1. Mechanical and hygrothermal properties of hemp-silica bio-composites.
- Author
-
Ayati, Bamdad, Gutierrez, Armor, and Chandler, Alan
- Subjects
- *
SOLUBLE glass , *HYGROTHERMOELASTICITY , *LIQUID sodium , *CONSTRUCTION materials , *THERMAL conductivity , *CONCRETE products , *NATURAL fibers , *THERMAL properties - Abstract
This research investigated the development of a fast-drying silica-based binder for hemp concrete products with enhanced mechanical and thermal properties. Hemp-silica bio-composites were prepared by mixing hemp shivs with a two-component binder system composed of liquid sodium silicate and tributyl citrate (TBC). Compressive strength, thermal conductivity, moisture buffering value, cyclic moisture resistance and microstructure of hemp-silica composites were analysed, and the results were compared with those of hemp-lime concrete. Hemp-silica blocks with shiv-liquid sodium silicate mass ratio of 1:3.75 and TBC content of 37.5 wt% of sodium silicate dry matter produced a compressive strength of 0.56 MPa only after 3 days of drying and 1.92 MPa after 28 days. These were higher than hemp-lime blocks at the same density range. Hemp-silica panels showed a thermal conductivity of 0.101 W/mK and an excellent moisture buffering value of 3.49. Hemp silica formed an open porosity with large air gaps between the particles and a water-resistance silica-based layer on the shiv surface producing a higher moisture resistance compared to hemp-lime systems. This paper focuses on the development of a novel fast-drying binder system with a potential for use in conjunction with other lingnocellular plant aggregates to form low-carbon and efficient multifunctional building materials. • A novel quick-drying silica-based binder for hempcrete was developed. • Hemp-silica concrete showed enhanced mechanical properties compared to hemp-lime. • Hemp-silica concrete reached 0.56 MPa only after 3 days of drying. • Tributyl citrate improved the water resistance of sodium silicate binder. [ABSTRACT FROM AUTHOR]
- Published
- 2024
- Full Text
- View/download PDF