Black poplar (Populus nigra L.) was thermally modified in nitrogen atmosphere. The effects of the modification process on poplar wood were evaluated for temperatures: 160 °C, 190 °C, and 220 °C applied for 2 h; and 160 °C and 190 °C for 6 h. The percentual impact of temperature and time of modification on the properties of modified wood was analysed. The study permitted the identification correlations between the chemical composition and selected physical properties of thermally modified poplar wood. The dimensional stability of poplar wood was improved after thermal modification in nitrogen. The higher the temperature of modification, the lower the equilibrium moisture content (EMC) of black poplar. At the temperature of 220 °C, EMC was two times lower than the EMC of non-modified black poplar. It is also possible to reduce the dimensional changes of wood two-fold (at the modification temperature of 220 °C), both in radial and tangential directions, independently of the acclimatization conditions (from 34% to 98% relative humidity, RH). Similar correlations have been found for wood that has been soaked in water. Higher modification temperatures and longer processing times contributed to a lower swelling anisotropy (SA). [ABSTRACT FROM AUTHOR]

Thermal modification of wood in nitrogen atmosphere permits its usability value to be improved. The aim of the research was to determine the impact of technological modification parameters at different levels on the colour of black poplar (Populus nigra L.). Black poplar was thermally modified in nitrogen atmosphere at a range of temperatures from 160 °C to 220 °C, at times between 2 h and 8 h. The parameters of wood colour were measured according to the CIE L*a*b* colour space model. The changes in a* and b* had a non-linear profile. The maximum value of a* for black poplar wood was achieved after a modification at the temperature of 200 °C, while the maximum value of the b* parameter was achieved after modification at 190 °C. Colour changes in the ΔE of black poplar after modification at 160 °C and 170 °C were similar, and the dynamics of changes increased after modification at the temperature of 180 °C. The highest value of ΔE, around 40, was observed after modification at the temperature of 220 °C and time of 8 h. There were no statistically significant differences between the ΔE for radial and tangential sections. Statistical analysis showed that modification temperature was responsible for the variability of the L* value in 90%, and in ca. 70% for the changes in parameters a* and b*. The influence of the modification time on the colour parameters was minor—below 4%. The influence of the interaction between modification temperature and time on the colour parameters was below 10%. As a consequence, in the case of ΔE of black poplar wood, the influence of temperature was at a level of ca. 80%. On the other hand, the influence of time and the interaction between temperature and time of modification was low—below 3%. [ABSTRACT FROM AUTHOR]