Search

In order to reduce the segregation of Cr and Mo and inhibit the precipitates, we added a small amount of B and Ce to traditional S31254 steel. Using an air-cooling and low-temperature diffusion treatment, the purpose was to control B and Ce at the grain boundary. The heat-treatment process could prompt co-segregation of B, precipitate-forming elements, and Ce at the grain boundary at 950 °C. After aging at 950 °C for different amounts of time, the diffusion treatment had an obvious inhibitory effect on the precipitates that caused them to become discontinuous, fine, and serrated. The B-containing serrated precipitates were only rich in Mo, while Cr was homogeneously distributed in the probed volume. A uniform distribution of Cr reduced the Cr-depleted zone in the area adjacent to the phase interface. Ce was observed to be segregated at the grain boundary. This showed that Ce could inhibit the formation of precipitates at the grain boundary. The serrated precipitates had an obvious resistance to intergranular corrosion. [ABSTRACT FROM AUTHOR]

Focusing on the serious volatilization of MoO3 in super austenitic stainless steel with a high Mo content, the influence of B on the formation of oxide film and the distribution of Cr and Mo was investigated at 900 °C and 1000 °C. Without the addition of B, Mo tends to diffuse to the surface, forming porous Cr/Mo-rich oxides, causing the volatilization of Mo. The addition of B can inhibit the diffusion of Mo to the surface, facilitate the diffusion of Cr to the surface and combines with O, providing conditions for the nucleation of Cr2O3. A large amount of Cr2O3 accumulated on the surface to form a dense passive film, which inhibited the diffusion of Mo to the surface, reduced the loss of Mo, and formed Mo/Cr-rich precipitates at grain boundaries that are close to the surface. However, it was difficult to form Mo-rich precipitates at the grain boundaries of a sample without B, which aggravated the volatilization of Mo from grain boundary to surface. Therefore, the addition of B can improve the oxidation resistance of 254SMO and inhibit the volatilization of Mo. [ABSTRACT FROM AUTHOR]

Aiming at serious oxidation problem of 254SMO super-austenitic stainless steel during hot working, the influence of B and Ce composite microalloying on its oxidation behavior was comparatively investigated at 1050 and 1100 °C. The results demonstrated that the combination of B and Ce can significantly alter the composition of the oxide film in 254SMO. Particularly, B and Ce composite microalloying can effectively promote the diffusion of Cr to the surface, and form a dense Cr 2 O 3 oxide film at a faster rate in the initial stage, which is more conducive to inhibiting the Mo volatilization and thus improving the oxidation resistance of 254SMO steels. Additionally, compared to the 0.005 wt% B (50B) and 0.005 wt% B together with 0.002 wt% Ce (50B + 20Ce) samples, the addition of 0.005 wt% B together with 0.005 wt% Ce (50B + 50Ce) had a more significant effect on improving high-temperature oxidation resistance of 254SMO. This research provides a valuable scholarly reference for improving the oxidation resistance of super-austenite stainless steels. • B and Ce composite microalloying can improve the oxidation resistance of 254SMO at 1050 and 1100 °C. • The combination of B and Ce can promote the formation of the dense Cr 2 O 3 on the surface. • At the initial oxidation stage at 1050 °C, the precipitation time of precipitates will affect the formation of oxide film. • When the Ce content reaches to 0.005 wt%, the oxidation resistance at 1100 °C can be significantly improved. [ABSTRACT FROM AUTHOR]