This study addresses the effect of the coatings prepared from aramid nanofibers (ANFs) on the surface treatment of aramid fiber and reinforced polycarbonate (PC) composite (AF/PC). Aramid fiber's smooth, inert surface bonds poorly with polycarbonate. In this research, the PC‐ANF coating was made by the PC/CH2Cl2 solution, which was modified by aramid nanofibers to improve the interfacial adhesion and compatibility of aramid fiber/PC composites. What's more, the silane (KH570) was added to improve the dispersion and interfacial strength of ANF and PC. The results showed the water contact angle of the aramid fiber modified by PSi‐ANF coating was reduced, indicating the modified fiber has a better wettability. The interfacial bonding strength between PC and aramid fiber increased by 77.2%. The AF/PC composites were prepared by hot‐compression, which the aramid fiber wovens treated with P‐ANF coating, PSi‐ANF coating. The tensile strength, flexural strength, interlaminar shear strength, and impact strength of the AF/PC composite reinforced by AF treated with PSi‐ANF containing 2.0 wt% ANF increased by 62.0%, 81.9%, 49.5%, and 27.6%, respectively. Therefore, this study demonstrates that incorporating ANF interphase may offer an innovative and practical way for enhancing the interface bonding properties of aramid‐reinforced composites. [ABSTRACT FROM AUTHOR]

Inspired by the application of nano‐fillers in composite materials, well‐dispersed aramid nanofibers (ANFs) were prepared and added into the epoxy resin (EP) to improve the toughness and tenacity properties of the ANF/EP composites. The composites were characterized by mechanical property test, surface analysis, thermodynamic property analysis, and contact angle. Results showed that when the EP was added with 0.15 wt% ANF, the tensile strength, bending strength, and impact strength are increased by 28.2%, 81.9%, and 81.8% compared with pure EP, respectively. The thermal stability and infiltration of the composites are improved. The interlaminar shear strength and interfacial shear strength of the aramid fiber were increased by 53.1% and 92.7% compared with the not reinforced EP, demonstrating that the epoxy reinforced with ANF is also beneficial for improving the interfacial bonding strength of aramid fiber and EP. The mechanism of the epoxy reinforcement by ANF and the interface enhancements showed that the ANF could cause several crack bridges and strong hydrogen bond interaction interface. [ABSTRACT FROM AUTHOR]