Search

The copolymer ethylene–octene (POE) has good aging resistance and is an inexpensive asphalt additive compared to the styrene–butadiene–styrene copolymer (SBS). However, POE is easy to segregate in asphalt during storage at high temperatures. Grafting glycidyl methacrylate (GMA) onto the molecular backbone of POE (i.e., POE-g-GMA) may solve this problem, for the epoxy groups in GMA can react with the active groups in asphalt. Asphalt modified with linear and crosslinked POE-g-GMA were prepared, and the hot storage stability, physical properties and thermal oxidation aging properties were discussed in detail. The results show that linear and low-degree crosslinked POE-g-GMA-modified asphalts are storage-stable at high temperatures via measurements of the difference in softening points and small-angle X-ray scattering (SAXS) characterizations from macro and micro perspectives. The difference in softening points (ΔSP) between the upper and lower ends is no more than 3.5 °C for modified asphalts after 48 h of being in an oven at 163 °C. More importantly, the crosslinking modification of POE-g-GMA can further increase the softening point and reduce the penetration as well as rheological properties via conventional physical property, dynamic shear rheometer (DSR) and multiple-stress creep recovery (MSCR) tests. Furthermore, asphalt modified with crosslinked POE-g-GMA reveals better aging resistance via measurements of the performance retention rate and electron paramagnetic resonance (EPR) characterizations after a rolling thin film oven test (RTFOT). This work may provide further guidelines for the application of polymers in asphalt. [ABSTRACT FROM AUTHOR] more...

To evaluate the long-term performances of different polymer-modified asphalt mixtures, three modifiers were chosen to modify AC-13 (defined as the asphalt concrete with the aggregate nominal maximum particle size of 13.2 mm); namely, high viscosity modifier (HVM), high modulus modifier (HMM), and anti-rutting agent (ARA). The deformation and cracking resistance of different polymer-modified mixtures were checked at different aging conditions (unaged, short-term aged, and long-term aged for 5, 10, and 15 days respectively). The results of the Hamburg wheel-track test and uniaxial penetration test (UPT) showed that the rutting resistance of all asphalt mixtures changed in a V-shape as the aging progressed. From the unaged stage to the long-term aging stage (5 days), the rutting resistance decreases gradually. While after the long-term aging stage (5 days), the rutting resistance increases gradually. Results from the semicircular bending test (SCB) and the indirect tensile asphalt cracking test (IDEAL-CT) indicated that the cracking resistance of all the mixtures gradually decline with the deepening of the aging degree, indicating that aging weakens the crack resistance of asphalt mixtures. Additionally, test results showed that the rutting resistance of ARA AC-13 (defined as AC-13 containing ARA) is the best, the cracking resistances of ARA AC-13, HMM AC-13 (defined as AC-13 containing HMM) and HVM AC-13 (defined as AC-13 containing HVM) have no significant difference, and different polymer modifiers had different sensitivities to aging due to the polymer content and the type of modifier. The conclusions of this study help to further understand the long-term performance of polymer-modified asphalt mixtures during service life and to help guide the selection of modifiers for mixtures. [ABSTRACT FROM AUTHOR] more...

Fiber length is a key parameter for the mixture design of basalt fiber-reinforced hot mix asphalt (HMA), which significantly affects the mix performance. To evaluate the suitability of fiber lengths for HMA with different nominal maximum aggregate size (NMAS), basalt fiber with the lengths of 3, 6, 9, 12, and 15 mm were selected for dense graded gradations with different NMASs (namely, SUP-13, SUP-20, and SUP-25), so as to prepare the fiber-reinforced HMA mixtures. Then, the mix performance was evaluated by an indirect tensile asphalt cracking test (IDEAL-CT), a four-point bending beam fatigue test, a wheel tracking test, a uniaxial penetration test, a low temperature bending beam test, and a freeze-thaw splitting test. Based on the performance results, the optimum fiber length for each mix gradation was proposed by the normalization method. The results showed that adding basalt fiber can enhance the comprehensive performance of all three types of HMA to a great extent. Furthermore, fiber length presented remarkable impact on the crack resistance, the fatigue resistance of the HMA, and the low temperature crack resistance, but it had limited influence on the high temperature deformation resistance, and water stability. The optimum fiber length for SUP-13, SUP-20, and SUP-25 was 6, 9, and 12 mm, respectively. [ABSTRACT FROM AUTHOR] more...

Incorporating reclaimed asphalt pavement (RAP) into asphalt mixtures achieves astonishingly environmental and economic benefits. However, there is hesitation to use higher RAP content due to the concern regarding the deterioration in pavement performance, especially the cracking resistance. Basalt fiber has been considered an effective additive to reinforce the performance of asphalt mixtures and, subsequently, the reinforcement effect is also expected for high-RAP content mixtures. Therefore, this study investigated the effect of basalt fiber on the pavement performance of asphalt mixtures with 0%, 30%, 40%, and 50% RAP contents against high-temperature performance, moisture susceptibility, low-temperature and intermediate-temperature cracking resistance, based on the wheel-tracking test, the uniaxial penetration test, the freeze-thaw splitting test, the low-temperature bending beam test, the semicircular bend fracture test and the indirect tensile asphalt cracking test, respectively. In addition, a performance-space diagram was developed to determine the mixture performance shift caused by basalt fiber. The results showed that adding basalt fiber compensated for the detrimental effect caused by RAP, leading to significant enhancement in moisture susceptibility and low- and intermediate-temperature cracking resistance of mixtures with high RAP content, along with the enhancement in high-temperature performance, indicating that basalt fiber can contribute to the use of high RAP content. [ABSTRACT FROM AUTHOR] more...

• The ARA could enhance the road performance of the LFSMA-13 for different ages and decrease the performance sensitivity to age. • The lignin fibers physically interact with the asphalt, while the ARA could chemically interact with the asphalt mixture. • The peak area of the imino and methyl in the asphalt decreases, and the peak area of the carbonyl and sulfoxide increases with age. • The correlation between the peak areas of imino, methyl, carbonyl, and sulfoxide, and the physical property indices of the LFSMA-13 and ALSMA-13 is good. This paper aims to analyze the long-term road performance of anti-rutting agent (ARA) reinforced asphalt mixture, and reveal its road performance from the micro morphology and chemical perspective. ARA was used to modify the lignin fiber-reinforced SMA-13 asphalt mixture (LFSMA-13). The unaged, and the short and long-term aged specimens were used to test the road performance (high and low-temperature properties, water stability, and anti-cracking) of the LFSMA-13 and ARA modified LFSMA-13 (ALSMA-13). In addition, the micromorphology of the additives and asphalt mixture and the chemical property of asphalt in the mixture were analyzed using the scanning electron microscope (SEM) test and Fourier transform infrared (FTIR) test. The relationship between road performance and chemical property was also analyzed. The results showed that the performance of the ALSMA-13 was better with age than the LFSMA-13. The SEM images showed that the lignin fiber and the ARA could form a network structure in the SMA-13 mixtures. The FTIR test indicated that the ARA's amino group (–NH–) could chemically interact with the asphalt in SMA-13. The peak area of the carbonyl and sulfoxide chemical group increased, and the imino and methyl decreased with age. The results showed a good correlation between the FTIR parameters and road performance. [ABSTRACT FROM AUTHOR] more...