Search

Phytoextracts modulated synthesis of nano‐scaled spherical lanthanum oxide nanoparticles (La2O3 NPs) are reported using the aqueous extracts of Hyphaene thebaica as a bioreducing and chelating agent. X‐ray diffraction (XRD) pattern revealed sharp peaks and single‐phase purity. The Debye–Scherrer approximation indicated an average crystallite size of 37 nm, whereas W‐H plot revealed a crystallite size of 59 nm, complemented by the high‐resolution transmission electron microscopy (HR‐TEM). The infrared spectroscopy revealed characteristic La‐O band at 426 and 648 cm−1. K‐M function revealed the bandgap of 5.6 eV, whereas broad intense emission peaks between 345 and 750 nm. The Raman spectra revealed peaks at 182, 325, 384, and 491 cm−1. Elemental composition was confirmed using energy‐dispersive X‐ray spectroscopy (EDS) spectrum, and the spotty rings from selected area electron diffraction (SAED) indicated the crystalline nature of the HT‐La2O3 NPs. In addition, the HT‐La2O3 NPs were investigated for in vitro antioxidant, anticancer, antiangiogenic, and cytotoxic potentials. DPPH free radical scavenging activity was highest, that is, 49.54 ± 0.88% at 1000 μg/mL. MTT assay on MCF‐7 and 3T3 cell lines revealed a median lethal concentration of 114 and 43 μg/mL, respectively. The antiangiogenic effect examined by chick chorioallantoic membrane (CAM) assay indicated inhibition of 57.14 ± 0.96% at 1000‐μg/mL concentration with an IC50 of 551 μg/mL. IC50 for the brine shrimp lethality assay was 314.2 μg/mL. Our study indicates cytotoxicity of HT‐La2O3 NPs, and it further concluded that HT‐La2O3 NPs were more potent against 3T3 cells as compared with MCF‐7 cells. Further research on the biological synthesis and anticancer studies are recommended for the large‐scale applications of the La2O3 NPs. [ABSTRACT FROM AUTHOR]

CaZrO3 nanoparticles were synthesized by biosynthesis process via Hyphaene thebaica natural extract as a reducing and stabilizing agent. The crystalline structure and vibration modes of CaZrO3 were investigated by X-ray diffraction and Raman spectroscopy. Their optical properties were studied using ultraviolet–visible diffused reflectance spectroscopy and photoluminescence spectroscopy. In order to study the effect of the synthesis method and the reduction of the grain size on the morphology and the electrical and dielectric properties of the material, the results obtained for CaZrO3 synthesized by the biosynthesis process were compared to those obtained for CaZrO3 prepared by the conventional solid-state method. Transmission electron microscopy shows a marked improvement in the morphology of the compound synthesized by the biosynthesis process compared to that prepared by the solid-state reaction. The ionic conductivity of both samples was measured using the electrochemical impedance technique. It was found that the contribution of grain boundary resistance to total resistance has increased significantly with size reduction and led to the improvement of the dielectric properties of the material by the increase of dielectric constant and the decrease of dielectric loss. [ABSTRACT FROM AUTHOR]

Phytoextracts modulated synthesis of nano‐scaled spherical lanthanum oxide nanoparticles (La2O3 NPs) are reported using the aqueous extracts of Hyphaene thebaica as a bioreducing and chelating agent. X‐ray diffraction (XRD) pattern revealed sharp peaks and single‐phase purity. The Debye–Scherrer approximation indicated an average crystallite size of 37 nm, whereas W‐H plot revealed a crystallite size of 59 nm, complemented by the high‐resolution transmission electron microscopy (HR‐TEM). The infrared spectroscopy revealed characteristic La‐O band at 426 and 648 cm−1. K‐M function revealed the bandgap of 5.6 eV, whereas broad intense emission peaks between 345 and 750 nm. The Raman spectra revealed peaks at 182, 325, 384, and 491 cm−1. Elemental composition was confirmed using energy‐dispersive X‐ray spectroscopy (EDS) spectrum, and the spotty rings from selected area electron diffraction (SAED) indicated the crystalline nature of the HT‐La2O3 NPs. In addition, the HT‐La2O3 NPs were investigated for in vitro antioxidant, anticancer, antiangiogenic, and cytotoxic potentials. DPPH free radical scavenging activity was highest, that is, 49.54 ± 0.88% at 1000 μg/mL. MTT assay on MCF‐7 and 3T3 cell lines revealed a median lethal concentration of 114 and 43 μg/mL, respectively. The antiangiogenic effect examined by chick chorioallantoic membrane (CAM) assay indicated inhibition of 57.14 ± 0.96% at 1000‐μg/mL concentration with an IC50 of 551 μg/mL. IC50 for the brine shrimp lethality assay was 314.2 μg/mL. Our study indicates cytotoxicity of HT‐La2O3 NPs, and it further concluded that HT‐La2O3 NPs were more potent against 3T3 cells as compared with MCF‐7 cells. Further research on the biological synthesis and anticancer studies are recommended for the large‐scale applications of the La2O3 NPs. [ABSTRACT FROM AUTHOR]