Objectives: To synthesize two different sizes of bioactive glass-coated mesoporous silica nanoparticles (BGN@MSNs) and to investigate their effects on dentinal tubule occlusion and remineralization. Materials and methods: Two different sizes of mesoporous silica nanoparticles (MSNs) were synthesized using the Stöber method (368A, 1840A) and coated with bioactive glass nanoparticles (BGNs) using a modified quick alkali-mediated sol-gel method (368B, 1840B). Sensitive tooth disc models were prepared and divided into six groups and the following treatments were applied: group 1—no treatment, group 2—bioglass, group 3—368A, group 4—368B, group 5—1840A, and group 6—1840B. Then, five discs were selected from each group and soaked in 6 wt% citric acid to test acid resistance. Dentinal tubule occlusion and occlusion ratio were observed using field-emission scanning electron microscopy. In vitro mineralization tests using simulated body fluid solution were performed to evaluate the remineralization effect of the treatment. Results: All samples effectively occluded the dentinal tubule and formed a membrane-like layer. After acid treatment, 1840B (group 6) exhibited the highest rate of dentinal tubule occlusion. Remineralization was observed in 368B and 1840B, and 1840B exhibited the fastest remineralization. Conclusions: Dentinal tubule remineralization induced by the BGN@MSN biocomposite can be used to stabilize long-term prognosis in dentin hypersensitivity. The 1840B induced the most efficient remineralization, and its smaller size and larger surface area were effective for remineralization. Clinical relevance: The BGN@MSN biocomposite with its smaller size and larger surface area was more effective for remineralization and dentinal tubule sealing. [ABSTRACT FROM AUTHOR]

White spot lesions (WSLs), a side effect of orthodontic treatment, can result in reversible and unaesthetic results. Graphene oxide (GO) with a bioactive glass (BAG) mixture (BAG@GO) was added to Low-Viscosity Transbond XT (LV) in a ratio of 1, 3, and 5%. The composite's characterization and its physical and biological properties were verified with scanning electron microscopy (SEM) and X-ray diffraction (XRD); its microhardness, shear bond strength (SBS), cell viability, and adhesive remnant index (ARI) were also assessed. Efficiency in reducing WSL was evaluated using antibacterial activity of S. mutans. Anti-demineralization was analyzed using a cycle of the acid-base solution. Adhesives with 3 wt.% or 5 wt.% of BAG@GO showed significant increase in microhardness compared with LV. The sample and LV groups showed no significant differences in SBS or ARI. The cell viability test confirmed that none of the sample groups showed higher toxicity compared to the LV group. Antibacterial activity was higher in the 48-h group than in the 24 h group; the 48 h test showed that BAG@GO had a high antibacterial effect, which was more pronounced in 5 wt.% of BAG@GO. Anti-demineralization effect was higher in the BAG@GO-group than in the LV-group; the higher the BAG@GO concentration, the higher the anti-demineralization effect. [ABSTRACT FROM AUTHOR]