Search

Purpose: To assess the compression and flexural strength of bone cement mixed with 0 ml, 1 ml, or 2 ml of blood., Methods: High viscosity polymethyl methacrylate (PMMA) loaded with or without gentamicin was used. Blood was collected from total knee arthroplasty patients. In the same operating room, one pack of cement each was mixed with 0 ml (control), 1 ml, or 2 ml of blood for 1 minute during the dough phase. The dough was extruded into cylindrical and rectangular moulds for 20 minutes of setting, and then cured in phosphate buffered saline at 37±1ºC for 7 days. The samples were visually inspected for fractures and areas of weakness, and then scanned using microcomputed tomography. 48 gentamicin-loaded and 59 non-gentamicin-loaded samples mixed with 0 ml (control), 1 ml, or 2 ml of blood were randomised for flexural and compression strength testing; each group had at least 6 samples., Results: In samples loaded with or without gentamicin, the flexural and compressive strength was highest in controls, followed by samples mixed with 1 ml or 2 ml of blood. In samples mixed with 2 ml of blood, the flexural strength fell below the standard of 50 MPa. In samples mixed with 2 ml of blood and all gentamicin-loaded samples, the compressive strength fell below the standard of 70 MPa. Microcomputed tomography revealed areas of voids and pores indicating the presence of laminations and partitions within., Conclusion: The biomechanical strength of PMMA contaminated with blood may decrease. Precautions such as saline lavage, pack drying the bone, change of gloves, and prompt insertion of the implant should be taken to prevent blood from contaminating bone cement.

Background: In cemented joint arthroplasty, the handling characteristics (doughing, working, and setting times) of polymethyl methacrylate (PMMA) bone cement is important as it determines the amount of time surgeons have to optimally position an implant. Storage conditions (temperature and humidity) and the time given for PMMA cement to equilibrate to ambient operating theater (OT) temperatures are often unregulated and may lead to inconsistencies in its handling characteristics. This has not been previously studied. Hence, the purpose of this study was to investigate the effect of storage temperatures on the handling characteristics of PMMA cement and the duration of equilibration time needed at each storage temperature to produce consistent and reproducible doughing, setting, and working times., Methods: SmartSet® HV cement was stored at three different controlled temperatures: 20 °C (control), 24 °C, and 28 °C for at least 24 h prior to mixing. The cement components were then brought into a room kept at 20 °C and 50 % humidity. Samples were allowed to equilibrate to ambient conditions for 15, 30, 45, and 60 min. The cement components were mixed and the dough time, temperature-versus-time curve (Lutron TM-947SD, Lutron Electronics, Inc., Coopersburg, PA), and setting time were recorded. Analysis was performed using the two-way ANOVA test (IBM SPSS Statistics V.22)., Results: At 20 °C (control) storage temperature, the mean setting time was 534 ± 17 s. At 24 °C storage temperature, the mean setting time was 414 ± 6 s (p < 0.001*) with 15 min of equilibration, 446 ± 11 s (p < 0.001*) with 30 min of equilibration, 501 ± 12 s (p < 0.001*) with 45 min of equilibration, and 528 ± 15 (p > 0.05) with 60 min of equilibration. At 28 °C storage temperature, the mean setting time was 381 ± 8 s (p < 0.001*) with 15 min of equilibration, 432 ± 30 s (p < 0.001*) with 30 min of equilibration, 487 ± 9 (p < 0.001*) with 45 min of equilibration, and 520 ± 16 s (p > 0.05) with 60 min of equilibration., Conclusions: This study reflects the extent to which storage temperatures and equilibration times can potentially affect the handling characteristics of PMMA cement. We recommend institutions to have a well-regulated temperature and humidity-controlled facility for storage of bone cements and a protocol to standardize the equilibration time of cements prior to use in the OT to improve consistency and reproducibility of the handling characteristics of PMMA cement.