Search

Deterioration of adhesively bonded CFRP/steel systems in salt fog environment, i.e., deicing salts and ocean environments, has to be taken into account in the design of steel strengthened structures. In the present work, monotonic and quasi-static cyclic loading were applied to CFRP-to-steel double strap joints for two kinds of CFRP laminates after being aged for a period of 5000 h to evaluate the bond behavior. The bonded joints exposed to salt fog had a different failure mode than that observed in the control specimens (0 h of exposure). The severe reduction of the maximum bond stress resulted from damage initiation that occurred in the corrosion region of the steel substrate, associated with final partial rupture on the corroded steel substrate around the edge of the bonded area: it was also correlated with reduced load carrying capacity. Results of pseudo-cyclic tests showed that the relationship between a local damage parameter (D) and normalized local dissipated energy (W d /G f) and the normalized slip increment (ΔS/ΔS ult) exhibited almost the same trend in the un-aged and aged bonded joints. The normalized slip increment can be seen as a direct indicator for the local and global damage for the un-aged and aged bonded joints. However, monotonic and quasi-static cyclic tests results revealed that the stress concentration due to local corrosion of steel substrate could lead to brittle rupture or accelerated cumulative damage once the aged bonded interface had become weaker. The bonded joints have exhibited also a smaller relative deformation capacity between CFRP and steel. [ABSTRACT FROM AUTHOR]

Carbon Fiber Reinforced Polymer (CFRP) composites have a large potential for strengthening and retrofitting steel parts but due to their premature debonding from steel, further data and research are still required for wider application in such situations. In the present paper, the bond characteristics of CFRP-to-steel joints in pull-pull loaded conditions were studied. Monotonic loading of the double strap joints with different bond lengths was applied and the failure modes and interfacial bond-slip curves were obtained. A tri-linear bond-slip model is proposed and it was derived from the experimental data. A closed-form solution approach is also proposed based on the tri-linear bond-slip model. The strength of the CFRP-to-steel interface, the distribution of the relative displacements between bonded materials, the strains developed in the CFRP laminate and the bond stresses along the interface are reported and the closed-form solution is compared with the experimental results. Two cases are selected for presentation: (i) one with the bond length greater than the effective bond length; and, inversely, (ii) one with bond length which is shorter than the effective bond length. The results predicted by the closed-form solutions are shown to be accurate enough when compared to the experiments. [ABSTRACT FROM AUTHOR]

Mechanical anchorage devices have the potential to efficiently improve the bond behavior of Carbon Fiber-Reinforced Polymers (CFRP) Externally Bonded (EB) onto steel with an adhesive. Existing relevant studies, however, have been very limited. Against this background, experimental and numerical studies on the double overlapped CFRP-to-steel bonded joints with an end mechanical anchorage were carried out in the present study. Two types of CFRP laminates (i.e. , SIKA CFRP and the other type made in Harbin Institute of Technology – HIT) were used in the bond tests, with or without end mechanical anchorage devices. The test results showed that the end mechanical anchorage had marginal effect on the bond-slip relationship between EB CFRP and steel as well as debonding load, but could increase the ultimate load. It was also found that CFRP laminate from HIT had a better bond performance than that from SIKA, in terms of both debonding load and ultimate load. Using ABAQUS, Finite Element (FE) model was established on such bonded joints and the accuracy was verified with test results. The verified FE model was adopted in a parametric study to further clarify the effect of key parameters on the bond behavior of such bonded joints. [ABSTRACT FROM AUTHOR]