9/2 to 6 H 15/2 transition and 4 F 9/2 to 6 H 13/2 transition of Dy 3+ ions, respectively. Their interesting photoluminescence properties indicate that the CLPGF:Dy 3+ phosphor is a promising white-emitting candidate for w -LEDs applications. [ABSTRACT FROM AUTHOR]

Emission-tunable phosphors Ca 9 La(PO 4 ) 5 (SiO 4 )F 2 :Ce 3+ ,Tb 3+ with apatite structure were synthesized by a solid-state reaction. The phase structure, photoluminescence (PL) properties, lifetimes and the PL thermal stability were investigated, respectively. The phosphor exhibited an asymmetric broad-band blue emission (Ce 3+ ) with peak at 403 nm and the line-type green emission with peak at 543 nm (Tb 3+ ). The varied color of the phosphors from blue to green can be achieved by properly tuning the relative ratio of Ce 3+ /Tb 3+ through the energy transfer from Ce 3+ to Tb 3+ ions. The critical distance was calculated to be 8.78 Å by using the concentration quenching method. When the temperature turned up to 150 °C, the emission intensity of Ca 9 La(PO 4 ) 5 (SiO 4 )F 2 :Ce 3+ ,Tb 3+ phosphor was 77% of its initial value at room temperature, which indicated the good thermal stability of the sample. All the properties indicate that the Ca 9 La(PO 4 ) 5 (SiO 4 )F 2 :Ce 3+ ,Tb 3+ phosphor has potential application of color-tunable w -LEDs. [ABSTRACT FROM AUTHOR]

A series of Eu 2+ and Eu 2+ /Tb 3+ co-doped Ba 3 GdNa(PO 4 ) 3 F phosphors have been synthesized via a high temperature solid-state reaction. The relative intensity of PL spectra of Ba 3 GdNa(PO 4 ) 3 F: x Eu 2+ increases with increasing x value, and reaches a maximum at x =0.04. Ba 3 GdNa(PO 4 ) 3 F:Eu 2+ , Tb 3+ phosphors exhibit a broad excitation band ranging from 220 to 450 nm, which matches perfectly with the characteristic emission of n -UV light-emitting diode (LED) chips. Upon 365 nm excitation, the Ba 3 GdNa(PO 4 ) 3 F:Eu 2+ , Tb 3+ phosphors show two dominating bands peaked at 466 and 543 nm, which are assigned to the 4f 7 →4f 6 5d 1 transition of the Eu 2+ ions and the 5 D 4 → 7 F 5 transition of the Tb 3+ ions, respectively. In view of the energy transfer mechanism between Eu 2+ and Tb 3+ , the Ba 3 GdNa(PO 4 ) 3 F:Eu 2+ , Tb 3+ emission color can adjust from blue to green, and their chromatic coordinates ( x , y ) vary from (0.16, 0.135) to (0.254, 0.398). The critical distance was also calculated to be 16.90 Å. The above results indicate that the Ba 3 GdNa(PO 4 ) 3 F: Eu 2+ , Tb 3+ phosphors are a candidate for blue–green components in the application of n -UV w -LEDs. [ABSTRACT FROM AUTHOR]